Many researches aim to develop different biomaterials that are compatible with natural tissues. In vitro and in vivo tests are used to evaluate this potential. Our aim was to report the importance of the critical defect’s location for in vivo assays, to evaluate this approach; in vivo studies were performed, using different compositions of biomaterials in two critical size defects: tibia and parietal bone. Polycaprolactone was used as the main polymeric matrix with and without addition of hydroxyapatite. In vivo studies on the standard critical size defect in tibia and parietal bone were performed using Wistars models: 3x2 and 5x1 dimensions, respectively. The animals were sacrificed after 32 days; neobone formation was assessed with the histological data. The in vivo data demonstrated differences between the tibia and parietal bone groups: the influence of the bone on the neobone’s formation was notable. All the tibia defect samples had greater neobone volume when compared to the parietal data. Indeed, these bones have distinct embryology, influence of mechanical forces and vascularization rate that are well known; moreover, these characteristics were demonstrated to be critical for neobone formation.

Rotary jet spinning (RJS) and electrospinning are techniques to obtain fibrous scaffolds. RJS is a simple method, which fabricates three-dimensional fibers by exploiting a high-speed rotating nozzle, creating a polymer jet which stretches until solidification, and does not require high voltage. In opposite, electrospinning technique needs the presence of an external electric field to create fiber from the polymeric jet solution. This article investigates both processes using two different biocompatible polymers: Poly(L-lactic acid) (PLLA) and Poly(ε-caprolactone) (PCL). Samples were characterized by scanning electron microscopy, thermogravimetric analysis, differential scanning calorimeter, and Fourier-transform infrared spectroscopy. Morphological observations showed the efficiency of both techniques in obtaining nanofibers. Thermal analyses of data indicate immiscible property of different blends and the total solvent evaporation. In vitro cytocompatibility test showed that RJS and electrospinning samples exhibited good cytocompatibility. Based on these results, it may be concluded that the fibers obtained with both technologies are non-cytotoxicity and with good biocompatibility, and might be suitable for applications as scaffold for cell growth.

The implant’s surface is responsible for direct interaction with the human body. For cases where osseointegration must be favored and the risk of bacteria proliferation is lower, rough surfaces are more suitable, while for implants where the risks are higher, a reduced surface roughness is required. This study aimed to analyze and produce different surface finishes on samples of Ti-6Al-4V alloy produced by additive manufacturing technique of Direct Metal Laser Sintering (DMLS). Surfaces of the samples were analyzed in the as-built condition, after blasting, after chemical etching, after electropolishing and two different combinations of these methods. The surfaces were studied using the technique of scanning electron microscopy, and surface roughness and mass measurements. The lower roughness value was obtained after a combination of blasting and chemical etching. Blasting results in a surface with uniform roughness while chemical etching cleans the surface and reduces its roughness.

PURPOSE:To investigate the osseointegration properties of prototyped implants with tridimensionally interconnected pores made of the Ti6Al4V alloy and the influence of a thin calcium phosphate coating.METHODS: Bilateral critical size calvarial defects were created in thirty Wistar rats and filled with coated and uncoated implants in a randomized fashion. The animals were kept for 15, 45 and 90 days. Implant mechanical integration was evaluated with a push-out test. Bone-implant interface was analyzed using scanning electron microscopy.RESULTS: The maximum force to produce initial displacement of the implants increased during the study period, reaching values around 100N for both types of implants. Intimate contact between bone and implant was present, with progressive bone growth into the pores. No significant differences were seen between coated and uncoated implants.CONCLUSION:Adequate osseointegration can be achieved in calvarial reconstructions using prototyped Ti6Al4V Implants with the described characteristics of surface and porosity.

Scaffolds produced with ceramics are commonly used as bone substitute. In this work calcium phosphate materials were used to produce the scaffolds, because HA and TCP have many similarities with bone tissue. For crystalline phase analysis the scaffolds were calcined at 750 °C and sintered at 1330 °C. Electron microscopy images showed HA and TCP nanoparticles and the compounds were identified by Fourier transform infrared spectrometer. X-ray diffraction showed this material to be mostly crystalline. X-ray fluorescence identified chemical contaminants. X-ray micro computerized tomography produces tomographic images of the objects in 360°. In vitro testing was used to study cells behavior in contact with this material in a controlled environment.

