The single-phase polycrystalline copper oxide (Cu2O) films were prepared on sapphire substrates by radio frequency (RF) magnetron sputtering technology which was characterized by low cost and high efficiency. The influences of oxygen flow rate on physical characteristics of the prepared films were investigated. The XRD results showed that the single-phase Cu2O film exhibited a (110) preferred orientation through the analysis of texture coefficient. The AFM images exhibited that the prepared Cu2O film had the highest surface roughness with a distinctive quadrangular surface morphology. The optical transmittance of the single-phase Cu2O film was under 35% and the band gap energy was calculated to be 2.30 eV, the absorption spectra included the peak wavelength of solar radiation and the high absorptivity made it to be a suitable absorbing material. The Hall measurement indicated that all the samples exhibited p-type conductivity. The resistivity, mobility and carrier concentration of the single-phase Cu2O film was 4625 Ω·cm, 1.87 cm2/v·s and 7.227×1014 cm−3, respectively.

PURPOSE: To demonstrate the relationship between of sphingosine-1-phosphate (S1P) expression and subarachnoid hemorrhage (SAH). METHODS: The basilar arteries from a "double-hemorrhage" rabbit model of SAH were used to investigate the relation between S1P expression and SAH. Various symptoms, including blood clots, basilar artery cross-sectional area, and S1P phosphatase expression were measured at day 3, 5, 7, 9. RESULTS: The expression of S1P was enhanced in the cerebral vasospasm after subarachnoid hemorrhage in the rabbits. And S1P expression was consistent with the basilar artery cross-sectional area changes at day 3, 5, 7, 9. CONCLUSION: Sphingosine-1-phosphate expression in the cerebral arterial may be a new indicator in the development of cerebral vasospasm after subarachnoid hemorrhage and provide a new therapeutic method for SAH.