Surface modification by deposition of hard coatings is a way to overpass the poor wear resistance of some metallic materials and one potential material is the Diamond-Like Carbon (DLC). We investigated the wear behavior, and the adhesion of the DLC deposited on a Ti6Al4V (Ti64) alloy after Surface Mechanical Attrition Treatment (SMAT). The SMAT was applied using 100Cr6 steel balls, and the DLC was deposited through the sputtering method. The nano-hardness was evaluated using a MTS Nano Indenter XP. The adhesion of the DLC was evaluated using a CSM Revetest, and the wear tests was performed in a reciprocating linear tribometer from CSM Instruments. The mean wear rate for the Ti64 was 437x10-6 mm3/N/m against 5x10-6 mm3/N/m for the Ti64+SMAT+DLC. The SMAT reduced the wear rate of the DLC coating, showing that the SMAT might be a viable treatment with promising results regarding the DLC wear resistance.

Mechanical and tribological properties os AISI 304 and AISI 316 stainless steels submited to glow discharge ion nitriding are reported.The atmosphere was 20:80 - N2:H2 with substrate temperatures ranging from 300 to 500 °C. Treatment at 300 °C produced expanded austenite (γN) in both steels. Increasing the temperature, the phases γ´-Fe4N and - Fe2+xN were present and the latter is the major phase for AISI 304. At 500 °C, the CrN phase was also identified in both steels. Hardnesses of about 13-14 GPa at near surface regions were obtained in both steels. Moreover, AISI 316 nitrided at 500 °C has the deepest hard layer. Tribological tests showed that wear can be reduced by up to a factor of six after the nitriding processes, even for a working temperature of 300 °C. The profiles during and after nanoscratch tests did not reveal significant differences after nitriding processes in both steels.