The aim of this in vitro study was to evaluate the tensile bond strength of a self-etching adhesive system to three different dentinal substrates. Primary molar teeth that had been recently exfoliated (RE), with unknown time of exfoliation (UT), and extracted due to prolonged retention (PR) were used for this investigation. Ten primary molar teeth of each group were cut in the middle following the mesio-distal direction, creating a total of twenty specimens per group. The specimens were included in acrylic resin and had a flat dentin surface exposed. The self-etching adhesive system was applied to this surface and a 3-millimeter high cone with diameter of 2 mm in the adhesion area was constructed using composite resin. The specimens were stored in distilled water at 37ºC for 24 hours. Fifteen specimens of each substrate were used for the tensile bond test (n = 15) and 5 had the interface analyzed by scanning electron microscopy (SEM). The data was examined by one-way ANOVA and presented no significant differences between groups (p = 0.5787). The mean values obtained for RE, UT and PR were 18.39 ± 9.70, 19.41 ± 7.80, and 23.30 ± 9.37 MPa, respectively. Any dentinal substrates of primary teeth studied are safe for tensile bond strength tests with adhesive systems.

Because a greater research effort has been directed to analyzing the adhesive effectiveness of self etch primers to dentin, the aim of this study was to evaluate, by microtensile testing, the bond strength to enamel of a composite resin combined with a conventional adhesive system or with a self-etching primer adhesive, used according to its original prescription or used with previous acid etching. Thirty bovine teeth were divided into 3 groups with 10 teeth each (n= 10). In one of the groups, a self-etching primer (Clearfil SE Bond - Kuraray) was applied in accordance with the manufacturer's instructions and, in the other, it was applied after previous acid etching. In the third group, a conventional adhesive system (Scotchbond Multipurpose Plus - 3M-ESPE) was applied in accordance with the manufacturer's instructions. The results obtained by analysis of variance revealed significant differences between the adhesive systems (F = 22.31). The self-etching primer (Clearfil SE Bond) presented lower enamel bond strength values than the conventional adhesive system (Scotchbond Multipurpose Plus) (m = 39.70 ± 7.07 MPa) both when used according to the original prescription (m = 27.81 ± 2.64 MPa) and with previous acid etching (m = 25.08 ± 4.92 MPa).

This study evaluated the influence of curing tip distance, shade and filler particle size on Vickers microhardness (VHN) of composite resins. Two composites were tested: Filtek Z250 microhybrid (3M ESPE; shades A1 and A3.5) and Filtek Supreme nanofilled (3M ESPE; shades A1B and A3.5B). For each resin, 42 specimens (5 mm in diameter and 2 mm height) were prepared being 21 for each shade. The specimens were exposed using a 20-second exposure to a quartz-tungsten-halogen light source with an irradiance of approximately 560 mW/cm², at the following distances: 0 mm (surface contact), 6 mm and 12 mm from composite surface. Effectiveness of cure of different resins, shades and curing distances was determined by measuring the top and bottom hardness (VHN) of specimens using a digital microhardness tester (load: 50 g; dwell time: 45 seconds) 24 hours following curing. The hardness ratio was calculated by dividing VHN of the bottom surface by VHN of top surface. Three-way ANOVA and Tukey's post-hoc test (p<0.05) revealed statistically significant differences for all analyzed factors. As for top hardness, as microhardness ratio (bottom/top), the factors shade, distance and composite filler particle size exerted influence on resin curing. Lighter shade composites (A1 and A1B) showed higher hardness values. At 6 and 12 mm curing tip distances, hardness was lower when compared to 0 mm. The microhybrid composite resin presented higheer hardness, being its microhardness ratio satisfactory only at 0 mm for both shades and at 6 mm for the lighter shade. The nanofilled composite resin did not present satisfactory microhardness at the bottom while the microhybrid composite resin had higher hardness than the nanofilled. Composite's curing tip distance and shade can influence hardness.

