Abstract Copper sulfides are materials with different technological applications due to different possibilities of phases, which result in different properties. Thus, obtaining particles with different stoichiometry of the materials is of great interest. Two simple chemical routes were used to obtain copper sulfides (Cu2-xS) particles of different phases and stoichiometry. One of the obtained powders was used for thin film deposition through resistive evaporation and characterized. From scanning electron microscopy the particle size was found as around 500 nm. The second route leads to non-stoichiometric powder with characteristic CuS, Cu9S5 and Cu2S planes detected in the XRD diffractograms. Thin films from this route were also obtained by resistive evaporation. The amorphous film obtained after evaporation was submitted to thermal annealing at 200 ° C/2h, becoming semi-crystalline. The deposited film showed good adhesion to the substrate and low roughness, in addition to a bandgap of 2.5 ± 0.1 eV and a resistivity of 1x10-2 Ω.cm, values in good agreement with those reported in the literature. The techniques used here proved to be of good quality for deposition of copper sulfide films, and can be used as a simpler alternative in addition to commonly used for deposition of copper sulfide films.

Abstract A derivation of the sol-gel-dip-coating deposition technique is proposed, where the precursor solution exhibits two separated liquid phases, reaching an equilibrium state in a heterogeneous solution. Structural, optical and photocatalytic properties of TiO2 films grown from the proposed two phases method are shown and discussed, along with the properties of films deposited when the top phase present distinct lengths, which are observed through SEM images and optical transmittance spectra. The dominant crystalline phase is anatase for all the films prepared. Films are tested towards their efficiency for photocatalysis, using methylene blue as dye degradation agent. It has been found that films deposited through the two phase method are more efficient on the photocatalyitic degradation of methylene blue.

Er3+ emission in the wide bandgap matrix SnO2 is observed either through a direct Er ion excitation process as well as by an indirect process, through energy transfer in samples codoped with Yb3+ ions. Electron-hole generation in the tin dioxide matrix is also used to promote rare-earth ion excitation. Photoluminescence spectra as function of temperature indicate a slight decrease in the emission intensity with temperature increase, yielding low activation energy, about 3.8meV, since the emission even at room temperature is rather considerable.