Novel civil construction materials based on waste can be an optimal alternative for waste management, reducing its improper disposal while engaging an otherwise discarded material as a raw material in other production processes. This research’s main objective was to develop and characterize two novel artificial stones based on waste glass from bottles and aggregated with epoxy resin (ASG-EP) and polyurethane resin (ASG-PU) from castor oil, respectively, as well as the comparison of the two developed materials. Plates were manufactured with 15% of epoxy or 15% polyurethane resins and 85% of waste glass from bottles. The mixture was molded with a process of 6Hz vibration, 600mmHg of vacuum, and hot compaction at 90ºC for EP and 80ºC for PU. Results evidenced that the development of ASGs based on waste glass from bottles is technically and economically viable.

The fique is a plant typical of the Colombian Andes, from which relatively common items are fabricated. One of these is woven fabric extensively applied in sackcloths. The mechanical strength of fique fabric have motivated recent investigations on possible reinforcement of polymer matrix composites. For this purpose its thermo-mechanical behavior was unveiled. In particular, dynamic mechanical analysis (DMA) of fique fabric reinforced polyester matrix composites disclosed improved viscoelastic behavior in association with change in the glass transition temperature. The present work extends this investigation to epoxy matrix, which is one of the most employed thermoset polymer for composite matrix. Fique fabric volumetric fractions of up to 50% are for the first time incorporated into epoxy composites. It was found that these incorporations significantly increased the viscoelastic stiffness of the composite, given by the storage modulus (E’), in the temperature interval from -50 to 170°C. An accentuated softening in viscoelastic stiffness was revealed for all composites above 75°C. Peaks in both the loss modulus (E”) and tangent delta (tan δ), respectively associated with the lower and upper limits of the glass transition temperature, were shifted towards higher temperatures with increasing amount of fique fabric.

Firearms threat has always been a matter of personal concern, especially to soldiers in armed conflicts as well as police officers and civilians involved with public security. A multilayered armor system (MAS) is intended to personal protection against high kinetic energy ammunition, such as that used in rifles. MAS layers are normally composed of a front ceramic followed by a layer that must show both high impact resistance and low weight. Usually, synthetic fiber fabrics, such as aramid in Kevlar® and ultra-high molecular weight polyethylene (UHMWP) in Dyneema® are commonly used as the second layer. Currently, composites reinforced with natural fibers are also being considered as second MAS layer due to their good performance associated with the advantages of being cheaper and environmentally friendly. The fique is a relatively unknown natural fiber extracted from leaves of a plant native of South American Andes. In the present work, fique fibers and fique fabrics incorporated in polyester composite plates with volume fraction of 10, 20 and 30% were ballistic tested. The calculated projectile loss of energy indicated a relatively large energy dissipation by the composite. The tested specimens were statistically treated by the Weibull analysis and were examined by scanning electron microscopy.