Com a grande busca pelo desenvolvimento das técnicas de polimerização das resinas compostas e dos sistemas adesivos, foram introduzidos no mercado os LEDs. Com base na literatura estudada, neste trabalho é avaliada a força de união da resina composta ao esmalte associado a um sistema adesivo convencional e a um sistema autocondicionante polimerizados por luz halógena e LED, por meio do teste de microtração. Os dentes bovinos foram divididos em 4 grupos com 10 dentes em cada um (n = 10), para aplicação do adesivo Scotchbond Multipurpose Plus (3M-ESPE) e do Clearfil SE Bond (Kuraray) conforme orientação do fabricante, ambos polimerizados por 10 s tanto pela luz halógena (Degulux Soft Start - Degussa Hulls) com potência de 550 mW/cm² como pelo LED (Kerr Demetron) com potência de 600 mW/cm². A resina composta Filtek Z-250 foi aplicada em 4 incrementos de 1 mm com auxílio de uma matriz de silicona de condensação de formato quadrado com dimensões de 5 mm x 5 mm; sendo polimerizada tanto pela luz halógena como pelo LED por 40 s. O adesivo Scotchbond Multipurpose Plus polimerizado com luz halógena apresentou os maiores valores de adesão (39,69 ± 7,07 MPa) e os outros grupos não apresentaram diferença estatisticamente significante entre si: Scotchbond Multipurpose Plus polimerizado por LED (22,28 ± 2,63 MPa), Clearfil SE Bond polimerizado por luz halógena (27,82 ± 2,65 MPa) e por LED (22,89 ± 5,09 MPa).

With the development of composite resin polymerization techniques, LEDs were introduced to the market place. Based on the studied literature, the aim of this study was to evaluate, through microtensile testing, the bond strength to enamel of a composite resin associated to a conventional (multi-bottle) adhesive system or to a self etching primer adhesive system, polymerized by halogen light or LED (light emitting diode). Bovine teeth were divided into 4 groups with 10 teeth each (n = 10). Then the adhesives Scotchbond Multipurpose Plus (3M-ESPE) and Clearfil SE Bond (Kuraray) were applied following the manufacturers’ instructions. Both systems were polymerized for 10 s by halogen light (Degulux Soft Start - Degussa Hulls) set at 550 mW/cm² or by LED (Kerr Demetron) set at 600 mW/cm². The composite resin Filtek Z-250 was applied in four 1 mm increments with the aid of a square, condensation silicon, 5 mm x 5 mm matrix, and polymerized by either of light sources for 40 s. Scotchbond Multipurpose Plus polymerized by halogen light presented the highest bond strength values (39.69 ± 7.07 MPa), and the other groups did not present statistically significant differences: Scotchbond Multipurpose Plus polymerized by LED (22.28 ± 2.63 MPa), Clearfil SE Bond polymerized by halogen light (27.82 ± 2.65 MPa) and by LED (22.89 ± 5.09 MPa).

Cinco combinações de materiais comumente utilizados para registros intermaxilares em casos de extremidades livres bilaterais foram avaliados: base de resina acrílica + cera; base de resina acrílica + pasta zincoenólica; base de resina acrílica + cera + resina Duralay; silicona de condensação; e placa de resina acrílica + hidrocolóide irreversível. Foi realizada a medida da distância vertical entre pontos referenciais em 6 regiões nas bases dos modelos articulados. As medidas obtidas com a articulação manual dos modelos foram tomadas como padrão de comparação para as medidas obtidas com os materiais testados. Os resultados foram submetidos à análise estatística por meio de análise de variância e teste de Tukey. Houve diferença estatisticamente significante (p<0.05) entre a silicona de condensação e a combinação da base de resina acrílica + cera, porém entre os demais materiais não houve diferença estatisticamente significante. A silicona de condensação apresentou as maiores diferenças em relação às medidas obtidas pela articulação manual dos modelos e a combinação da base de resina acrílica + cera apresentou as menores diferenças. Com base nos achados deste estudo, a seguinte escala de reprodutibilidade pode ser estabelecida, do melhor para o pior: base de resina acrílica + cera; placa de resina acrílica + hidrocolóide irreversível; base de resina acrílica + cera + pasta zincoenólica; base de resina acrílica + cera + resina Duralay; e silicona de condensação.

