Objective: The aim of the present study was to analyze the influence of root canal and glass fiber post diameters on the biomechanical behavior of the dentin/cement/post interface of a root-filled tooth using 3D finite element analysis. Material and Methods: Six models were built using micro-CT imaging data and SolidWorks 2007 software, varying the root canal (C) and the glass fiber post (P) diameters: C1P1-C=1 mm and P=1 mm; C2P1-C=2 mm and P=1 mm; C2P2-C=2 mm and P=2 mm; C3P1-C=3 mm and P=1 mm; C3P2-C=3 mm and P=2 mm; and C3P3-C=3 mm and P=3 mm. The numerical analysis was conducted with ANSYS Workbench 10.0. An oblique force (180 N at 45º) was applied to the palatal surface of the central incisor. The periodontal ligament surface was constrained on the three axes (x=y=z=0). Maximum principal stress (σmax) values were evaluated for the root dentin, cement layer, and glass fiber post. Results: The most evident stress was observed in the glass fiber post at C3P1 (323 MPa), and the maximum stress in the cement layer occurred at C1P1 (43.2 MPa). The stress on the root dentin was almost constant in all models with a peak in tension at C2P1 (64.5 MPa). CONCLUSION: The greatest discrepancy between root canal and post diameters is favorable for stress concentration at the post surface. The dentin remaining after the various root canal preparations did not increase the stress levels on the root.

OBJECTIVES: The non-homogenous aspect of periodontal ligament (PDL) has been examined using finite element analysis (FEA) to better simulate PDL behavior. The aim of this study was to assess, by 2-D FEA, the influence of non-homogenous PDL on the stress distribution when the free-end saddle removable partial denture (RPD) is partially supported by an osseointegrated implant. MATERIAL AND METHODS: Six finite element (FE) models of a partially edentulous mandible were created to represent two types of PDL (non-homogenous and homogenous) and two types of RPD (conventional RPD, supported by tooth and fibromucosa; and modified RPD, supported by tooth and implant [10.00x3.75 mm]). Two additional Fe models without RPD were used as control models. The non-homogenous PDL was modeled using beam elements to simulate the crest, horizontal, oblique and apical fibers. The load (50 N) was applied in each cusp simultaneously. Regarding boundary conditions the border of alveolar ridge was fixed along the x axis. The FE software (Ansys 10.0) was used to compute the stress fields, and the von Mises stress criterion (svM) was applied to analyze the results. RESULTS: The peak of svM in non-homogenous PDL was higher than that for the homogenous condition. The benefits of implants were enhanced for the non-homogenous PDL condition, with drastic svM reduction on the posterior half of the alveolar ridge. The implant did not reduce the stress on the support tooth for both PDL conditions. Conclusion: The PDL modeled in the non-homogeneous form increased the benefits of the osseointegrated implant in comparison with the homogeneous condition. Using the non-homogenous PDL, the presence of osseointegrated implant did not reduce the stress on the supporting tooth.

O objetivo deste estudo foi avaliar a influência dos altos valores de torque de inserção na distribuição de tensões e deformações no osso cortical e medular. Com base em imagens de tomografia computadorizada, um modelo matemático representativo de um segmento da maxila foi construído utilizando os programas Mimics 11.11 e Solid Works 2010. Seis modelos foram construídos e cada um recebeu um implante com os seguintes torques de inserção no hexágono externo: 30, 40, 50, 60, 70 ou 80 Ncm. O osso cortical e medular foi considerado anisotrópico. A interface osso/implante foi considerada perfeitamente unida. A análise numérica foi realizada através do Ansys Workbench 10.0. A convergência de análise (6%) determinou o refinamento da malha. A tensão máxima principal (σmax) e a deformação máxima principal (εmax) foram obtidos para o osso cortical e medular ao redor do implante. O teste de correlação de Pearson foi utilizado para determinar a correlação entre torque de inserção e de concentração de tensões e deformações no tecido ósseo peri-implantar, considerando o nível de significância de 5%. O aumento no torque de inserção gerou um aumento nos valores σmax e εmax para o osso cortical e medular. O σmax foi menor para o osso medular, com maior variação de tensão entre os torques de inserção. O εmax foi maior no osso medular em relação ao osso cortical. De acordo com a metodologia utilizada e com os limites do estudo, pode-se concluir que torques alto de inserção aumentou as concentrações de tensões de tração e compressão no tecido ósseo peri-implantar.

The aim of this study was to evaluate the influence of the high values of insertion torques on the stress and strain distribution in cortical and cancellous bones. Based on tomography imaging, a representative mathematical model of a partial maxilla was built using Mimics 11.11 and Solid Works 2010 softwares. Six models were built and each of them received an implant with one of the following insertion torques: 30, 40, 50, 60, 70 or 80 Ncm on the external hexagon. The cortical and cancellous bones were considered anisotropic. The bone/implant interface was considered perfectly bonded. The numerical analysis was carried out using Ansys Workbench 10.0. The convergence of analysis (6%) drove the mesh refinement. Maximum principal stress (σmax) and maximum principal strain (εmax) were obtained for cortical and cancellous bones around to implant. Pearson's correlation test was used to determine the correlation between insertion torque and stress concentration in the periimplant bone tissue, considering the significance level at 5%. The increase in the insertion torque generated an increase in the σmax and εmax values for cortical and cancellous bone. The σmax was smaller for the cancellous bone, with greater stress variation among the insertion torques. The εmax was higher in the cancellous bone in comparison to the cortical bone. According to the methodology used and the limits of this study, it can be concluded that higher insertion torques increased tensile and compressive stress concentrations in the periimplant bone tissue.

