Mesoporous gamma-aluminas (γ-Al2O3) were synthesized starting from an unusual precursor of polyoxohydroxide aluminum (POHA). This precursor was obtained from aluminum oxidation in alkaline water-ethanol solvent in the presence of d-glucose that induces the formation of a gel, which leads to the POAH powder after ethanolic treatment. Precipitated POHAs were calcined at different temperatures (300, 400, 700 and 900 °C) resulting in the metastable γ-Al2O3 phase. Whereas at 300 °C no γ-Al2O3 phase was formed, unexpectedly, mesoporous γ-Al2O3 was obtained at 400 ºC having a high specific surface area (282 m2/g) and a narrow pore size distribution. At higher temperatures, the aluminas had the expected decrease in surface area: 166 m2/g (700 °C) and 129 m2/g (900 °C), respectively. The structural change from POHA to alumina calcined at 400 ºC occurs directly without the need to isolate the hydroxide or oxyhydroxide aluminum precursors. Both POHA and transition aluminas were characterized by Fourier Transform Infrared spectroscopy (FTIR), X-ray diffraction (XRD), N2 sorption and Scanning Electron Microscopy (SEM). These findings show an alternative route to produce high standard aluminas.

The reaction of Naphthalene 1,4,5,8-dianhydride (NTCDA) with elemental aluminum(0) powder is studied in an aqueous alcoholic KOH mixture to search for the NTCDA anion and dianion electron-adducts. After analyzing various reaction conditions it was found that the reaction yielded a greenish precipitate in 3:1 (v:v) ethanol:water mixture. This powder is composed mainly of aluminum trihydroxide crystallites of bayerite [α-Al(OH3)(s)] and the organic content is approximately 6%. This hybrid material proved to be paramagnetic even after exposure to air for one year and at temperatures up to 200 ºC. Typical carbonylic bound to metal IR bands and reflectance UV-VIS spectra demonstrate the entrapment of NTCDA radical anion into the aluminum trihydroxide, hence rendering its green color and a paramagnetic behavior. Thus, besides the understanding of an aluminum reaction in suspension, the entrapment of an organic material (NTCDA) that stays stable as the corresponding radical can provide an interesting option for the synthesis of aluminum trihydroxide composites.