ABSTRACT Composite materials using vegetal fibers and industrial waste are being applied in different areas and structures, requiring, more and more, researches that highlight their characteristics. In this context, the study of manufacturing techniques becomes increasingly necessary in order to use the appropriate tools and obtain the best conditions of the materials. Thus, this article demonstrates the behavior of the materials, which used the polyester resin with ground paper residue to generate the two composites studied in this paper, Polyester/smaller paper (PO/ PME) and Polyester/large paper (PO/PMA). These two materials were molded by hot compression and subjected to manufacturing processes. Joinery equipment were chosen for the experimentation of cutting, drilling, screw insertion and sanding to analyze the performance of these composite materials. As a general result, it can be observed that the composites maintained their physical integrity, because the particles of the load remained well anchored in the matrix in the two composite materials tested, giving the finish an aspect without damages, cracks or imperfections after the operations. Therefore, it is concluded that the materials created can be submitted to the manufacturing techniques evaluated in this article, reinforcing previous studies that suggest its use in the development of products such as furniture, table tops, decorative objects and others. Thus, this study contributes to Designer has knowledge of the potential of the material and make the best use of it.

ABSTRACT Concerns for the environment are recurrent in our society, and research on low impact materials such as those produced from waste is an alternative. This work is based on the reuse of scrap paper and rice hulls aiming to increase the life cycle of these waste products and to find better destination. Composites with a volumetric filler content (dispersed phase) of 80% were produced via compression molding using polyurethane (PU) based on castor oil or polyester resin as matrix, in four distinct families: polyester/rice hulls, PU/rice hulls, polyester/paper and PU/paper. The following tests were performed: water sorption, contact angle, hardness, impact and tensile testing. Scanning electron microscopy (SEM) was used for fracture morphology study. Basic visual analysis showed greater void content for the rice hull composites, making them less aesthetically appealing compared to paper. It was observed in the case of PU matrix the filler greatly influenced the rigidity since this pure material was more flexible compared to pure polyester. Filler incorporation decreased tensile strength of the polyester matrix but significantly increased that of the PU matrix.

ABSTRACT This study aimed to analyze the waterproofing MDF with different coatings. For this, a comparative study was conducted with the following coatings on MDF: Vegetable polyurethane resin on castor oil-based, acrylic lacquer and marine varnish. To carry out the research, sewed up the samples in sequence, they received the coatings, and then we performed the test water absorption. As a result, the polyurethane resin to castor oil-based coating was presented the best results, that is, lower levels of water absorption lower thickness swelling and volume. Finally, it is believed that the study of waterproofing MDF plant originated from polyurethane castor oil is beneficial because it is a renewable source of material.