O objetivo dessa pesquisa foi mensurar a espessura da camada hibrida de adesao (CH), o comprimento dos prolongamentos resinosos (Tags) e a resistencia de uniao (RU) em um mesmo especime e analisar a correlacao entre esses fatores, usando o adesivo autocondicionante Adper Prompt L Pop em dentina higida. Dez molares humanos foram utilizados e apos a realizacao dos procedimentos restauradores, de acordo com os fabricantes, cada especime foi cortado ao meio no sentido mesio/distal. Em uma hemi-seccao dental os especimes foram descalcificados para analise e mensuracao dos tags e da camada hibrida de adesao em microscopia optica comum (AXIOPHOT, 400X). Na outra hemi-seccao, foi realizado o teste de microtracao em uma velocidade de 0,5 mm/min ate sua ruptura. A superficie fraturada foi mensurada e classificada de acordo com o tipo de fratura observada em microscopia eletronica de varredura. Os valores obtidos para os fatores em analise, correspondentes a cada especime foram submetidos a um teste de correlacao. As medias correspondentes a CH, Tags e RU foram 3,36μm, 12,97 μm 14,10 MPa, respectivamente. Nao foi observado correlacao entre a CH e RU (R2= 0,011, p>0,05) e entre os Tags e RU (R2= 0,038). Diante dos resultados, observamos nao haver correlacao entre a camada hibrida e a resistencia a tracao, assim como entre os tags e a resistencia a tracao do sistema adesivo autocondicionante empregado.

The objective of this study was to measure the thickness of the hybrid layer (HLT), length of resin tags (RTL) and bond strength (BS) in the same teeth, using a self-etching adhesive system Adper Prompt L Pop to intact dentin and to analyze the correlation between HLT and RTL and their BS. Ten human molars were used for the restorative procedures and each restored tooth was sectioned in mesio-distal direction. One section was submitted to light microscopy analysis of HLT and RTL (400×). Another section was prepared and submitted to the microtensile bond test (0.5 mm/min). The fractured surfaces were analyzed using scanning electron microscopy to determine the failure pattern. Correlation between HLT and RTL with the BS data was analyzed by linear regression. The mean values of HLT, RTL and BS were 3.36 μm, 12.97 μm and 14.10 MPa, respectively. No significant relationship between BS and HLT (R2= 0.011, p>0.05) and between BS and RTL (R2= 0.038) was observed. The results suggested that there was no significant correlation between the HLT and RTL with the BS of the self-etching adhesive to dentin.

The presence of porosities at the dentin/adhesive interface has been observed with the use of new generation dentin bonding systems. These porosities tend to contradict the concept that etching and hybridization processes occur equally and simultaneously. Therefore, the aim of this study was to evaluate the micromechanical behavior of the hybrid layer (HL) with voids based on a self-etching adhesive system using 3-D finite element (FE) analysis. MATERIAL AND METHODS: Three FE models (Mr) were built: Mr, dentin specimen (41x41x82 μm) with a regular and perfect (i.e. pore-free) HL based on a self-etching adhesive system, restored with composite resin; Mp, similar to M, but containing 25% (v/v) voids in the HL; Mpp, similar to Mr, but containing 50% (v/v) voids in the HL. A tensile load (0.03N) was applied on top of the composite resin. The stress field was obtained by using Ansys Workbench 10.0. The nodes of the base of the specimen were constrained in the x, y and z axes. The maximum principal stress (σmax) was obtained for all structures at the dentin/adhesive interface. RESULTS: The Mpp showed the highest peak of σmax in the HL (32.2 MPa), followed by Mp (30 MPa) and Mr (28.4 MPa). The stress concentration in the peritubular dentin was high in all models (120 MPa). All other structures positioned far from voids showed similar increase of stress. CONCLUSION: Voids incorporated into the HL raised the σmax in this region by 13.5%. This behavior might be responsible for lower bond strengths of self-etching and single-bottle adhesives, as reported in the literature.

The bond strength of composite resins (CRs) to dentin is influenced by the interfacial microstructure of the hybrid layer (HL) and the resin tags (TAG). The contemporary self-etching primer adhesive systems overcame the inconvenient of the etch-and-rinse protocol. Studies, however, have demonstrated that HL thickness and TAG length vary according to the wetting time and additional use of acid-etching prior to self-etching primers. This study investigated the localized stress distribution in the HL and the dentin/adhesive interface. Two HL thicknesses (3 or 6 µm), two TAG lengths (13 or 17 µm) and two loading conditions (perpendicular and oblique-25º) were investigated by the finite element (FE) analysis. Five two-dimensional FE models (M) of a dentin specimen restored with CR (38 x 64 µm) were constructed: M1 - no HL and no TAG; M2 - 3 µm of HL and 13 µm of TAG; M3 - 3 µm of HL and 17 µm of TAG; M4 - 6 µm of HL and 13 µm of TAG; and M5 - 6 µm of HL and 17 µm of TAG. Two distributed loadings (L) (20N) were applied on CR surface: L1 - perpendicular, and L2 - oblique (25º). Fixed interfacial conditions were assigned on the border of the dentin specimen. Ansys 10.0 (Ansys®, Houston, PA, USA) software was used to calculate the stress fields. The peak of von Mises (sigmavM) and maximum principal stress (sigmamax) was higher in L2 than in L1. Microstructures (HL and TAG) had no effect on local stresses for L1. Decreasing HL decreased sigmavM and sigmamax in all structures for L2, but the TAG length had influence only on the peributular dentin. The thickness of HL had more influence on the sigmavM and sigmamax than TAG length. The peritubular dentin and its adjacent structures showed the highest sigmavM and sigmamax, mainly in the oblique loading.