Five combinations of materials commonly used for intermaxillary records in cases of bilateral free end saddle were evaluated: acrylic resin base + wax; acrylic resin base + wax + ZOE paste; acrylic resin base + wax + Duralay resin; condensation silicone; and acrylic resin plate + irreversible hydrocolloid. The materials were evaluated by measuring the vertical distance between pairs of reference points located on the bases of the upper and lower articulated casts. The measurements obtained by manual articulation of the casts were used as the standards to which the measurements obtained with the recording materials were compared. ANOVA revealed significant differences among the materials and the Tukey's test showed that condensation silicone differed significantly (p<0.05) from the acrylic resin + wax combination, while no significant differences (p>0.05) were observed among the remaining materials. The condensation silicone presented the greatest differences from the measurements obtained by manual articulation of the casts whereas the acrylic resin base + wax combination presented the least differences. Based on the findings of this study, the following scale of fidelity can be settled from best to worst: acrylic resin base + wax; acrylic resin plate + alginate; acrylic resin base + wax + ZOE; acrylic resin base + wax + Duralay; and condensation silicone.

O uso do laser de argônio (488 nm) tem sido sugerido como uma nova alternativa para polimerização de materiais adesivos. Este estudo tem o objetivo de avaliar a resistência adesiva de uma resina composta microparticulada (A110, 3M) inserida pela técnica incremental (3 incrementos de 1 mm) e de incremento único (3 mm) polimerizada com laser de argônio por 10, 20 e 30 segundos e com luz halógena por 40 segundos. Oitenta (8 grupos com 10 dentes) dentes bovinos recém-extraídos foram armazenados em geladeira, em água destilada, por uma semana. As coroas foram separadas das raízes. Foi realizada a pulpectomia, e as coroas foram seladas com cera. As faces vestibulares foram desgastadas com seqüência de lixas (120, 400 e 600) para expor a dentina superficial, e os dentes foram incluídos em resina acrílica. Foi utilizada uma mesa metálica para fixar cada espécime com a matriz de polipropileno preta (3 mm de altura com delimitação interna milimetrada) e inserir a resina de acordo com os grupos estudados. Os tempos de polimerização foram de 10, 20 e 30 segundos para a polimerização com laser e de 40 segundos para a polimerização convencional. Os testes de resistência adesiva foram realizados com a máquina universal de ensaios 4442 (Instron) com velocidade de 0,5 mm/min e carga de 500 N. De acordo com a metodologia usada, a técnica incremental aumentou os valores de resistência adesiva. Não houve diferença entre as técnicas de polimerização usadas quando a resina foi inserida em 3 incrementos.

The use of argon laser (488 nm) has been suggested as a new alternative for polymerizing adhesive materials. This study aimed to evaluate the tensile bond strength of a microfilled composite (A110, 3M) inserted by incremental technique (3 increments of 1 mm) and by single increment (3 mm) polymerized by argon laser for 10, 20 and 30 seconds and halogen light for 40 seconds. Eighty (8 groups of 10 teeth) freshly extracted bovine teeth were stored in a freezer in distilled water for one week. The crowns were cross-sectioned from the roots. Pulpectomy was performed and the pulp chambers were sealed with wax. The buccal surfaces of the teeth were ground with wet sandpaper (grains: 120, 400, and 600) to expose the surface dentin, and the teeth were then included in acrylic resin. A metal device was used to fix each sample and a black propylene matrix25 (3 mm high with an internal millimetric delimitation) was used to insert the material according to the groups studied. The polymerization intervals were of 10, 20 and 30 seconds for the laser polymerization and 40 seconds for the conventional polymerization. Tensile tests were performed by a Universal Testing Machine 4442 (Instron) at a speed of 0.5 mm/min and 500 N load. According to the methodology used, the incremental technique increased bond strength values. There was no difference between the studied polymerization techniques when resin was filled in 3 increments.

