Two types of crustacean commercial chitosans (CS1, CS2) were dissolved in lactic acid solutions, hydrolysed by lysozyme and finally fractioned by methanol solutions into two parts containing chito-oligomers (CS-O1, CS-O2). The antioxidant power and antimicrobial properties of both fractions were studied and compared with non-hydrolysed CS1 and CS2. The antioxidant properties were determined by the ferric ion reducing antioxidant power (FRAP) method while the bioactive properties were evaluated against a strain of Listeria monocytogenes. CS-O obtained from the solid fraction of the chito-oligomers solid fractions treated with 90% methanol showed the highest reducing power. Microbiological tests showed that CS-O exhibit higher antilisterial activity than CS.

Glioxal pode ser obtido a partir de biomassa (como da oxidação de lipídeos) e não é tóxico ou volátil, tendo sido por isso utilizado no presente trabalho como substituto de formaldeído na preparação de resina fenólica do tipo novolaca, sendo usado como catalisador o ácido oxálico, que também pode ser obtido de fontes renováveis. A resina glioxal-fenol foi utilizada na preparação de compósitos reforçados com celulose microcristalina (CM, 30, 50 e 70% em massa), uma celulose com elevada área superficial. As imagens de microscopia eletrônica de varredura (MEV) das superfícies fraturadas demonstraram que os compósitos apresentaram boa interface reforço/matriz, consequência da elevada área superficial da CM e presença de grupos polares (hidroxilas) tanto na matriz como na celulose, o que permitiu a formação de ligações hidrogênio, favorecendo a compatibilidade entre ambas. A análise térmica dinâmico-mecânica (DMTA) demonstrou que todos os compósitos apresentaram elevado módulo de armazenamento à temperatura ambiente. Além disso, o compósito reforçado com 30% de CM apresentou baixa absorção de água, comparável à do termorrígido fenólico, que é utilizado em escala industrial. Os resultados demonstraram que compósitos com boas propriedades podem ser preparados usando elevada proporção de materiais obtidos de biomassa.

Glyoxal, which can be obtained from biomass (as by lipids oxidation), is non-toxic and non-volatile. It was used as a substitute of formaldehyde, which does not have these properties, in the synthesis of a novolac-type phenolic resin, using oxalic acid as a catalyst, which can also be obtained from renewable sources. The glyoxal-phenol resin was used in the preparation of composites reinforced with microcrystalline cellulose (MCC 30, 50, and 70% w/w). Scanning electron microscopy (SEM) images of the fractured surfaces showed that the composites presented a good reinforcement/matrix interface. This can be attributed to the high surface area of the MCC and also to the presence of polar groups (hydroxyl) in both cellulose and matrix, which allowed the formation of hydrogen bonds, leading to a good adhesion between the components present at the interface. Dynamic mechanical thermoanalysis (DMTA) showed that all of the obtained composites have high storage modulus at room temperature. Moreover, the composite reinforced with 30% of MCC showed the lowest water absorption, almost the same as that of the phenolic thermoset, which is used in industrial applications. The results showed that composites with good properties can be prepared using high proportions of materials obtained from biomass.

Fibras de bagaço de cana-de-açúcar não alvejadas (FBC) e alvejadas com peróxido de hidrogênio (FBC-AP) foram enxertadas com o absorvedor de UV hidroxifenilbenzotriazol (1) e/ou com um radical nitróxido do tipo piperidiniloxi (3). As fibras FBC-AP foram também acetiladas com anidrido acético. A fotossensibilidade dessas fibras à radiação UV foi avaliada comparativamente, empregando coordenadas Lab color, assim como pela monitoração dos seus espectros de reflectância difusa no UV-Visível. As fibras FBC mostraram-se fotoestáveis, enquanto que as FBC-AP apresentaram certa sensibilidade à radiação UV. A estabilidade das FBC deve-se à presença de unidades do composto fotoestável p-hidroxifenilpropano, proveniente dos fragmentos de lignina. As fibras FBC enxertadas e não-enxertadas apresentam comportamentos similares frente à radiação UV e Visível enquanto que as FBC-AP enxertadas são fotoestabilizadas pela presença de 2 ou 4, ou ambos. A acetilação das fibras FBC-AP induz a fotoestabilização, em adição a certo efeito de fotoalvejamento. O fotoalvejamento foi também apresentado por medidas de emissão de fluorescência. Como conseqüência dessas observações, as fibras FBC devem ser consideradas como materiais lignocelulósicos com elevado potencial de aplicação em ambientes externos.

Unbleached (SCB) and peroxide bleached (PB-SCB) sugarcane bagasse fibers were grafted with hydroxyphenylbenzotriazole UV absorber (1) and/or hindered nitroxide radical of piperidinyloxy type (3). PB-SCB fibers were also acetylated with acetic anhydride. The photosensitivity of the various fibers to UV light was comparatively evaluated using Lab color coordinates and by monitoring their UV-Visible diffuse reflectance spectra. SCB fibers were found to be photostable whereas PB-SCB fibers presented some sensitivity to UV light. The stability of SCB fibers was attributed to the presence of photostable para-hydroxyphenylpropane units in SCB lignin. The grafted and non-grafted SCB fibers showed similar behaviors against UV-Visible light whereas grafted PB-SCB were photostabilized by the presence of 2 or 4 or both. Acetylation of PB-SCB fibers induced photostabilization in addition to some photobleaching effect. The photobleaching was also revealed by fluorescence emission studies. As a consequence of these observations, SCB fibers might be considered to have a high potential for lignocellulosic materials to be used outdoors.