Abstract Resin composites containing surface pre-reacted glass (S-PRG) have been introduced to reduce demineralization and improve remineralization of the tooth structure. However, water diffusion within the material is necessary for its action, which can impair its overall physicomechanical properties over time, including color stability. This study aimed to evaluate the color stability and related degree of conversion (DC) of four resin composites. Discs (6 x 4 mm, n = 5/group) of microhybrid (MH), nanofilled (NF), nanohybrid (NH), and S-PRG-based nanohybrid (S-PRG-NH) composites with two opacities (A2/A2E and A2O/A2D) were prepared. Color (CIELab and CIEDE2000) was evaluated with a spectrophotometer after aging in grape juice (2 x 10 min/10mL/7days). The DC was analyzed by using Fourier transform infrared spectroscopy before and after light-curing. Data were statistically analyzed by using two-way analysis of variance and post-hoc least significant difference tests (p<0.05). In the color stability analysis, the interaction between filler type and opacity was significant (CIELab, p = 0.0015; CIEDE2000, p = 0.0026). NH presented the highest color stability, which did not differ from that of MH. The greatest color alteration was observed for S-PRG-NH. S-PRG fillers also influenced DC (p < 0.05). The nanohybrid resin composite presented favorable overall performance, which is likely related to its more stable organic content. Notwithstanding the benefits of using S-PRG-based nanohybrid resins, mostly in aesthetic procedures, professionals should consider the susceptibility of such resins to color alteration, probably due to the water-based bioactive mechanism of action.

Abstract Objectives To analyze the effect of 5 toothpastes containing different percentages of S-PRG fillers compared to NaF toothpaste and NaF varnish on the dentin hydraulic conductance (Lp). Methodology Dentin disks (1.0±0.2 mm thickness) were cut from third molars, and their Lp values were evaluated using Flodec. The specimens were allocated into 7 groups (n=8). The minimum (smear layer) and the maximum (after acid etching) Lp values were recorded. Lp was also assessed after treatment with either a 0wt.%, 1wt.%, 5wt.%, 20wt.%, or 30wt.% S-PRG toothpaste, a NaF toothpaste, or a NaF varnish. Toothpastes were applied by brushing for 15 s, allowing it to settle for 1 min, and rinsing with deionized water. The NaF varnish was applied for 4 min and was removed with a probe. Specimens were exposed to citric acid (6%, pH 2.1, 1 min) and their final Lp was recorded. The pH of all products was recorded (n=3) and specimens from each group were analyzed by Laser Scanning Confocal Microscopy (LSCM). Data were subjected to 2-way repeated measures ANOVA and post-hoc Bonferroni (a=0.05). Results The highest Lp reduction was noticed for the 5wt.% S-PRG toothpaste, NaF toothpaste, and NaF varnish. However, the toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG were similar to all toothpastes but differed from the NaF varnish. After erosion, all groups retrieved their maximum Lp values, except for the NaF varnish. The LSCM evidenced deposits on the surface of specimens treated with 5%, 20%, and 30% S-PRG-based toothpastes and NaF toothpaste. Even more deposits were observed for the NaF varnish. After the erosive challenge, the deposits were diminished in all groups. Conclusion Toothpastes containing 5wt.%, 20wt.%, and 30wt.% of S-PRG fillers behaved similarly to a conventional NaF toothpaste, even after an erosive challenge. The NaF varnish promoted better reduction of the Lp, but its effect was also diminished after erosion.

Resumo O presente estudo teve como objetivo avaliar as propriedades de polimerização de materiais bulk-fill (baixa e alta viscosidade) utilizando luz contínua de alta intensidade e fotoativação intermitente em relação ao estresse de contração de polimerização e grau de conversão (DC). As seguintes resinas compostas Bulk-fill e nanohíbridas convencionais foram avaliadas: Filtek Z350XT Flow (3M/ESPE), SureFil SDR Flow (Dentsply), Filtek Bulk Fill Flow (3M/ESPE), Filtek Z350XT (3M/ESPE) e Filtek Bulk Fill Posterior (3M/ESPE). Um dispositivo de LED (DB 685, Dabi Atlante) foi utilizado nos dois protocolos: fotoativação contínua e intermitente contínua (ciclos de liga e desliga) com exposição idêntica (14 J/cm2). A tensão de contração de polimerização (n=6) foi avaliada através da inserção de um incremento único de 12 mm3 entre duas placas de aço inoxidável (6×2 mm) adaptadas a uma Máquina de Ensaio Universal (UTM), em tempos diferentes. As medições foram registradas após a fotoativação. O grau de conversão foi avaliado por FTIR-ATR (n=5). Os dados foram analisados pelos testes ANOVA a três fatores e teste de Tukey (α=0,05). A resina Bulk Fill Posterior apresentou maiores valores de tensão de contração quando fotoativadas com a técnica intermitente (p<0,05). A fotoativação intermitente aumentou o grau de conversão nas resinas bulk-fill de baixa viscosidade (p<0,05). Portanto, o uso de fotoativação modulada (intermitente) deve ser indicado com cautela, uma vez que seu uso pode influenciar a tensão de contração e o grau de conversão dos compósitos, o que varia de acordo com as formulações da resina.

