ABSTRACT Luffa Cylindrica is a tropical plant from the Cucurbitaceae family, whose fruit becomes very fibrous when fully ripened. The lignocellulosic sponges of Luffa can be suitable for use as reinforcement of epoxy matrix composites, because they have a morphology with spatial 3-D arrangement as well as are eco-friendly materials (biodegradable, and high available) and have economic advantages compared to composites reinforced with synthetic fibers derived from non-renewable sources. Surface modification of the Luffa fibers was carried out by hornification and mercerization methods and was verified by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and X-Ray Diffraction (XRD). For the fabrication of non-biodegradable composites by hand layup technique, the sponges were impregnated with an epoxy resin based on bisphenol in a metallic mold with dimensions 150×200×3 mm3, followed by compression at 5 MPa. The dynamic modulus of the fabricated composites were measured using the nondestructive impulse excitation technique (IET), according to the ASTM E1876 standard. Bar specimens with dimensions 80×25×3 mm3 of the laminated composites were tested at room temperature, with Sonelastic® (ATCP) equipment and its associated software. Results showed that the Luffa/epoxy composites has higher loss factor and dynamic modulus when the Luffa fiber is treated before the composite fabrication. The highest Young's modulus obtained was 4.05±0.31 GPa for mercerized Luffa/epoxy. For hornificated Luffa/epoxy composite the highest loss factor and shear modulus values obtained, were 0.0337±0.003 and 1.46±0.13 GPa respectively.

RESUMO A madeira é o material biológico mais conhecido e utilizado como matéria-prima desde os primórdios da humanidade até os dias atuais. Como um compósito natural e renovável, seu tempo de vida útil é limitado pela degradação de seus elementos básicos. Essa degradação pode ser ocasionada por reações químicas ou por agentes biológicos capazes de acelerar o processo de deterioração. Nesse contexto, esse trabalho teve como objetivo avaliar, sob condições laboratoriais, características de abrasão, térmica, microestruturais e de biodeterioração em sistemas estáticos da espécie de madeira Pau-Brasil (Caesalpinia echinata), com a finalidade de avaliar sua utilização em projetos de design. Os resultados mostram que o pau-brasil apresentou bom desempenho visual após ensaio de abrasão, pois não mostrou aumento representativo da rugosidade. Além disso o pau-brasil tem alto índice de cristalinidade de, aproximadamente, 68% e foi pouco sensível a ataques de fungos, com a formação de apenas 5,3 x 103 UFC/mL. Não houve também qualquer variação de textura causada por água ou suor.

ABSTRACT Wood is the best-known biological material used as a raw material since the dawn of mankind until present days. As a natural and renewable composite, its lifetime is limited by the degradation of its basic elements. This degradation can be caused by chemical reactions or by biological agents capable of accelerating the process of deterioration. In this work, the wear, thermal, and micro-structural characteristics, as also the bio-degradation behavior in static systems, of the wood species Brazilwood (Caesalpinia echinata) were studied under laboratory conditions in order to use these woods in design. The results show that Brazilwood has a good visual performance after abrasion test, since it has not shown any representative roughness increase. In addition, Brazilwood has high level of crystallinity of, approximately, 68% and was almost insensitive to fungi attack, forming only 5.3 x 103 CFU/mL. Besides, its texture did not change due to exposure to water or sweat.

Abstract The water absorption behavior of the DGEBA/TETA epoxy system was evaluated as a function of the epoxy monomer to amine hardener ratio. Weight gain versus immersion time curves were obtained and the experimental points were fitted using Fickian and Non-Fickian diffusion models. The results obtained showed that for all epoxy monomer to hardener ratios analyzed water diffusion followed non-Fickian behavior. It was possible to correlate the water absorption behavior to the macromolecular structure developed when the epoxy/ hardener ratio was varied. All epoxy/hardener ratios present a two-phase macromolecular structure, composed of regions with high crosslink density and regions with lower crosslinking. Epoxy rich systems have a more open macromolecular structure with a lower fraction of the dense phase than the amine rich systems, which present a more compact two-phase structure.

Digital image analysis was used to fully characterize the microstructure of human dentin. With the automatic routine implemented, field and region parameters related to human dentin characterization were obtained in significant statistical quantities. The results obtained for the density, area fraction, distance between neighbors, tilt angle, area and average diameter of the dentinary tubules are presented for unerupted third molars. The results, grouped per class of dentin or per tooth, are discussed in the light of the previous data found on the literature.

Um tubo fabricado com material compósito de matriz polimérica reforçado por fibras de vidro foi caracterizado através de microscopia eletrônica digital. Uma seção circunferencial do tubo foi observada em um microscópio eletrônico de varredura com captura digital de imagem. Um mosaico com imagens em alta magnificação foi gerado para que fosse possível uma caracterização que abrangesse desde as fibras individualmente até a distribuição espacial das camadas de fibras. Através do desenvolvimento de uma seqüência de processamento, dados como o diâmetro das fibras e ângulo de enrolamento foram obtidos, bem como foi realizada a identificação das várias camadas de fibras presentes.

A tube made with a glass-fiber reinforced polymer-matrix composite material was characterized through digital microscopy. A circumferential section of the tube was observed in a Scanning Electron Microscopy with digital image acquisition. A mosaic of high magnification images was created in order to allow complete characterization of the material. Through the development of an image analysis method, the fiber diameters, the winding angles and the discrimination of the layers were obtained.

An investigation was carried out on the room temperature ageing of off-stoichiometric DGEBA/TETA epoxy formulations. The results obtained show that the epoxy rich mixtures have their inherent brittleness increased by the ageing treatment due to recrystalization of the unreacted epoxy monomers, although homopolymerization could also play a minor role. The initial reaction steps dominated by the amine addition reactions control the macromolecular structure and the mechanical performance of the stoichiometric and near stoichiometric formulation with excess of epoxy monomer. Plasticization due to absorbed -OH results on a significant increase of the deformability of these formulations. The amine rich mixtures have the more stable structures, although plasticization due to moisture absorption from the surrounding environment also produces an increase on the deformability of all, but one, of the formulations investigated.