Este trabalho analisou in vitro duas marcas de adesivos de quarta geração do sistema simplificado (Optisolo - Kerr, com carga, e Single Bond - 3M, sem carga) e duas marcas de resinas compostas (Prodigy - Kerr e Z100 - 3M), com o objetivo de verificação da adesividade na dentina. Oitenta corpos-de-prova, confeccionados a partir de molares humanos extraídos, foram incluídos em resina acrílica e desgastados até exposição de dentina no sentido longitudinal, e divididos em 4 grupos. Cones de resina composta foram aderidos a estes corpos-de-prova precedidos dos sistemas adesivos, seguindo a orientação dos fabricantes. Os corpos-de-prova foram submetidos a teste de tração numa máquina de ensaios Universal Mini-Instron 4442, a uma velocidade de 0,5 mm/min. Os resultados obtidos foram transformados em MPa de acordo com a área de adesão e submetidos a análise estatística pela ANOVA. Pelos resultados obtidos, concluiu-se que houve diferença estatisticamente significante (p < 0,01) entre os adesivos (F = 7,24), sendo que o adesivo Optisolo (m = 11,03 ± 4,23) apresentou maior resistência de união que o Single Bond (m = 8,37 ± 4,54). Entre as duas resinas (F = 0,43), não foi detectada diferença estatisticamente significante (p > 0,05).

This study analyzed in vitro two brands of one-step adhesive systems of fourth generation (Optisolo - Kerr, filled; and Single Bond - 3M, unfilled) and two composite resins (Prodigy - Kerr and Z100 - 3M), aiming at evaluating their bond strength to dentin. Eighty human extracted molars were embedded in acrylic resin and grounded until dentin was exposed in longitudinal direction. The specimens were divided in 4 groups. Composite resin cones were bonded to the specimens using the mentioned adhesive systems, following the instructions of the manufacturers. The test-specimens were submitted to tensile tests using a 4442 Universal Mini-Instron Machine with the speed of 0.5 mm/min. The results were converted into MPa, according to the area of adhesion, and submitted to statistical analysis with ANOVA. There was significant statistical difference (p < 0.01) between the adhesive systems (F = 7.24). Optisolo (m = 11.03 ± 4.23) showed better bond strength than Single Bond (m = 8.37 ± 4.54). There was no significant statistical difference (p > 0.05) between the composites (F = 0.43).

Os autores estudaram o efeito de quatro diferentes técnicas de polimento de restaurações de amálgama feitas em laboratório com duas ligas convencionais e três ligas com alto teor de cobre, sendo o polimento realizado no tempo de 168 horas após a condensação. A utilização de brocas multilaminadas para o acabamento superficial dos corpos-de-prova exibiu níveis de rugosidade semelhante aos corpos-de-prova não polidos. No tocante às ligas utilizadas, a liga DFL mostrou os mais altos valores de rugosidade superficial, enquanto a liga GS 80 exibiu os melhores valores. A trituração foi efetuada segundo a indicação dos fabricantes e o amálgama foi condensado em uma matriz de aço fabricada especialmente para a pesquisa. A matriz tinha uma cavidade de 4,0 mm de diâmetro com 2,0 mm de profundidade. Cinco minutos após a condensação, foi feita a escultura com uma lâmina de aço e em seguida a brunidura. Depois de 25 minutos, o corpo-de-prova de amálgama era retirado utilizando-se um parafuso da própria matriz. Então, 168 h após a condensação, os corpos-de-prova eram polidos e submetidos aos testes de rugosimetria.

The authors studied the effect of four different polishing techniques on amalgam restorations made of two conventional and three high-copper alloys. Polishing was performed 168 hours after condensation. The use of multilaminated burs in the superficial finishing of the amalgam samples led to rugosity similar to that of the nonpolished samples. Regarding the utilized alloys, DFL exhibited the highest values of superficial rugosity, meanwhile GS 80 showed the lowest values. Trituration was performed as the manufacturer indicated and amalgam was condensed in a steel matrix fabricated especially for this research. The matrix had a cavity with 4.0 mm in diameter and 2.0 mm in depht. Five minutes after condensation the amalgam surfaces were submitted to sculpture with a steel blade and then to burnishing. After 25 minutes, the amalgam samples were removed with the aid of the matrix screw. Then, 168 hours after condensation, the samples were polished and submitted to rugosimetric tests.

