The aim of this paper was to evaluate a possible correlation between obturation limits and leakage. Thirty-six extracted human mandibular incisors were used, characterized by straight and single canals, non-anatomical complexities, absence of previous endodontic treatment, complete root formation and patent foramen. For standardization of the specimens for the leakage analysis, foraminal instrumentation was performed up to a Flexofile #25 (Dentsply-Maillefer, Ballaigues, Switzerland). All specimens were instrumented and filled following the same protocol, and the obturation limits were measured using Axiovision 4.5 Software (Carl Zeiss Vision, Hallbergmoos, Germany). The specimens were then separated into three groups (n = 12) according to the following variables: Group I - obturation limits ranging from 0 mm to 0.76 mm of the main apical foramen. Group II - obturation limits ranging from 0.77 mm to 0.98 mm of the main apical foramen. Group III - obturation limits ranging from 0.99 mm to 1.68 mm of the main apical foramen. Apical leakage was quantified by fluid filtration. The analyses were confronted using Pearson's test (p > 0.05). Groups I, II and III showed Pearson correlation values (r2) of -0.152, -0.186 and 0.058, respectively. No correlation was found between the obturation limits and apical leakage

A liberação de monômeros residuais pode afetar o comportamento clínico e a biocompatibilidade dos materiais resinosos. O objetivo deste estudo foi detectar e quantificar os principais monômeros residuais liberados de resinas compostas, usando cromatografia líquida de alta performance (HPLC). Discos foram construídos de resinas compostas de uso odontológico (Herculite XRV, Tetric Ceram and Filtek Z250) e imersos em água deionizada a 37ºC durante 28 dias, com mudanças de água em 24 horas, 7, 14 e 21 dias. As concentrações médias dos monômeros residuais foram submetidas ao teste de Kruskal-Wallis (p<0,05). Tetric Ceram apresentou as maiores concentrações de monômeros lixiviados. Bis-GMA foi o monômero liberado em menores concentrações para todos os materiais. Não houve diferença estatística significante entre TEGDMA e UDMA. A maioria dos monômeros demonstrou máxima concentração no período de 7 dias. A análise por meio de HPLC identificou Bis-GMA, TEGDMA e UDMA em quantidades detectáveis para todas as resinas compostas testadas.

The aim of this study was to detect and quantify the main residual monomers released from composites, using high performance liquid chromatography (HPLC). Discs were made with dental composites (Herculite XRV, Tetric Ceram and Filtek Z250) and immersed in deionized water at 37ºC for 28 days, with water changes in 1, 7, 14 and 21 days. The mean concentration of residual monomers were subject to the Kruskal-Wallis test (p<0.05). Tetric Ceram exhibited significantly higher concentrations of leached monomers. Bis-GMA was the monomer released in lower concentrations for all the materials. There was no statistical difference between the amounts of TEGDMA and UDMA. Most of the monomers demonstrated maximal concentration at the 7-day period. The HPLC analysis identified Bis-GMA, TEGDMA and UDMA in detectable quantities for all the tested composites.