The aim of this study was to evaluate the early and 12-month bond strength of two adhesive systems (Single Bond-SB and One Step-OS) applied to demineralized dentin (WH) and demineralized/NaOCl-treated dentin (H). Twenty flat dentin surfaces were exposed, etched, rinsed and slightly dried. For the H groups, a solution of 10% NaOCl was applied for 60 s, rinsed (15 s) and slightly dried. The adhesives were applied according to the manufacturer's instructions and composite resin crowns were incrementally constructed. After 24 h (water-37ºC), the specimens was sectioned in order to obtain resin-dentin sticks (0.8 mm²). The specimens were tested in microtensile (0.5 mm/min) immediately (IM) or after 12 months of water storage (12M). The data (MPa) were subjected to ANOVA and Tukey's test (a=0.05). Only the main factors adhesive and time were significant (p=0.004 and p=0.003, respectively). SB (42.3±9.1) showed higher bond strengths than OS (33.6±11.6). The mean bond strength for IM-group (42.5±8.7) was statistically superior to 12M (33.3±11.8). The use of 10% NaOCl, after acid etching, did not improve the immediate and the long-term resin-dentin bond strength.

Desde a introdução de sistemas adesivos nos procedimentos restauradores com materiais estéticos, tem-se estudado de forma abrangente o tipo de tratamento na superfície dentinária para se consagrar uma técnica ideal. A utilização do ácido fosfórico a 37% sobre a dentina é atualmente ainda o método que mais se domina em termos de adesividade. Porém, métodos de tratamento alternativos, na dentina, têm sido discutidos na literatura, entre eles a aplicação de alguns tipos de irradiação a laser. O objetivo desta pesquisa foi avaliar morfologicamente a união adesivo/resina composta e dentina irradiada com laser Er:YAG e laser Nd:YAG num estudo comparativo por microscopia de varredura, utilizados em substituição ao condicionamento ácido ou associados ao mesmo. Foram utilizados dentes bovinos recém-extraídos, que receberam um preparo de cavidade de classe V, e restauração com sistema adesivo e resina composta fotoativada. Como variantes alguns deles receberam o tratamento prévio de irradiação com laser Er:YAG e outros de irradiação com laser Nd:YAG, à aplicação do agente adesivo e da resina composta. As amostras foram seccionadas, preparadas para microscopia de varredura e submetidas a uma análise morfológica, e foram feitos os registros por meio de fotomicrografias. Com base nessas observações microscópicas, concluímos que somente no tratamento da superfície da dentina com laser Er:YAG e condicionamento ácido houve penetração da resina na dentina. Nos tratamentos com laser Nd:YAG, houve apenas aparente superposição da resina na superfície dentinária, sugerindo que houve oclusão dos túbulos com características de fusão na dentina superficial.

Since bonding systems were introduced in the restorative procedures carried out with esthetic materials, the treatment of dentin surfaces has been widely studied in order to establish the ideal technique. The application of 37% phosphoric acid on dentin is still the best known method. However, alternative methods for treating the dentin surface have been discussed in the literature, including the utilization of some kinds of laser irradiation. The purpose of this research was to morphologically evaluate the bond between adhesive materials and the dentin treated with Er:YAG and Nd:YAG lasers, in a comparative study by means of scanning electron microscopy (SEM). Irradiation either substituted acid etching, or was associated to it. Recently extracted bovine incisors were utilized. They received class V cavity preparations and were restored with a bonding system and a light-cured composite resin. Meanwhile, some of the teeth underwent irradiation with Er:YAG laser or Nd:YAG laser before the application of the bonding agent and the composite resin. The samples were selected, prepared for SEM and submitted to morphological analysis. Data were registered in photomicrographs. Based on the microscopic observations, we concluded that only in the dentin surfaces submitted to irradiation with Er:YAG laser and to acid conditioning there was penetration of resin into the dentine. With the Nd:YAG laser treatment, there was only visual superposition of resin over the dentin surface, which suggests that there was only occlusion of the tubules, with characteristics of fusion in the superficial dentine.

