Abstract The effects of disinfection by microwave irradiation and immersion in peracetic acid on the physical-mechanical properties of a microwave-activated acrylic resin were evaluated. Specimens of acrylic resin were divided into a control group (specimens not disinfected) and 2 test groups subjected to one disinfection method: microwave irradiation at 850 W for 1 minute or immersion in 50 mL of 0.2% peracetic acid for 5 minutes. Specimens were submitted to Knoop hardness, flexural strength, flexural modulus, Izod impact, water sorption and solubility, glass transition temperature, and degree of conversion tests. Microwave disinfection significantly increased the mean Knoop hardness, Izod impact strength, water sorption, water solubility and glass transition temperature, whereas the flexural properties remained unaffected. Microwave disinfection increased the degree of conversion. Peracetic acid disinfection showed no changes in any properties. Both disinfection techniques did not adversely affect the evaluated properties.

RESUMO Objetivo: Analisar se corantes e fibras de nylon influenciam nas propriedades de uma resina acrílica ativada por energia de micro-ondas. Métodos: Espécimes retangulares e em forma de disco foram confeccionados em resina acrílica rosa médio com e sem fibras de nylon e incolor sem fibras. Para obter os espécimes retangulares, foi utilizada uma matriz de aço inoxidável com as seguintes dimensões: 64 X 10 X 3 (± 0,5mm) e para obter os espécimes em forma de disco, foi utilizada uma matriz com 50mm (± 0,5mm) de diâmetro e 0,5mm (±0,05mm) de espessura. Os mesmos foram randomizados para formar os grupos controle (acrílico incolor sem fibras) e experimentais (rosa médio com e sem fibras), sendo cada grupo composto por dez (10) espécimes retangulares e cinco (5) em forma de disco. Foram os mesmos então submetidos a seis (6) ensaios (resistência ao impacto izod, n=10; dureza knoop, n=10; temperatura de transição vítrea, n=3; sorção e solubilidade, n=5; grau de conversão, n=1; resistência à flexão e módulo de flexão, n=10). Todas as variáveis foram submetidas à análise de variância seguida pelo teste de comparações múltiplas de Tukey, com nível de significância de 5%. Resultados: O grau de conversão foi de 88% para os 3 grupos de resinas e os resultados não mostraram diferença estatisticamente significativa entre os mesmos para cada variável (p>0,05). Conclusão: Os resultados mostraram que o corante e a presença de fibras de nylon em resina acrílica não afetaram as propriedades analisadas nesse estudo.

ABSTRACT Objective: The aim of this study is to analyze if both color and nylon fibers have an influence on microwave-cured acrylic resin properties. Methods: Rectangular and disk-shaped specimens were prepared using acrylic resins; medium pink with and without nylon fibers and colorless without nylon fibers. To obtain the rectangular specimens, a stainless steel die was used with the following dimensions: 64 X 10 x 3 mm (± 0.5mm). To obtain disk-shaped specimens, a die 50mm (±0.5mm) in diameter and 0.5mm (±0.05mm) thick was employed. They were randomized to form groups: control (colorless acrylic) and experimental (medium pink, with and without nylon fibers), with each group consisting of ten (10) specimens rectangular in shape and five (5) disk-shaped. They were analyzed in six (6) assays (izod impact strength, n=10; Knoop hardness, n=10; glass transition temperature, n=3; water sorption and solubility, n=5; degree of monomer/polymer conversion, n=1; flexural strength and flexural modulus, n=10). All variables were subjected to the analysis of variance test followed by Tukey's multiple comparison test, at a 5% level of significance. Results: The analysis of the monomer/polymer degree of conversion did not reveal any difference between the three groups of resins (medium pink, with and without nylon fibers and colorless resin); it was approximately 88%. The results did not show significant differences between the groups for each variable (p>0.05). Conclusion: The results showed that color and presence of nylon fibers in acrylic resins did not affect the properties analyzed in this study.

Objetivo: Avaliar a eficácia dos métodos de desinfecção em microondas e imersão em ácido peracético em resina acrílica termopolimerizável, autopolimerizável e resina acrílica polimerizada por microondas, contaminadas com Candida albicans. Métodos: Cinco amostras foram preparadas para cada tipo de resina acrílica. Todas foram infectadas com Candida Albicans, incubadas a 37 ° C durante 24 h. O grupo submetido a energia de microondas foi irradiada com uma potência de 840W durante 1 minuto e o outro grupo foi submetido a desinfecção por imersão de ácido peracético a 0,2% durante 5 minutos. Resultados: Todas as amostras mostraram estar contaminadas depois do período de incubação. Depois dos diferentes processos de desinfecção, tanto a imersão em 0,2% de ácido peracético, como a irradiação de microondas foram eficazes na desinfecção dos 3 tipos de resinas acrílicas contaminados por Candida Albicans. Conclusão: Concluiu-se que a imersão em ácido peracético 0,2% durante 5 minutos e a irradiação de microondas com potência de 840W durante 1 minuto são métodos eficazes para a desinfecção de resina acrílica termopolimerizável, resina acrílica autopolimerizável e resina acrílica polimerizada por microondas, contaminados com Candida Albicans.

