Chitosan was acetylated during 2, 5 and 10h and physical gels were obtained at different polymer concentrations in N,N-dimethylacetamide containing 5% of LiCl. Acetylation was confirmed by infrared spectroscopy and 13C NMR, and degrees of acetylation in the range of 0.82-0.91 were determined by NMR. The O-acetylation degree (0.12-0.15) was exclusively determined by a volumetric method. Rheological studies showed that the storage modulus values were smaller for the more acetylated samples and increased with the temperature and the polymer concentration. All the gels presented storage modulus superior to loss modulus, evidencing more elastic than viscous characteristics. The results obtained in this work suggest a gelation process based on a balance between O and N-acetylation and intermolecular bonds.

In this work, samples of chitosan obtained in different conditions were characterized by molecular weight distribution, using Gel Permeation Chromatography (GPC), in two different solvents. It was observed that the increase in the number of deacetylation steps promotes a increase in the degree of deacetylation followed by a decrease in the average of molecular weight and polydispersion. The GPC curves obtained for chitosan samples in the two solvents used (CH3COOH 0.30 mol/dm³ - CH3CONa 0.20 mol/dm³ and CH3COOH 0.10 mol/dm³ <FONT FACE="Symbol">-</FONT> NaCl 0.20 mol/dm³) showed small difference in elution volume, but significant changes in the average molecular weight (Mn and Mw) and polydispersion that, in agree with the values of Huggins constant, present evidences of chitosan aggregates formation in the second solvent.