O objetivo deste trabalho foi avaliar, in vitro, se a utilização do cimento de óxido de zinco e eugenol exerce influência na microdureza da restauração de resina composta (Z100) realizada com dois sistemas adesivos (Scotchbond Multi-Purpose Plus® - sistema que remove o "smear layer", e o Clearfil Liner Bond 2® - adesivo que promove o tratamento do "smear layer", sem removê-lo totalmente). Para isto, foram utilizados 40 molares humanos hígidos que foram divididos igualmente em 4 grupos. Para cada adesivo havia um grupo controle (sem óxido de zinco e eugenol) e outro onde foram realizadas e removidas as restaurações provisórias com cimento de óxido de zinco e eugenol. Após sete dias de armazenamento em estufa a 37ºC, os dentes foram cortados e mediu-se a microdureza da resina composta na região a 0,3 mm da interface dente-restauração em um microdurômetro SHIMADZU HMV 2000, com ponta penetradora Knoop de 50 gramas por 45 segundos. Os resultados obtidos foram analisados estatisticamente pela ANOVA (alfa = 1%), e verificou-se não haver diferença estatisticamente significante na microdureza da resina composta entre os grupos estudados.

The zinc oxide-eugenol cement is still widely used as a temporary restorative material. Its use is known, however, to disturb the curing process of composite resins used in the final restoration. Nevertheless, with the development of dentin bonding systems, total etch is used to remove or treat the smear layer before the construction of the composite resin restoration. The purpose of this study was to evaluate if the zinc oxide-eugenol cement influenced the microhardness of composite resin (Z100) restorations used in association with either one of two bonding systems (Scotchbond Multi-Purpose Plus® and Clearfil Liner Bond 2®). Forty molars were divided into four groups. For each bonding material there was a control group that did not receive cement and a group that received a temporary zinc oxide-eugenol restoration that was removed after seven days. The specimens were stored in a dry heat sterilizer at 37ºC, for seven days before the sectioning procedure. Microhardness was measured 0.3 mm far from the tooth-restoration interface by means of a SHIMADZU HMV 2000 apparatus, with a Knoop hardness tip of 50 g, for 45 seconds. Statistical analysis of the results was performed using ANOVA (alpha = 1%) and revealed no statistically significant differences in the microhardness of the composite resin, among the studied groups.

O grau de polimerização das resinas compostas, avaliado principalmente pela microdureza vem sendo estudado relacionado com inúmeros fatores. Algumas pesquisas in vitro fazem uso de matrizes como base para a confecção de corpos-de-prova e não dentes naturais. Para as resinas fotopolimerizáveis, a intensidade de luz que atinge o material exerce influência direta no seu grau de polimerização. A cor e/ou transparência dessas matrizes não deveriam induzir a diferenças nos resultados finais de microdureza. Com essa preocupação, este trabalho teve por objetivo avaliar o efeito de duas matrizes de polipropileno utilizadas para testes com resina composta. Uma delas era branca e outra preta. A resina foi inserida e polimerizada em incremento único de 3 mm e em 3 incrementos de 1 mm cada e sua dureza medida a 3 mm de profundidade. Analisando os resultados pode-se concluir que houve diferença estatisticamente significante entre as duas cores, sendo que a microdureza foi menor com a matriz preta. A técnica de inserção e polimerização em incremento único induziu a menor grau de polimerização que a técnica incremental em ambas as matrizes (p < 0,01). Pôde-se obter com esses resultados, que ao utilizar matrizes pretas para confecção de corpos-de-prova de resina composta fotopolimerizável, os valores obtidos, principalmente relacionados com profundidade de polimerização, demonstram o menor grau possível de polimerização, e que depende exclusivamente das propriedades da resina.