Objective: The objective of this study was to evaluate the effectiveness of disinfection methods in microwave and immersion in peracetic acid in heat-cured, self-cured and microwave-cured acrylic resin, contaminated with Candida albicans. Methods: Five specimens were prepared for each type of acrylic resin. All were infected with Candida Albicans, incubated at 37°C for 24 hours. The group which underwent microwave energy was irradiated with a power of 840W for 1 minute and the other group underwent disinfection by soaking of 0.2% peracetic acid for 5 minutes. Results: All samples proved to be contaminated after the incubation period. After the different processes of disinfection, both immersion in 0.2% peracetic acid as microwave irradiation were effective in disinfection of the 3 types of acrylic resins contaminated by Candida Albicans. Conclusion: Concluded that soaking in 0,2% peracetic acid for 5 minutes with microwave irradiation power 840W for 1 minute are effective methods for disinfecting heat-cured acrylic resin, self-cured acrylic resin and microwave-cured acrylic resin, contaminated with Candida Albicans.

OBJECTIVE: To evaluate the response of elastomeric ligatures in several colors for a 4 mm traction over time. METHODS: Morelli® elastomeric ligatures, were submitted to traction forces using two rods of circular cross section, until a 4 mm distance was reached, matching the approximate diameter of an upper central incisor bracket of the same manufacturer. The ligatures were kept in artificial saliva immersion at 37 ºC. Forces levels were measured immediately (0 h), 2, 4, 6, 8, 10, 12, 24, 48, 72, 96 hours, 1, 2, 3, 4 weeks and results were submitted to two-way repeated-measures ANOVA statistical analysis. RESULTS: The gray samples showed the higher initial values of tensile strength. The lowest values were presented by purple, light pink, green, black and red groups. The greater tensile strength instability was presented by red, black, silver, green and gray groups. The greater tensile strength stability was presented by deep pink, dark blue, blue, purple and light pink groups. CONCLUSION: Elastomeric ligatures do not present stable behavior when suffering traction forces over time and different colors display different behaviors. Deep pink, dark blue, blue, purple and light pink groups, displayed the most stable forces, suggesting that they should be used during the treatment to obtain constant forces.

OBJETIVO: O objetivo deste estudo foi avaliar a eficácia do ácido peracético (PAA) na desinfecção de resinas acrílicas dentais experimentalmente contaminadas com Candida albicans, Escherichia coli, Staphylococcus aureus e Pseudomonas aeruginosa. METODOLOGIA: Quinze corpos de prova (CP) foram utilizados para cada tipo de resina (termopolimerizáveis, autopolimerizáveis e ativados por energia de micro-ondas). Cada CP foi colocado em um tubo teste com meio de cultura contendo uma suspensão de cada microrganismo e incubado. Posteriormente, os CP foram lavados e transferidos para outros tubos contendo 50 mL de água por 5 minutos, em 0,2% de ácido peracético por 5 min ou em glutaraldeído por 30 minutos, plaqueados em ágar de cultura e incubados. O crescimento microbiano foi determinado por contagem de colônias após o plaqueamento. RESULTADO: O crescimento de Candida albicans foi inibido nos tratamentos com ácido peracético e glutaraldeído. O número de colônias nas resinas tratadas com solução salina foi superior a 10(5) UFC/mL. Nas resinas infectadas com E. coli, S. aureus e P. aeruginosa, o crescimento das colônias não foi inibido nas resinas tratadas com salina e ácido peracético, mas foi totalmente inibida pelo glutaraldeído. CONCLUSÃO: A desinfecção com ácido peracético inibiu efetivamente o crescimento de C. albicans em todas as resinas acrílicas.

PURPOSE: The aim of this study was to assess the efficacy of peracetic acid (PAA) for the disinfection of dental acrylic resins experimentally contaminated with Candida albicans, Escherichia coli, Staphylococcus aureus and Pseudomonas aeruginosa. METHODS: Fifteen materials were used for each type of resin (thermosetting, self-curing and microwave-curing). Each material was placed in a test tube containing culture medium with a suspension of each microorganism and then incubated. The materials were rinsed and transferred to other tubes containing 50 mL of water for 5 min, 0.2% peracetic acid for 5 min or glutaraldehyde for 30 min. The materials were placed in the culture agar and incubated. Microbial growth was determined by colony counting after plating. RESULTS: Candida albicans growth was inhibited by peracetic acid and glutaraldehyde treatments. The number of colonies on resins treated with saline was greater than 10(5) CFU/mL. In resins infected with E. coli, S. aureus and P. aeruginosa the colony growth was not inhibited by saline and peracetic acid, but it was totally inhibited by glutaraldehyde. CONCLUSION: Surface disinfection using peracetic acid effectively inhibited C. albicans growth on all acrylic resins.