Carbon fiber reinforced polymer (CFRP) have been gaining prominence in replacing metallic alloys for infrastructure in prostheses, with the possibility of edentulous patients to acquire fixed prostheses. For this, procedures are required to connect these implants to the implant-supported fixed prosthesis, such as holes and notches that can reduce their mechanical properties. In addition, the infrastructure requires longer cantilevers, causing greater stress on the prosthetic system. Then, the objective is to analyze the stress concentration in the CFRP subjected to bending loads with holes (4 and 6 mm diameter to verify the influence of the diameter-to-width ratio) in four-point-bending test. Two composite laminates were evaluated: one with thermoplastic matrix of poly(phenylene sulphide) PPS; and another with epoxy matrix combined with carbon fibers fabric. The presence of holes in the studied dimensions did not present significant differences in the flexural modulus and maximum bending strength. Therefore, the use of CFRP showed some advantage regarding the reduced effect of stress concentration compared to metallic alloys.

Abstract Glaze application on monolithic zirconia (Y-TZP) can be a practical approach to improve the mechanical properties of this material. Objective Our study evaluated the effect of glazing side and mechanical cycling on the biaxial flexure strength (BFS) of a Y-TZP. Methodology Eighty sintered Y-TZP discs (Ø:12 mm; thickness: 1.2 mm - ISO 6872) were produced and randomly assigned into eight groups (n=10), according to the factors “glazing side” (control – no glazing; GT – glaze on tensile side; GC – glaze on compression side; GTC – glaze on both sides) and “mechanical aging” (non-aged and aged, A – mechanical cycling: 1.2×106, 84 N, 3 Hz, under water at 37°C). Specimens were subjected to BFS test (1 mm/min; 1,000 Kgf load cell) and fractured surfaces were analyzed by stereomicroscopy and SEM. Hsueh’s rigorous solutions were used to estimate the stress at failure of glazed specimens. Two-way ANOVA, Tukey’s test (5%), and Weibull analysis were performed. Results The “glazing side”, “mechanical aging” and the interaction of the factors were significant (p<0.05). Groups GC (1157.9±146.9 MPa), GT (1156.1±195.3 MPa), GTC (986.0±187.4 MPa) and GTC-A (1131.9±128.9 MPa) presented higher BFS than control groups (Tukey, 5%). Hsueh’s rigorous solutions showed that the maximum tensile stress was presented in the bottom of zirconia layer, at the zirconia/glaze interface. Weibull characteristic strength (σo) of the GC was higher than all groups (p<0.05), except to GT, GTC-A and GTC, which were similar among them. The fractography showed initiation of failures from zirconia the tensile side regardless of the side of glaze application and fatigue. Conclusion Glazing zirconia applied on both tensile and compression sides improves the flexural strength of Y-TZP, regardless the mechanical aging.

Abstract: The effects of several ceramic surface treatments on bond strength of a polymer-infiltrated ceramic network and resin composite as repair material were evaluated. CAD-CAM blocks of a polymer-infiltrated ceramic network (Vita Enamic) were sliced and subjected to aging process, followed by embedding in acrylic resin. The bonding/repair area was treated as follows (n = 30): C– without treatment; UA– universal adhesive application; FM– 10% hydrofluoric acid and silane application; OM–airborne-particle abrasion with aluminum oxide and silane application; RP– tribochemical silica coating; and CA– surface grinding and application of universal adhesive. Composite resin cylinders were made on the treated surface. Specimens from each group were assigned randomly to two subgroups (n = 15) considering storage condition: Baseline (shear tests after 48 hours) or Storage (tests after 6 months under distilled water). The treated surfaces were analyzed by goniometry, roughness, and SEM. Two-way ANOVA and 1-way ANOVA were applied to analyze the bond data and roughness / contact angle data, respectively, followed by Tukey's test (α = 5%). Surface treatments and storage conditions affected bond strengths (p < 0.01). Surface grinding (CA) followed by universal adhesive promoted the highest value of bond strength (14.5 ± 4.8 MPa for baseline, 8.5 ± 3.4 MPa for storage) and the roughest ceramic surface. Grinding with silicon carbide paper (simulating diamond bur) followed by the application of a universal adhesive system is the best option for repairing fractures of the polymer-infiltrated ceramic network.