Conventional single superphosphate (SSP) is known as one of the most important and common sources of phosphorus in agriculture. Despite SSP has been widely produced as a fertilizer, a few studies have been done to describe the fundamental aspects of this P-fertilizer, i.e., phase composition, thermal degradation behavior, and solubility kinetics. Therefore, this paper reports on the detailed characterization of SSP powders by correlating their properties with particle size and surface area. Commercial SSP fertilizers were milled under different conditions and the resulting powders were characterized by X-ray diffraction, thermogravimetric analyses, scanning electron microscopy, FT-IR spectroscopy, and solubilization tests. It was observed that short milling times favored the solubilization kinetics, whereas long milling times were deleterious due to agglomeration effects. It was pointed out that agglomeration plays an important role in phosphate availability. These results provided a deeper understanding of SSP powders in microstructural terms, and may be used as a foundation for the development of novel strategies of alternative production of phosphorus fertilizers.

Foram produzidas amostras de amido termoplástico (TPS) reforçadas com materiais de alta área superficial, com o intuito de verificar a variação nas propriedades do polímero, com especial enfoque na sua permeabilidade a vapor d'água. Foram utilizadas como carga a sílica coloidal (área superficial de 122,7 m²/g) e uma zeólita do tipo ZSM-5, produzida em laboratório (área superficial de 261,3 m²/g), em teores de 2 a 10% em massa. Os resultados demonstraram que a adição de ambos os materiais melhorou as propriedades mecânicas do TPS, embora nos maiores teores houve redução da qualidade das interfaces e dessas propriedades, principalmente para a ZSM-5. Em todos os casos a introdução da carga inorgânica reduziu a permeabilidade ao vapor d'água em até 20% quando comparada à permeabilidade do TPS, porém a melhor dispersão da sílica coloidal na matriz permitiu as maiores reduções, apesar da área superficial inferior.

Compositions of thermoplastic starch (TPS) reinforced by high surface area materials were produced, intending to study the variation in polymer properties, focusing on the permeability to water vapor. Colloidal silica (surface area 122.7 m²/g) and a ZSM-5 zeolite (surface area 261.3 m²/g) were used, in loadings from 2 to 10% weight. The results demonstrated that the addition of both materials was favorable to the TPS mechanical properties, however in higher loadings the quality of polymer interfaces and these properties were negatively affected, especially for ZSM-5. In all the cases the inorganic particles reduced the permeability to water vapor in levels below 20% when compared to pure TPS, although the best dispersion of colloidal silica determined better reductions, despite its lower surface area.