The polymerizing degree of composite resins, mainly evaluated through their microhardness, has been studied in relation to many factors. Some in vitro researches use matrices as basis for manufacturing test specimens instead of, natural teeth. For photopolymerized resins, the light intensity that reaches the material directly influences its polymerization degree. The color, as well as the transparency of the resins, should not induce differences on the final microhardness results. With this awareness in mind, this work had the aim of evaluating the effect of two polypropylene resins used in tests of composite resins. One of them was white and the other was black. The resin was applied and polymerized in a single portion of 3 mm, and in 3 increments of 1 mm each, and the hardness index was measured at 3 mm of depth. After analyzing the results, a great difference was noticed between both colors, being the microhardness smaller in the black one. The single portion polymerization and applying techniques resulted in a smaller polymerization degree for both matrices (p < 0.01). We could notice that, when using black matrices for manufacturing test specimens of photopolymerized composite resin, the values obtained, mainly in relation to the depth of polymerization, showed the smallest possible degree of polymerization, and they also showed that it depends only on the resin properties.

As propriedades das resinas compostas têm sido estudadas com freqüência, bem como os fatores que podem influenciar seu grau de polimerização. Diante da evolução desses materiais e da necessidade de buscarmos melhora do seu comportamento na cavidade bucal, objetivamos, por meio deste estudo avaliar a eficácia de dois aparelhos fotopolimerizadores do tipo pistola (de alta intensidade de luz), comparando com a de um aparelho a cabo (de baixa intensidade de luz), com tempos de exposição de 20 e de 40 segundos e em profundidades de 1 a 4 milímetros. Os testes avaliaram o grau de polimerização da resina por meio de testes de microdureza Knoop. Os resultados mostraram haver diferença estatisticamente significante entre os tempos, sendo que com 40 segundos a dureza foi maior que com 20 segundos para as 4 diferentes profundidades. Para o fator aparelhos, os dois aparelhos tipo pistola se comportaram superiores ao do tipo cabo Fibralux (Dabi Atlante), e entre eles, o XL 1500 (3M) promoveu dureza maior que o Optilight II (Gnatus) no tempo de polimerização de 40 segundos. As profundidades de 1, 2, 3 e 4 milímetros mostraram estatisticamente diferença entre si tendo sido encontrada maior dureza para as menores profundidades (p < 0,05).

The properties of composite resins have been frequently studied, as well as the factors that might influence the polymerization degree. Considering the evolution of composites and the need to improve their clinical performance, this study intends to evaluate the efficacy of two high-intensity and one low-intensity photocuring units, as a function of exposure time (20 and 40seconds) and composite depth (from 1 to 4 millimeters). Composite properties were evaluated via Knoop Microhardness Test. Statistical analysis (1 way ANOVA, p < 0.05) of the obtained results showed that there was statistically significant difference regarding the time factor. The 40-seconds polymerization time showed the best results, for the four depths. Concerning the photocuring unit factor, there was statistically significant (1- way ANOVA, p < 0.05) difference between the tested devices. The high-intensity units demonstrated better results than the low-intensity one. There were statistically significant differences between the analysed composite depths, being the highest microhardness values achieved for the lowest depths.

Na busca da reprodução do aspecto dental, a porcelana se destaca entre os materiais restauradores. Desse modo, a utilização do material vem atualmente crescendo cada vez mais, e, com ela, a probabilidade de fraturas. Porém, uma falha nem sempre exige a troca da restauração: existe a possibilidade de um reparo com resina composta. Este trabalho se propôs a avaliar, in vitro, a força de união da resina composta à porcelana feldspática, quando efetuados os seguintes tratamentos superficiais na porcelana: asperização com instrumento cortante rotatório diamantado ou jateamento com óxido de alumínio de 50 micra, em aplicação isolada ou associada a condicionamento com ácido fosfórico, por 15 segundos, ou com ácido fluorídrico, por 1 ou por 4 minutos. Todos os espécimes foram previamente regularizados com lixa nº 220. Após os tratamentos superficiais, receberam o sistema de união adesivo para porcelana Scotchbond Multi-Purpose Plus Dental Adhesive System (3M). Feita a união com a resina composta (Restaurador Z100, 3M), foram armazenados em água destilada a 37ºC, em estufa, por 7 dias, e termociclados (600 ciclos de 1 minuto, entre 5 e 55ºC), sendo então submetidos a teste de tração. Pelos resultados obtidos, pôde-se concluir que ocorreu melhora na resistência à tração com todos os tratamentos propostos (em comparação ao observado no grupo controle, sem nenhum tratamento superficial). O jateamento produziu maior resistência de união que a asperização com instrumento cortante rotatório diamantado; mas, quando associados ao condicionamento com qualquer dos ácidos selecionados, independente do tempo de aplicação, não houve diferença estatística entre esses tratamentos.

