ABSTRACT This study evaluated the influence of different levels of power density on resin polymerization in the staining of composite resins. Thirty-six specimens were made with composite resin (Z350 3M ESPE) with cylindrical Teflon matrix (8 mm X 1 mm). The light curing was performed with different degrees of power density for each group (n=12): 300mW/cm², 700mW/cm² e 1000mW/cm². Afterwards, the specimens had their color checked, with the help of a spectrophotometer and immersed in coffee solution during 7 days. After, a new measuring was done (CIEL*a*b* color system). Results showed, for Δa, only G1000 group obtained a significantly lower value, and the same result was found in the evaluation of Δb. For ΔE and ΔL, no significant differences were found between groups. It is concluded that, low and medium power density entails more reddish and bluish composite resin, while the specimens submitted to high power density and then immersed in coffee did not present color change in a short term.

Resumo Objetivo: avaliar o efeito de curto prazo de dois protocolos de desafio erosivo, in vitro, na resistência adesiva de braquetes ortodônticos metálicos em esmalte bovino. Métodos: Sessenta incisivos bovinos foram selecionados e divididos aleatoriamente em seis grupos: SA7 (saliva artificial - 7 dias, Grupo Controle); CC7 (Coca-Cola® - 7 dias); SL7 (suco de limão - 7 dias); SA30 (saliva artificial - 30 dias, Grupo Controle); CC30 (Coca-Cola® - 30 dias); SL30 (suco de limão - 30 dias). Foi realizado o teste de microdureza antes do desafio erosivo, para verificar a padronização das amostras. A imersão foi realizada quatro vezes ao dia, por cinco minutos, durante 7 ou 30 dias. Finalizadas as imersões, os braquetes foram colados e, após 48 horas, foi avaliada a resistência ao cisalhamento. O Índice de Adesivo Remanescente (IAR) também foi avaliado. Para análise dos dados, foram utilizados os testes ANOVA dois fatores, seguido do post-hoc de Tukey e teste t de Student para amostras pareadas, e o teste não-paramétrico de Kruskal-Wallis (α?#8197;= 5%). Resultados: a média e o desvio-padrão do teste de microdureza das amostras totais foi igual a 281,89 ± 44,51 KHN. Não houve diferença estatisticamente significativa na resistência ao cisalhamento para o fator tempo (7 ou 30 dias; F5,54= 0,105; p= 0,901). Contudo, houve diferença estatisticamente significativa para o fator solução (F5,54=6,671; p= 0,003). Essas diferenças ocorreram entre as soluções de Saliva x Coca-Cola® (p= 0,003) e Coca-Cola® x suco de limão (p= 0,029). Ao avaliar o Índice de Adesivo Remanescente, não foi possível verificar diferença significativa entre os grupos. Conclusões: o tempo de imersão utilizado nos protocolos de erosão não afetou a resistência de união dos braquetes aos dentes. A Coca-Cola® induziu valores de resistência ao cisalhamento significativamente mais altos do que o suco de limão e a saliva artificial. No entanto, os efeitos em curto prazo de 7 e 30 dias, nesse estudo in vitro, não podem ser extrapolados para os estudos in vivo. Estudos clínicos devem ser conduzidos, fundamentando os resultados laboratoriais.

Abstract Objective: To assess the short-term effect of two in vitro erosive challenge protocols on the bond strength of metal orthodontic brackets on bovine enamel. Methods: Sixty bovine incisors were selected and randomly divided into six groups: AS7 (artificial saliva - 7 days, Control Group); CC7 (Coca-Cola™ - 7 days); LJ7 (lime juice - 7 days); AS30 (artificial saliva - 30 days, Control Group); CC30 (Coca-Cola™ - 30 days); LJ30 (lime juice - 30 days). Microhardness testing was performed prior to the erosive challenge to verify the standardization of samples. Immersion was performed 4x/day for five minutes, for either 7 or 30 days. After immersions were concluded, the brackets were bonded and shear bond strength was assessed after 48 hours. The Adhesive Remnant Index (ARI) was also assessed. Data were analyzed by two-way ANOVA, followed by Tukey’s post-hoc and Student’s t test for paired samples, and the Kruskal-Wallis non-parametric test (α = 5%). Results: The mean and standard deviation of microhardness testing of total samples were 281.89 ± 44.51 KHN. There was no statistically significant difference in shear bond strength for the time factor (7 or 30 days; F5.54= 0.105; p = 0.901). However, there was a statistically significant difference for the solution factor (F5.54= 6.671; p = 0.003). These differences occurred among solutions of Saliva x Coca-Cola™ (p = 0.003) and Coca-Cola™ x Lime Juice (p= 0.029). The assessment of the Adhesive Remnant Index showed no significant difference between groups. Conclusions: The immersion time used in the erosion protocols did not affect the bond strength of brackets to teeth. Coca-Cola™ induced significantly higher shear bond strength values than lime juice and artificial saliva. However, the short term effects of 7/30 days in this in vitro study may not be extrapolated for in vivo ones. Clinical studies should be conducted, substantiating the laboratory results.

