Abstract: Poly(aspartic acid-citric acid) copolymer (PAC) is a new product of poly(carboxylic acid) scale inhibitor. The study aims to develop a "green" water treatment agent for calcium phosphate scale. The article compares the efficiency of three polymeric antiscalants, poly(aspartic acid-citric acid) copolymer (PAC), polymaleic acid (HPMA) and a compound inhibitor (PAC-HPMA), for calcium phosphate scale prevention under varying experimental conditions. Inhibitor concentration, calcium concentration, system pH, temperature and experimental time were varied to determine their influences on inhibitor performance by the static scale inhibition method. The copolymer (PAC) was characterized by FTIR, 1H NMR and 13C NMR. The compound inhibitor was applied in the actual circulating cooling water system. An atomic force microscope (AFM), X-ray powder diffraction (XRD) and a scale formation process analysis were used to explore the scale inhibition mechanism. The results showed that scale inhibition rates of PAC, HPMA and PAC-HPMA against Ca3(PO4)2 were, respectively, about 23%, 41.5% and 63% when the dosage was 8 mg/L in the experiment. The compound inhibitor showed the better inhibition performance than the above two kinds of monomers. Under the actual working conditions, the inhibition rate of compound inhibitor was close to 100% and completely met the actual application requirements of scale inhibitor in circulating cooling water systems. The main inhibition mechanism was the decomposition-chelation dispersion effect. The compound inhibitor can be used as an efficient "green" scale inhibitor for calcium phosphate.

The dual-concentric-core photonic crystal fiber composed of pure silica and air is proposed in this paper. Around 1.55 ¼m, it exhibits a negative chromatic dispersion as high as -5850 ps/km/nm. Based on multipole method, a systemic and in-depth simulation is realized to investigate the mode characteristics. The explanations to propagation states of the fundamental mode and the second mode are given elaborately. Finally, the variation of structural parameters is investigated to evaluate the tolerance of the fabrication. As a result, the designed fiber can be fabricated easily.