The objective of this work is the Hot Filament Chemical Vapor Deposition (HFCVD) of diamond films on stainless steel substrates using a new technique for intermediate barrier forming, made by laser cladding process. In this technique, a powder layer is irradiated by a laser beam to melt the powder layer and the substrate surface layer to create the interlayer. The control of the laser beam parameters allows creating homogeneous coating layers, in rather large area in few seconds. In this work, the silicon carbide powder (SiC) was used to create an intermediate layer. Before the diamond growth, the samples were subjected to the seeding process with diamond powder. The diamond deposition was performed using Hot-Filament CVD reactor and the characterizations were Scanning Electron Microscopy, X-ray diffraction, Raman Scattering Spectroscopy and Scratch Test.

AbstractThis paper shows successful hindering of the negative effects of the cobalt binder in the process of coating WC-Co cutting tools with CVD diamond films. The strategy was creating a boron-rich layer on the surface of the WC-Co substrates as an interlayer to block Co migration. The traditional boriding technique was improved by preheating the salt powders and controlling the brittle region thickness in the substrate surface. These procedures produce a tougher surface for diamond growth. Adding CF4 to the gas mixture also enhanced diamond adhesion to the surface. The adhesion of diamond films to WC-Co substrates was evaluated by indentation tests. Samples were characterized by Scanning Electron Microscopy (SEM), Energy Dispersive X-ray (EDX), X-ray Diffraction (XRD) and Raman Scattering Spectroscopy (RSS).