The objective of this work was to evaluate biaxial-flexural-strength (σf), Vickers hardness (HV), fracture toughness (K Ic), Young's modulus (E), Poisson's ratio (ν) and porosity (P) of two commercial glass-ceramics, Empress (E1) and Empress 2 (E2), as a function of the hot-pressing temperature. Ten disks were hot-pressed at 1065, 1070, 1075 and 1080 °C for E1; and at 910, 915, 920 and 925 °C for E2. The porosity was measured by an image analyzer software and s f was determined using the piston-on-three-balls method. K Ic and HV were determined by an indentation method. Elastic constants were determined by the pulse-echo method. For E1 samples treated at different temperatures, there were no statistical differences among the values of all evaluated properties. For E2 samples treated at different temperatures, there were no statistical differences among the values of σf, E, and ν, however HV and K Ic were significantly higher for 910 and 915 °C, respectively. Regarding P, the mean value obtained for E2 for 925 °C was significantly higher compared to other temperatures.

Aluminum nitride is a relatively new engineering ceramic and its mechanical properties have not been extensively studied. In this work, the effects of porosity (~0 to 38%) on sonic velocities, Poisson's ratio, and elastic moduli of partially sintered A1N, both pure and with additives, were investigated. The elastic constants, determined by the ultrasonic pulse-echo method, were significantly influenced by the porosity, but not by the different types of additives used (2 wt. (%) of CaCO3, CaO, and Y2O3). All elastic constants evaluated decreased with increasing porosity, but the rates of decrease were higher for elastic moduli compared do sonic velocities and Poisson's ratio. The results were analyzed in the light of stress concentration and loading bearing area models proposed in the literature.