Abstract This study aimed to evaluate the polymerization properties of bulk-fill materials (low and high-viscosity) by using high-intensity continuous light and intermittent photo-activation in terms of polymerization shrinkage stress and degree of conversion (DC). The following Bulk-fill and Conventional nanofilled resin composites were evaluated: Filtek Z350XT Flow (3M/ESPE), SureFil SDR Flow (Dentsply), Filtek Bulk Fill Flow (3M/ESPE), Filtek Z350XT (3M/ESPE) and Filtek Bulk Fill Posterior (3M/ESPE). A LED device (DB 685, Dabi Atlante) was used for both protocols: continuous uniform and intermittent photo-activation (light-on and light-off cycles) with identical radiant exposure (14 J/cm2). The polymerization shrinkage stress (n=6) was evaluated by inserting a single increment of 12 mm3 between two stainless steel plates (6×2 mm) adapted to a Universal Testing Machine (UTM), at different times. Measurements were recorded after photo-activation. The degree of conversion was evaluated by Fourier transformed infrared spectroscope (FTIR) with an attenuated total reflectance (ATR) accessory (n=5). Data were analyzed by three-way ANOVA and Tukey’s HSD (α=0.05) tests. Bulk Fill Posterior presented higher shrinkage stress values when photo-activated with the intermittent technique (p<0.05). The intermittent photo-activation increased the degree of conversion for the low-viscosity bulk-fills (p<0.05). Therefore, the use of modulated photo-activation (intermittent) must be indicated with caution since its use can influence the shrinkage stress and degree of conversion of composites, which varies according to the resin formulations.

Abstract Objectives: The aim of this in vitro study was to evaluate the bonding strength of non-simplified dentin bonding systems (DBS) to dentin irradiated with a diode laser (970 nm) immediately and after 12 months of water storage following either primer or bond application. Material and methods: The experimental design included three different factors: DBS type [AdperTM Scotchbond Multipurpose (MP) and Clearfil™ SE Bond (CSE)], irradiation [without irradiation - control (C), irradiation after primer application (AP), and irradiation after bond application (AB)], and time [initial (I) and after 12 months of water storage (12 m)]. Sixty sound human third molars (n = 10) were obtained, and their flat occlusal dentin areas were prepared and standardized. Laser irradiation was performed in the contact mode perpendicular to the dental surface over an automatically selected scanning area at a pulse energy of 0.8 W, frequency of 10 Hz, and energy density of 66.67 J/cm2. After 7 days of treatment, the specimens were cut, and half of them were subjected to microtensile testing (500 N/0.05 mm/min), whereas the remaining sticks were examined after 12 months of water storage. The obtained data were analyzed by three-way analysis of variance (ANOVA) followed by a Tukey test (p<0.05). The observed fracture modes were investigated using a portable digital microscope with a magnification of 40x. Results: Among the utilized DBS, MP generally exhibited higher bond strengths, but did not always differ from CSE under similar conditions. The irradiation factor was statistically significant only for the MP/AB groups. After 12 months of storage, all groups demonstrated a significant reduction in the bond strength, whereas the results of fracture analysis showed a predominance of the adhesive type. Conclusions: The laser treatment of non-simplified DBS was not able to stabilize their bonding characteristics after 12 months.

Abstract Simplified dentin-bonding systems are clinically employed for most adhesive procedures, and they are prone to hydrolytic degradation. Objective This study aimed to investigate the effect of laser diode irradiation on the degree of conversion (DC), water sorption (WS), and water solubility (WSB) of these bonding systems in an attempt to improve their physico-mechanical resistance. Material and Methods Two bonding agents were tested: a two-step total-etch system [Adper™ Single Bond 2, 3M ESPE (SB)] and a universal system [Adper™ Single Bond Universal, 3M ESPE (SU)]. Square-shaped specimens were prepared and assigned into 4 groups (n=5): SB and SU (control groups – no laser irradiation) and SB-L and SU-L [SB and SU laser (L) – irradiated groups]. DC was assessed using Fourier transform infrared spectroscopy with attenuated total reflectance. Additional uncured resin samples (≈3.0 µL, n=5) of each adhesive were also scanned for final DC calculation. For WS/WSB tests, similar specimens (n=10) were prepared and measured by monitoring the mass changes after dehydration/water storage cycles. For both tests, adhesive fluids were dropped into standardized Teflon molds (6.0×6.0×1.0 mm), irradiated with a 970-nm laser diode, and then polymerized with an LED-curing unit (1 W/cm2). Results Laser irradiation immediately before photopolymerization increased the DC (%) of the tested adhesives: SB-L>SB>SU-L>SU. For WS/WSB (μg/mm3), only the dentin bonding system (DBS) was a significant factor (p<0.05): SB>SU. Conclusion Irradiation with a laser diode improved the degree of conversion of all tested simplified dentin bonding systems, with no impact on water sorption and solubility.