This article reports the synthesis and characterization of pure and N-, B-, and Ag-doped TiO2 and the ability of these oxides to photodegrade methylene blue (MB) under sunlight or UV-ABC radiation. The compounds were synthesized using the sol-gel method and characterized by scanning electron microscopy, X-ray diffraction, diffuse reflectance spectroscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis, and X-ray photoelectron spectroscopy. Photocatalytic efficiency was significantly increased by N-doping, resulting in 98% MB decomposition under UV-ABC irradiation for 180 min. Ag- and B-doped TiO2 lowered MB degradation rates to 52 and 73%, respectively, compared with pure TiO2. The same behavior was observed with exposure to UV-Vis, with 88, 65, 60, and 42% MB removal with N-doped, pure, B-doped, and Ag-doped TiO2, respectively. Under visible light alone, N-doped TiO2 exhibited higher photocatalytic efficiency than commercial P25-type TiO2. Photocatalysis with N-doped TiO2 proved to be a promising alternative for MB degradation, given the potential of employing solar energy, thus minimizing operating costs.

Although the classical Fenton process exhibits a high initial rate of the organic compounds degradation, this process is not complete due to the formation of refractory compounds which resist the attack of the hydroxyl radicals. In the presence of Cu(II), the degradation is slower, but results in a greater reduction of TOC (total organic carbon) measurements of net mineralization at the end of the reaction (t=120min). The addition of Cu(II) ions to classical Fenton reaction conditions (Fe(II) plus H2O2 at pH 3) is shown to accelerate the degradation of organic compounds. This synergic effect causes an approximately 15% additional reduction of the TOC. Voltammetric studies confirm the catalytic role of catechol in the presence of Fe(III)/Fe(II) and Cu(II)/Cu(I). Addition of aliphatic acids to the reaction medium, did not interfere with the cupro-Fenton reaction, but had an inhibitory effect on the classical Fenton reaction, consistent with the following order of interaction with the ion Fe(III): Oxalic Acid (OA) >> Formic Acid (FA) ~ Acetic acid (AA).

The purpose of this study was to synthesize TiO2-polymer composites able to act as photocatalyst membranes. TiO2 catalysts were prepared using the sol-gel method to contain 0.0, 0.5, 1.0, and 2.0 wt.% of embedded Ag particles, subsequently incorporated into natural rubber latex at a weight fraction of 15%. Samples of these ceramic powders were suspended in a latex emulsion (natural rubber), cast in Petri dishes and slowly dried in an oven. The resulting materials were evaluated by X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray, diffuse reflectance spectroscopy, differential scanning calorimetry, thermogravimetry, and photocatalytic assaying using methylene blue as an organic pollutant reference. All composite membranes exhibited good photoactivity conferred by TiO2 powder, with 98% dye fading after 300 min of ultraviolet irradiation.

This article reports the characterization of mesoporous Nb2O5 synthesized by the sol-gel method for application in photocatalysis. The emerging contaminant methylviologen was employed for photocatalytic tests. Parameters inherent to the synthesis process, such as stirring rate, aging temperature, and calcination temperature, were employed for a range of values to improve the synthetic route. The powders obtained were characterized by thermogravimetric analysis, X-ray diffraction, scanning and transmission electron microscopy, specific surface area, infrared spectroscopy, energy-dispersive spectroscopy, and diffuse reflectance spectroscopy. In samples calcined at 450 °C, a mixture of amorphous and hexagonal phases was observed, with a predominance of the former, while in samples calcined at 650 °C the orthorhombic phase predominated. Samples calcined at 450 °C exhibited larger specific surface areas. Mesoporous structures were confirmed for samples T8035M450 and T8045mi450, which displayed higher photoactivity, with roughly 90% removal of methylviologen.

The addition of Cu2+ ions to the classical Fenton reaction (Fe2+ plus H2O2 at pH 3) is found to accelerate the degradation of organic compounds. This synergic effect causes an approximately 15 % additional reduction of the total organic carbon (TOC), representing an overall improvement of the efficiency of the mineralization of phenol. Although Fe2+ exhibits a high initial rate of degradation, the degradation is not complete due to the formation of compounds refractory to the hydroxyl radical. The interference of copper ions on the degradation of phenol by the Fenton reaction was investigated. In the presence of Cu2+, the degradation is slower, but results in a greater reduction of TOC at the end of the reaction (t = 120 min). In the final stages of the reaction, when the Fe3+ in the solution is complexed in the form of ferrioxalate, the copper ions assume the role of the main catalyst of the degradation

Um estudo da interferência de íons Zn2+ na reação de Fenton (Fe2+/Fe3+ + H2O2) na degradação de fenol é relatado. Um dos intermediários formados inicialmente na reação, catecol, pode reduzir Fe3+ a Fe2+, e na presença de H2O2 inicia um ciclo redox catalítico. Nas etapas iniciais da reação, este ciclo mediado por catecol torna-se a principal via de degradação térmica de fenol e seus produtos de oxidação. A adição de íons Zn2+ aumenta o tempo de persistência do catecol, provavelmente por estabilização do radical semiquinona via complexação.

A study of the interference of Zn2+ ions on phenol degradation by Fenton reaction (Fe2+/Fe3+ + H2O2) is reported. One of the first intermediates formed in the reaction, catechol, can reduce Fe3+ to Fe2+ and, in the presence of H2O2 initiates an efficient catalytic redox cycle. In the initial stages of the reaction, this catechol-mediated cycle becomes the principal route of thermal degradation of phenol and its oxidation products. The Zn2+ ion addition enhances the persistence time of catechol, probably by stabilization of the corresponding semiquinone radical via complexation.