OBJECTIVES: To evaluate the microtensile bond strength (µTBS) of one- (Xeno III, Dentsply) and two-step (Tyrian-One Step Plus, Bisco) self-etching adhesive systems bonded to dentin and cemented to chemically cured (C&B Metabond) or light-cured paste of a dual-cure resin cement (Variolink II, Ivoclar) within a short (24 h) and long period of evaluation (90 days). MATERIAL AND METHODS: Forty recently extracted human molars had their roots removed and their occlusal dentin exposed and ground wet with 600-grit SiC paper. After application of one of the adhesives, the resin cement was applied to the bonded surface and a composite resin block was incrementally built up to a height of 5 mm (n=10). The restored teeth were stored in distilled water at 37ºC for 7 days. The teeth were then cut along two axes (x and y), producing beam-shaped specimens with 0.8 mm² cross-sectional area, which were subjected to µTBS testing at a crosshead speed of 0.05 mm/min and stressed to failure after 24 h or 90 days of storage in water. The µTBS data in MPa were subjected to three-way analysis of variance and Tukey's test (α= 0.05). RESULTS: The interaction effect for all three factors was statistically significant (three-way ANOVA, p<0.001). All eight experimental means (MPa) were compared by the Tukey's test (p<0.05) and the following results were obtained: Tyrian-One Step Plus /C&B/24 h (22.4±7.3); Tyrian-One Step Plus /Variolink II/24 h (39.4±11.6); Xeno III/C&B/24 h (40.3±12.9); Xeno III/Variolink II/24 h (25.8±10.5); Tyrian-One Step Plus /C&B/90 d (22.1±12.8) Tyrian-One Step Plus/VariolinkII/90 d (24.2±14.2); Xeno III/C&B/90 d (27.0±13.5); Xeno III/Variolink II/90 d (33.0±8.9). CONCLUSIONS: Xeno III/Variolink II was the luting agent/adhesive combination that provided the most promising bond strength after 90 days of storage in water.

The aim of this study was to compare intrapulpal temperature increase produced by high-speed handpiece, Er:YAG laser and CVDentus ultrasound tips during cavity preparation. Thirty bovine mandibular incisors with an enamel/dentin thickness of 4 mm at buccal surface had their roots amputated and were allocated to the following groups (n=10): Group I- high-speed handpiece; Group II- noncontact Er:YAG laser (250 mJ/4Hz); and Group III- CVDentus ultrasouns tips. All devices were used with water cooling. Class V cavities were prepared to a depth of 3.5 mm, measured with a periodontal probe. A type T thermocouple was placed inside the pulp chamber to determine the temperature increase (°C), which was recorded by a data acquisition system ADS 2000 IP (Lynx Technology) linked to a notebook computer. Data were analyzed statistically by one-way ANOVA and Tukey's test (p=0.05). The mean temperature rises were: 1.10°C (±0.56) for Group I, 0.84°C (±0.55) for Group II, and 3.00°C (± 1.34) for Group III. There were no statistically significant differences (p>0.05) between Groups I and II, but both of them differed significantly from Group III (p<0.05). In conclusion, the use of Er:YAG laser and high-speed handpiece for cavity preparation resulted in similar temperature increase. Although ultrasound tips generated significantly higher intrapulpal temperature increase, it remained below the critical value of 5.5°C and may be considered safe for use.