We have carried out van der Pauw resistivity and Hall effect measurements on a series of Molecular Beam Epitaxy InAs/GaAs superlattice samples containing InAs quantum dots. Three growth parameters were varied, the InAs coverage, the number of repetitions of the InAs/GaAs layers, and the GaAs spacer thickness. The results can be grouped in two sets, those samples presenting low and high resistivity. The group presenting low resistivity is composed by the samples with GaAs spacer of 30 monolayers (ML) and InAs coverage of 1.9 monolayers. The group presenting high resistivity is composed of samples with GaAs spacer of 40 ML. We claim that the high resistivity characteristic is due to the presence of deep level. Increasing the spacer from 30 to 40 ML decouples the InAs planes favouring the deep level formation.

We have carried out our experiments on a semi-insulating GaAs sample grown by low temperature Molecular Beam Epitaxy. Three parameters were used to fine tune the experiments, namely, temperature, illumination, and applied bias. We have used powerful tools of time series analysis in order to assess the embedding dimension through near false nearest neighbors. We have also measured the maximum Lyapunov exponent and the correlation dimension [1]. The main contribution was in presenting new experimental data and its analysis which presents self-generated chaos.

In this work we present studies for the behavior of impurity breakdown of two GaAs samples grown by Molecular Beam Epitaxy at 200°C and 300°C. We vary the temperature and the illumination intensity. For the sample grown at 200°C, the transport mechanism after the breakdown is of the same type of the main free carriers at low electric fields. Below 100K, a clear dependence of the threshold electric field with temperature was observed. The sample grown at 300°C shows a breakdown due to an acceptor level at 41meV from the valence band. The threshold electric field increases with illumination due to the generation of free electrons by deep levels. A similar behavior was also observed for a Cr doped GaAs sample.