In the current work, XRD, SEM, EBSD and TEM techniques were used to evaluate the microstructure of stainless Fe-Mn-Si-Cr-Ni-Co shape memory steel processed by ECAE and annealed for one hour at temperatures ranging from 650ºC to 950ºC. The results were then correlated with the mechanical and shape-memory properties of the steel. It was observed that the samples containing large grains and a microstructure free of defects or precipitates presented a high volume fraction of multi-variant thermal martensite and stress-induced martensite, resulting in good shape recovery, owing to the memory effect. The grain refinement and precipitation of second-phase particles decreased the volume fraction and number of martensite variants and considerably increased the mechanical resistance, enhancing the elastic shape recovery. It was shown that shape memory properties were essentially related to the mechanical resistance of the matrix, which in turn was related to the microstructure.

A [211]-oriented niobium single crystal was deformed by equal channel angular pressing (ECAP) at room temperature using the route Bc to a total strain of 9.2. A sharp cube texture develops after ECAP processing. The deformed samples were annealed in vacuum from 400ºC (673 K) to 900ºC (1173 K) for 1 h to evaluate their microstructural stability. Scanning electron microscopy (SEM) was used to image the microstructures of as-deformed and annealed specimens. Electron backscatter diffraction (EBSD) was employed to determine the respective microtextures before and after annealing. Coarsening of the microstructure occurs at a maximum rate at 550ºC (823 K) due to discontinuous recrystallization. Normal grain growth replaces discontinuous recrystallization as the main coarsening mechanism above 700ºC (973 K).

ABSTRACT: Maraging steels have low carbon content and are highly alloyed, having as main feature the ability to increase the mechanical strength after thermal aging. Therefore, the objective of this work is to analyze the effect of aging in a Co-free maraging steel, Fe - 0.014% C - 0.3% Mn - 3.9% Mo - 2.1% Cu - 0.19% Si - 11.8% Cr - 9.1% Ni - 1.0% Ti (wt), at different heat treatment times (10 min - 960 min) at constant temperature (550°C), after cold rolling up to 66% and 77% area reduction. Microstructures were analyzed by scanning electron microscopy (SEM - EDS) and mechanical properties by Vickers hardness measurements. The results showed a significant increase in the hardness of the material after aging heat treatment on the solution treated and deformed samples. The aging heat treatment which was harder about 650 HV was 550°C/60 min.

The current work evaluated the microstructures and martensitic transformation temperatures of NiTi shape memory alloy (SMA) deformed by equal channel angular extrusion (ECAE). The Ti-55.27wt.%Ni alloy was processed by 1 ECAE pass at 250 °C using a die with an intersection angle of 120°. After processing, samples were annealed at 300 °C, 400 °C and 500 °C for 1h to evaluate the microstructural changes. Microstructural characterization was performed by scanning electron microscopy (SEM) equipped with an energy dispersive spectrometer (EDS) device, and Vickers hardness measurement. Martensitic transformations temperatures were analyzed by differential scanning calorimetry (DSC). Results show that the annealing treatments presented no significant change in the microstructure of the ECAE processed samples. Meanwhile, the DSC curves corresponding to the annealing treatments performed at 300 °C and 400 °C show two step martensitic transformation related to B2→R→B19'. For the annealing at 500 °C, the martensitic transformation temperatures returned to the ST condition, indicating a reduction of the processing defects.

The effect of the microstructure on the shape recovery in stainless Fe-8Mn-5Si-13Cr-6Ni-12Co shape memory steel (SSMS) was evaluated using tensile tests and reversion temperature of 600ºC for a pre-strain of 4%. The tests were performed for a solution treated and annealed conditions at different temperatures after wire drawing of 57% area reduction. The best total shape recovery (TSR) was 83% for a sample deformed and annealed at 850ºC. It was concluded that the elastic (or, superelastic) shape recovery (ESR) is high when the austenitic matrix strength is high surpassing the value of shape recovery due to memory effect (SR) and once the austenitic matrix becomes softer, the contribution of SR increases and that of ESR decreases.