Abstract Purpose: This study determined the effectiveness of the preemptive administration of etodolac on risk and intensity of tooth sensitivity and the bleaching effect caused by in-office bleaching using 35% hydrogen peroxide. Material and methods: Fifty patients were selected for this tripleblind, randomized, crossover, and placebo-controlled clinical trial. Etodolac (400 mg) or placebo was administrated in a single-dose 1 hour prior to the bleaching procedure. The whitening treatment with 35% hydrogen peroxide was carried out in two sessions with a 7-day interval. Tooth sensitivity was assessed before, during, and 24 hours after the procedure using the analog visual scale and the verbal rating scale. Color alteration was assessed by a bleach guide scale, 7 days after each session. Relative risk of sensitivity was calculated and adjusted by session, while overall risk was compared by the McNemar's test. Data on the sensitivity level of both scales and color shade were subjected to Friedman, Wilcoxon, and Mann-Whitney tests, respectively (α=0.05). Results: The preemptive administration of etodolac did not affect the risk of tooth sensitivity and the level of sensitivity reported, regardless of the time of evaluation and scale used. The sequence of treatment allocation did not affect bleaching effectiveness, while the second session resulted in additional color modification. The preemptive administration of etodolac in a single dose 1 hour prior to in-office tooth bleaching did not alter tooth color, and the risk and intensity of tooth sensitivity reported by patients. Conclusion: A single-dose preemptive administration of 400 mg of etodolac did not affect either risk of tooth sensitivity or level of sensitivity reported by patients, during or after the in-office tooth bleaching procedure.

Apesar da alta taxa de sucesso, os pacientes comumente relatam a ocorrência de sensibilidade dental durante os procedimentos clareadores em consultório. Recentemente, foi demostrado que o uso de uma moldeira customizada (denominada de técnica de consultório selada) reduz a penetração de peróxido. O objetivo deste ensaio clínico randomizado foi avaliar sensibilidade dentária e eficiência de clareamento do clareamento selado, em comparação com a técnica convencional de consultório. Vinte pacientes foram aleatoriamente divididos em dois grupos. Em ambos os grupos, um gel de peróxido de hidrogênio a 35% foi usado em uma simples aplicação de 45 minutos. Para a técnica selada, uma moldeira de clareamento customizada foi confeccionada e cuidadosamente posicionada sobre o agente clareador durante a sessão. A cor foi registrada no início, 7 e 28 dias após a sessão de clareamento usando a espectrofotômetro Vita easy shade. Sensibilidade dental foi registrada durante (20 e 40 minutos) e imediatamente após o tratamento usando uma escala visual analógica. A eficácia do clareamento foi avaliada por ANOVA de medidas repetidas, enquanto o risco absoluto de sensibilidade dental e a sua intensidade foram avaliados pelos testes de Fisher e Mann-Whitney, respectivamente (α=0.05). Nenhuma diferença na eficácia do clareamento foi observada entre as técnicas convencional (7.4 e 8.1 ΔE) e selada (7.8 e 8.3 ΔE) para ambos os tempos de avaliação. Nenhuma diferença foi observada em relação ao risco de sensibilidade dental (p = 0,15). A técnica selada mostrou uma significante diminuição da intensidade de sensibilidade após 40 minutos (p = 0,03). A técnica selada de clareamento reduziu a intensidade da sensibilidade durante o procedimento clareador, sem afetar a eficácia do clareamento

Regardless of the high success rate, patients commonly report the occurrence of tooth sensitivity during the in-office bleaching procedures. Recently, it has been demonstrated that using a customized tray (called sealed in-office bleaching technique) reduces peroxide penetration. The aim of this randomized clinical study was to evaluate tooth sensitivity and bleaching efficacy of sealed bleaching, in comparison with a conventional in-office technique. Twenty patients were randomized allocated in two groups in which 35% hydrogen peroxide gel was used in a single 45-min application. For the sealed technique, a customized bleaching tray was fabricated and carefully positioned over the bleaching agent during the session. The color was recorded at a baseline, 7 and 28 days after the bleaching session, using Vita Easy Shade spectrophotometer. Tooth sensitivity was recorded during (20 and 40 min) and immediately after the treatment using a visual analogue scale. The bleaching efficacy was evaluated by repeated-measures ANOVA, while the absolute risk of tooth sensitivity and its intensity were evaluated by Fisher's exact and Mann-Whitney tests, respectively (α=0.05). No significant difference on bleaching efficacy was observed between the conventional (7.4 and 8.1 ΔE) and sealed techniques (7.8 and 8.3 ΔE) at both evaluation periods. No significant difference was observed regarding the absolute risk of tooth sensitivity (p=0.15). Sealed technique showed a significant decrease of sensitivity intensity after 40 min (p=0.03). Sealed bleaching technique was able to reduce the sensitivity intensity during the bleaching procedure, without jeopardizing the bleaching efficacy

Direct composite resin restorations have become a viable alternative for patients that require anterior restorative procedures to be integrated to the other teeth that compose the smile, especially for presenting satisfactory esthetic results and minimum wear of the dental structure. Technological evolution along with a better understanding of the behavior of dental tissues to light incidence has allowed the development of new composite resins with better mechanical and optical properties, making possible a more artistic approach for anterior restorations. The combination of the increasing demand of patients for esthetics and the capacity to preserve the dental structure resulted in the development of different incremental techniques for restoring fractured anterior teeth in a natural way. In order to achieve esthetic excellence, dentists should understand and apply artistic and scientific principles when choosing color of restorative materials, as well as during the insertion of the composite resin. The discussion of these strategies will be divided into two papers. In this paper, the criteria for color and material selection to obtain a natural reproduction of the lost dental structures and an imperceptible restoration will be addressed.