Titania-supported Ir catalysts were used in the hydrogenation of furfural. Reactions were carried out in a stirred batch type reactor at 0.62MPa and 363K using a 0.10M solution of furfural in a 1:1 mixture n-heptane -ethanol as solvent. Catalysts containing 2 wt% of Ir were reduced in H2 flow at different temperatures in the range 473-773K. The catalysts were characterized by H2 chemisorption, TEM, TPR, TPD of NH3 and XPS. Conversion of furfural is higher at lower reduction temperatures, but leads to byproducts whereas reduction at higher temperatures shows selectivity to furfuryl alcohol close to 100%.

The effect of chromium on the catalytic properties of MCM-41 was evaluated in order to develop new catalysts for the trimethylbenzene transalkylation with benzene to produce ethylbenzene, a high-value aromatic in the industry. It was found that chromium decreases the specific surface area but increases the acidity, turning MCM-41 into an active and selective catalyst for ethylbenzene and toluene production. The coke produced on the catalyst is hydrogenated and mainly located outside the pores and thus can be easily removed. The catalyst is more active and selective than mordenite, a commercial catalyst, and thus more promising for commercial applications.