The sol-gel process is a technique used to synthesize materials from colloidal suspensions and, therefore, is suitable for preparing materials in the nanoscale. In this work hydroxyapatite was used due to its known properties in tissue engineering. Hydroxyapatite Ca10(PO4)6(OH)2 is a bioactive ceramic which is found in the mineral phase of bone tissue and is known for its great potential in tissue engineering applications. For this reason, this material can be applied as particle aggregates on ceramic slurry, coating or film on materials with a poorer biological response than hydroxyapatite. In this work, hydroxyapatite gel was obtained by the sol-gel process and applied as nanoparticle aggregation in the mixture of hydroxyapatite and tricalcium phosphate to form a ceramic slurry. This process is the polymer foam replication technique used to produce scaffolds, which are used in tissue engineering. For HA gel characterization it was used enviromental scanning electron microscopy (ESEM), transmission electron microscopy (TEM), electron energy loss spectroscopy (EELS), scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray fluorescence (XRF). The crystallite size was calculated from XRD data using the Scherrer equation. The nanoparticles size before firing was approximately 5nm. The crystallite size calculated after calcination was approximately 63 nm. The EELS results showed that calcium phosphate was obtained before firing. After HA gel calcination at 500 ºC the XRD results showed hydroxyapatite with a small content of beta-TCP. The scaffolds obtained by polymer foam replication technique showed a morphology with adequate porosity for tissue engineering.

The influence of silicon doping on calcium phosphate cement were explored in this work. α-TCP and Si-α-TCP were prepared by solid state reaction employing "Mg-free" CaHPO4, CaCO3 and CaSiO3 as precursors. It was possible to obtain TCP powders with low contents of β phase as contaminant. Cement liquid phase was an aqueous solution containing 2.5 wt. (%) of Na2HPO4 and 1.5 wt. (%) of citric acid. The liquid-to-powder ratio was 0.6 mL.g-1. Chemical, physical and mechanical properties of the cement samples were determined by means of XRD, FTIR, XRF, compressive strength and SEM. The calcium phosphate cements obtained achieved satisfactory properties; however, Si-α-TCP presented a decrease on the rate of setting reaction.

There are evidences considering the effectiveness of Si on enhancing biological properties of calcium phosphates; however, there are not many works relating to the Si-alpha-TCP bone cement. The influence of silicon doping on the properties of Α-TCP cement was analyzed. Si-TCP was obtained by a solid state reaction employing CaCO3, CaHPO4 and CaSiO3 and powder was analyzed by XRD, FTIR, XRF and BET specific area. Cement samples were analyzed for their surface of fracture morphology, mechanical resistance and SBF bioactivity. Cement mechanical resistance was not satisfactory for biomedical application; nonetheless, sample's surface was coated by an apatite layer after immersion in SBF. Notwithstanding, to ensure that silicon is the element responsible for increasing the material's bioactivity it is necessary to evaluate the in vivo performance of the bone cement obtained in this work.

The use of porous bioresorbable scaffolds in the field of tissue engineering represents an alternative for the treatment of lesions and losses of biological tissues. This work evaluates the leaching salt effect of two different processes and polymers. Dense and porous scaffolds were prepared with poly(epson-caprolactone) (PCL) and poly(D,L-lactic acid-co-glycolic acid) (50/50) (PLGA50) by casting and melting compression process. Sodium citrate with particles sizes of 180-250 µm of diameter was used as porogen. The dense and porous samples were immersed in distilled water for 30 hours and evaluated for pH and mass variations, by scanning electronic microscopy (SEM), differential scanning calorimetric (DSC) and thermogravimetric analysis (TGA). The results of the analyses showed that the inclusion of the salt and leaching process did not affect the properties of the scaffold, indicating that the method is useful to make porous scaffolds to be potentially used in tissue engineering.

Foi estudada comparativamente a resposta do músculo tríceps sural e reto do abdome de ratos Wistar à implantação da polisulfona (PSU) e do polietileno de ultra alto peso molecular (UHMWPE ) sob a forma de bastões e partículas, por um período de até 52 semanas. Ao final, a PSU foi considerada como tendo a mesma biocompatibilidade do UHMWPE, segundo os critérios utilizados.

A comparative study was performed of the reaction of triceps sural and abdominal retus muscle of Wistar mice to implantation of polysulfone (PSU) and ultra high molecular weight poliethilene (UHMWPE) as particles and rods, for a period up to 52 weeks. At the end, PSU was considered as having the same biocompatibility as UHMWPE, according to the used method.