In the search for the recovery of the dental aspect, the porcelain stands out among restoring materials. The use of this material has increased considerably over the last years, therefore increasing the probability of fractures. Even so, not every failure demands the restoration of the material: the possibility of a repair exists with compounded resin. This study proposed to evaluate in vitro the bonding strength of the composite resin to feldspathic porcelain with several surface treatments: roughened with diamond burs or sandblasted with aluminum oxide of 50 micra, isolated or associatedly etched with phosphoric acid for 15 seconds, or with hydrofluoric acid for 1 or 4 minutes. All the specimens were previously regularized with 220-grit silicon carbide paper. After the superficial treatments, they received the adhesive system for porcelain, Scotchbond Multi-Purpose Dental Plus Adhesive System (3M). After making the union with the composed resin (Restorative Z100, 3M), they were stored in distilled water at 37ºC, for 7 days, followed by thermocycling (600 cycles of 1 minute, between 5 and 55ºC), and submitted to a tensile strength test. With the obtained results, the conclusion was that with all the proposed treatments an improvement happened in the resistance of the tensile bonding strength (when compared to those observed in the group control without any superficial treatment). The sandblasting produced a better resistance than the roughening with a diamond bur; but, when associated to the etching with any of the selected acids, independent of the time of application, there was no statistical difference among those treatments.

Cilindros de selante, padronizados, foram unidos ao esmalte das superfícies vestibulares de incisivos bovinos, após serem planificadas e condicionadas, com ácido fosfórico a 37%, durante 30 segundos. Foram utilizados 40 dentes, aleatoriamente divididos em 4 grupos, cujas coroas foram secionadas, de modo a obter-se duas porções, cervical e incisal. No Grupo I, após o condicionamento, aplicou-se o selante Fluroshield; no Grupo II, antes da aplicação do selante, uma camada do "primer" do Probond foi aplicada; no Grupo III, após o "primer", aplicou-se o adesivo do Probond; e no Grupo IV, somente o adesivo foi aplicado antes do selante. Os espécimes foram armazenados em água a 37°C, durante 36 horas, e então submetidos aos ensaios de cisalhamento. A análise estatística revelou significante diminuição na resistência ao cisalhamento, quando o "primer" foi aplicado previamente ao selante, enquanto a resistência ao cisalhamento do selante foi semelhante quando o adesivo do Probond foi aplicado, com ou sem o "primer". A resistência ao cisalhamento do selante ao esmalte é maior no terço incisal que no terço cervical da coroa.

Standardized cylinders of sealants were bonded to the flattened labial enamel of bovine incisor teeth that had previously been subjected to 37% phosphoric acid gel for 30 seconds. A total of 40 teeth were tested, randomly divided in four groups of 10 teeth each. In Group I, the sealant Fluroshield was applied after etching; in Group II after etching, the "primer" of Probond was used before the sealant; in Group III after etching, the bond of Probond was used after the "primer"; and in Group IV only the bond was applied before the sealant. Specimens were stored in water at 37°C during 36 hours, before shear testing using a Universal Testing Machine. There was significant reduction in shear bond strength of the sealant when only the "primer" was used previously to the application of the sealant. There were no significant differences in the shear bond strength of the sealant when the Probond Adhesive System was applied with or without "primer". The shear bond strength of enamel sealant was higher in the incisal third than in the cervical third.