O objetivo desse estudo foi avaliar, in vitro, a microinfiltração marginal em cavidades de classe V submetidas ao tratamento com laser de Er:YAG e restauradas com materiais estéticos. Foram selecionados 60 dentes humanos e realizados preparos de classe V no terço cervical das faces vestibular e lingual. A técnica restauradora seguiu as especificações dos fabricantes. Os dentes foram divididos em três grupos de 20 dentes: Grupo 1 (controle), Grupo 2: procedeu-se previamente à restauração um tratamento com laser de Er:YAG na superfície do esmalte do ângulo cavo-superficial, Grupo 3: antes da restauração, aplicou-se uma fina camada de cimento de Ca(OH)2 na parede axial. Cada grupo foi dividido em quatro subgrupos e restaurados com materiais estéticos diferentes. Todos os dentes foram submetidos a ciclagem térmica e técnica de infiltração com nitrato de prata a 50%. Com base nos resultados, concluiu-se que existem diferenças entre as doze condições experimentais realizadas. As amostras que apresentaram maior microinfiltração foram, em primeiro lugar, as com tratamento com laser de Er:YAG e restauradas com cimento de ionômero de vidro fotoativado. Em segundo, as tratadas com laser de Er:YAG e restauradas com a técnica do sanduíche (cimento de ionômero de vidro convencional + resina composta fotoativada). Em terceiro, as restauradas com cimento de ionômero de vidro fotoativado, e por último as restauradas com a técnica do sanduíche.

The aim of this in vitro study was to evaluate marginal microleakage in class V preparations submitted to treatment with Er:YAG laser and restored with aesthetic materials. Sixty human molars were selected and class V cavities were prepared on the buccal and lingual aspects of their cervical thirds. The restorative technique followed the instructions of the manufacturers. The samples were divided in 3 groups of 20 teeth each: Group 1 - control; Group 2 - Er:YAG laser was applied on the enamel margin before the restoration was placed; Group 3 - a thin layer of calcium hydroxide was applied on the axial wall before the restoration was placed. Each group was divided in 4 sub-groups and the teeth were restored with different aesthetic materials. All samples were submitted to thermocycling and stained with 50% silver nitrate. Based on the obtained results, we could conclude that there are statistically significant differences between the 12 experimental conditions tested. The samples which presented the greatest microleakage were those treated with Er:YAG laser and restored with light-cured glass ionomer cement, followed by those that received Er:YAG laser and the sandwich technique, the cavities restored with light-cured glass ionomer cement and those restored by means of the sandwich technique, in this order.

Neste estudo, avaliou-se a rugosidade superficial de resinas classificadas como compactáveis e uma híbrida tradicional comparando-se diferentes técnicas de polimento. Confeccionaram-se corpos-de-prova, que foram armazenados em água destilada por 24 horas e posteriormente submetidos a duas técnicas de tratamento superficial, em que foram empregados dois sistemas de discos de acabamento e polimento e pontas siliconizadas. Os resultados revelaram maior rugosidade superficial da resina AlertTM em relação a Solitaire® e Degufill Mineral®, não havendo diferenças estatisticamente significantes entre as últimas citadas. A rugosidade superficial das restaurações cujo polimento foi executado com as pontas Enhance® foi maior que o polimento obtido com os sistemas de discos, não havendo diferenças estatisticamente significante entre esses.

In this study, the superficial roughness of two composite resins classified as condensable and of a traditional hybrid composite resin was analyzed after different polishing techniques. Test specimens were confected, immersed in distilled water for 24 hours and submitted to two different techniques of superficial treatment, in which disc systems (Sof-LexTM and Super Snap®) and silicon tips (Enhance®) were utilized. The results revealed the greater superficial roughness of AlertTM, when compared with Solitaire® and Degufill Mineral® - no statistically significant differences were observed between the last two materials. The superficial roughness of the specimens polished with Enhance® tips was greater than that of the specimens polished with discs and there were no statistically significant differences between both disc systems.

Este trabalho teve como objetivo comparar a resistência à tração de três sistemas adesivos associados a resina composta aderidos à superfície dentinária. Quarenta e cinco superfícies de dentina foram obtidas a partir de molares humanos extraídos, sobre elas foi preparado "smear layer" e foram divididas em 3 grupos: G1) adesivo autocondicionante + resina micro-híbrida; G2) adesivo de componente único + ácido e resina micro-híbrida e G3) adesivo convencional (ácido + "primer" + bond) + resina micro-híbrida, aplicados de acordo com as instruções dos fabricantes. Os corpos-de-prova foram preparados para teste de tração, imersos em água destilada por 24 horas a 37ºC. Findo este tempo, o teste de tração foi realizado em máquina de ensaio Inströn com velocidade constante de 0,5 mm/min. Os resultados foram expressos em MPa e submetidos a análise de variância (p < 0,05). Os autores concluíram que: o tipo de sistema adesivo influenciou na resistência à tração das resinas compostas testadas; o sistema adesivo de componente único apresentou os melhores resultados de resistência adesiva.

The aim of this in vitro study was to compare the tensile bond strength of 3 different bonding systems, associated to composite resins, bonded to dentinal surfaces. Forty-four dentinal surfaces were obtained from recently extracted human molars. A standardized smear layer was obtained and the surfaces were divided in 3 groups: G1) self etch + microhybrid composite; G2) single-component adhesive + phosphoric acid + microhybrid composite and G3) conventional system (acid + primer + bond) + microhybrid composite. Specimens made of composite resin were constructed in the shape of an inverted truncated cone with 3 mm of diameter. Tensile bond strength test was performed at the speed of 0.5 mm/min, and the results were expressed in MPa. The analysis of variance ANOVA (p < 0.05) determined that the type of bonding system used influenced tensile bond strength. Tukey’s test, however, showed that the results of the comparison between G2 and G3 were the only statistically significant ones, with G2 showing greater values of tensile bond strength.

As constantes recidivas dos tratamentos preconizados para a hipersensibilidade dentinária são causa de estudos a respeito desta patologia. Neste trabalho, in vitro, nos propomos a avaliar, por meio de microscopia eletrônica de varredura, a possível formação de película impermeabilizadora quando da aplicação de substâncias dessensibilizantes, acompanhada de condicionamento ácido da dentina. Discos de dentina, foram utilizados onde foi preparado um esfregaço padronizado, realizado condicionamento ácido e aplicação das substâncias testadas, à base de glutaraldeído, oxalato e fluoretos. Para compor o grupo controle um corpo-de-prova foi mantido sem tratamento e outro apenas condicionado com ácido. Dos resultados morfológicos obtidos pode-se concluir que o condicionamento ácido prévio ao tratamento com substâncias à base de glutaraldeído e de oxalato não é capaz de formar uma película uniforme, impermeabilizante sobre a dentina. O uso de fluoretos forma uma camada sobre a dentina facilmente removível, não produzindo porém efeitos a longo prazo nestes tipos de tratamento.

The constant recurrence of indicated treatments for dentine hypersensitivity has motivated many studies on the subject, in the search for good long-term clinical results. The aim of this in vitro study was to evaluate, by SEM, the formation of an impermeable film when desensitizing substances are applied after acid etching of the dentine surface. Dentine discs with a standardized smear layer were acid etched with 35% phosphoric acid and substances based on glutaraldehyde, oxalate and sodium fluoride were applied according to manufacturer’s instructions. Discs without treatment were used as the control group and only one of them was acid etched. Morphological results showed that acid etching of the dentine surface prior to the application of substances based on glutaraldehyde and oxalate are not able to form a uniform, impermeable film over dentine. On the other hand, sodium fluoride containing substances can form a layer over dentine, but it is easily removable, probably with no long-term effect.