Procedimentos com o intuito de remover manchas nos dentes têm sido muito requisitados. Dentre esses procedimentos, pode-se citar as técnicas de microabrasão do esmalte, obtendo-se resultados esteticamente mais aceitáveis. Neste trabalho propomo-nos a avaliar o efeito da técnica de microabrasão com pasta de pedra-pomes e ácido fosfórico, aplicada manual e mecanicamente, para o tratamento de lesões de mancha branca. Além do aspecto clínico, será também avaliada a rugosidade superficial das lesões antes e após os procedimentos clínicos, através de microscopia eletrônica de varredura. Foram selecionados pacientes com lesões brancas, sem cavitação. No primeiro paciente foi realizado o procedimento clínico, ao passo que desse procedimento no segundo, além e, foram realizadas moldagens em diferentes etapas para a obtenção de espécimes a ser observados em microscopia eletrônica de varredura. Nos casos analisados, pode-se concluir que as técnicas de microabrasão com ácido fosfórico e pedra-pomes, tanto utilizadas com instrumentos rotatórios quanto com com o auxílio de cunha de madeira aplicada manualmente, apresentaram resultados clínicos satisfatórios. Na microscopia eletrônica de varredura dos modelos, detectou-se a recuperação da lisura superficial do esmalte tratado.

Procedures aiming at removing stains form teeth have been widely pursued. Among these procedures are the techniques of enamel microbrasion, which can produce more favorable esthetic results. The aim of this study was to compare the results obtained clinically with application of different microabrasion techniques on white spot lesions, and also to evaluate enamel roughness in treated and untreated specimens using scanning electron microscopy. Patients with white spot lesions without cavitation were selected. On the first patient a mechanically applied clinical procedure was performed, while on the second one the clinical procedure was performed manually, and impressions were taken at different steps of the procedure in order to obtain samples to be examined under the scanning electron microscope. From the obtained results, it could conclude that the microabrasion techniques carried out with phosphoric acid and pumice flour, either with rotatory instruments or applied manually with a wood wegde, presented clinically satisfactory results. Under the scanning electron microscope, restoring of the superficial smoothness of treated enamel could be observed.

A resistência de união dos adesivos dentinários tem sido aumentada com o desenvolvimento de cada nova geração. Pouca importância tem sido dada à resistência coesiva da dentina. A proposta deste estudo foi avaliar a resistência coesiva da dentina. Dezessete caninos humanos hígidos, os quais tinham sido extraídos há mais de um ano, foram usados. Os dentes foram desgastados até a obtenção de corpos-de-prova em dentina, de formato quadrangular, com tamanho aproximado de 2 X 2 mm. Os dentes foram incluídos em resina acrílica e, então, submetidos ao teste de cisalhamento em uma máquina de ensaios universais Wolpert, com uma velocidade de 0,5 mm/min. A resistência coesiva média da dentina no teste de cisalhamento foi de 33,95 (+- 9,72) MPa. O tipo de fratura foi analisado com um aumento de 40X. Foi realizada uma análise com elemento finito, para observar a distribuição do estresse relacionada com o teste de cisalhamento. O padrão de fratura encontrado foi compatível com o tipo de teste executado e com a distribuição do estresse obtida a partir da análise de elemento finito

The bond strength of dentin adhesives to dentin has increased after each generation. Although dentin substratum is part of the bonding process, little importance has been given to measure dentin cohesive strength. The aim of this study was to evaluate the cohesive strength of dentin in human canines. Seventeen non carious canines were selected. All of them had been extracted for more than one year. The teeth were ground until dentin square samples with approximately 2 X 2 mm were obtained. They were embedded in acrylic resin and subjected to shear stress, in a Wolpert Machine, at a crosshead speed of 0.5 mm/min. The mean cohesive strength of dentin in shear mode was 33.95 (+-9.72) MPa. The fracture surfaces were observed under a X40 magnification. A finite element analysis was performed to observe the stress distribution as related to the shear test. The failure pattern was compatible with the shear test and also with the stress distribution in the finite element analysis