Abstract Self-healing concrete (SHC) is obtained with self-healing agents, which can seal small cracks without additional repair works, improving concrete durability. The present paper studied the influence of cement content (450, 475, and 500 kg/m3) on mechanical properties (compressive and tensile strength) and porosity (capillary water absorption, water absorption, and void index) of SHC with crystalline admixture. A crack induction was carried out in SHC, and the results were compared with two reference concretes (with and without crack induction). SHC had similar compressive strength with reference concrete made without crack induction, independently of cement content. Water absorption and void index of SHC decreased with higher cement content, and a significant reduction of capillary water absorption was found after 90 days. The crystalline admixture was very efficient in decreasing concrete porosity mainly at longer ages. SHC made with high cement content developed a higher porosity reduction.

Resumo Além de vários aspectos positivos nas propriedades técnicas, aglomerantes geopoliméricos têm consideráveis vantagens do ponto de vista ambiental, com menor consumo de energia e menor emissão de CO2. Neste estudo, conduziu-se uma revisão sobre os materiais empregados na produção de geopolímeros por alguns pesquisadores brasileiros, e também um experimento empregando-se dois tipos de resíduos (resíduos de cerâmica vermelha e cinza de casca de arroz). A resistência à compressão do material resultante desenvolveu-se muito rapidamente, alcançando valor de 11 MPa após 1 dia. A microestrutura foi analisada por microscopia eletrônica de varredura, revelando uma microestrutura compacta e a presença de materiais precursores do resíduo de cerâmica vermelha que não reagiram completamente. Os resultados indicaram a viabilidade de se produzir material geopolimérico sem usar o silicato de sódio comercial e curado em temperatura ambiente, apresentando uma opção para a produção de materiais de construção com menores impactos ambientais.

Abstract In addition to several positive aspects in technical properties, geopolymeric binders have considerable advantages in the environmental point of view, with lower energy consumption and lower CO2 emission. In this study, it was conducted an overview about the utilized materials by some Brazilian researchers in geopolymers production, and also an experiment employing two types of wastes (red ceramic waste and rice husk ash). The compressive strength of the resulting material developed very fast, reaching a value of 11 MPa after one day. The microstructure was evaluated by scanning electron microscopy, revealing a compact microstructure and the presence of starting materials from the red ceramic waste that not completely reacted. The results indicated the feasibility of producing geopolymeric material without using commercial sodium silicate and cured at room temperature, showing an option for building materials production with lower environmental impacts.

Há dois tipos de especificações: prescritivas e por desempenho. As especificações prescritivas focam nas características das matérias-primas, na dosagem do concreto, na mistura e no transporte e numa grande variedade de operações, tais como lançamento e cura. Nestas especificações, o desempenho desejado do concreto não é necessariamente descrito. Por outro lado, as especificações por desempenho estipulam o que se requere do produto e não prescrevem como o produto deve ser produzido. Em outras palavras, elas focam no desempenho desejado ao invés de focarem nos materiais constituintes, dosagem e métodos construtivos. Esses aspectos são responsabilidade daqueles individuos que devem cumprir contratualmente com as especificações. Em contraste, as especificações por desempenho tratam daquilo que se requer do produto, e não prescrevem como esse produto deve ser produzido. Em outras palavras, ao invés de partirem dos materiais que compõem o concreto, partem do desempenho desejado, em termos de suas propriedades mensuráveis no estado plástico,endurecido e em termos de du- rabilidade, deixando a seleção dos materiais, a dosagem e os métodos construtivos a cargo daqueles que, contratualmente, devam atender às especificações. Nesse caso, como não há restrições dos materiais ou de suas proporções, soluções mais inovadoras podem ser usadas. Atualmente, a maioria das especificações de concreto é predominantemente prescritiva com alguns aspectos de desempenho. No entanto, há um consenso de que essa realidade deve ser mudada para um aumento de vida útil das estruturas. Esse artigo apresenta um panorama das especifica- ções internacionais e descreve os esforços internacionais para a implementação de especificações por desempenho na indústria do concreto.

There are two types of specifications: prescriptive and performance based. The prescriptive specifications focus on materials properties, materials proportions, mixing and transporting procedures and on a variety of processes, such as placing and curing. In these specifications, the concrete desired performance it is not necessarily described. On the other hand, performance specifications stipulate what is required from the product and do not prescribe how the product should be produced. In other words, they focus on the desired performance rather than on the concrete ingredients, materials selection, proportioning or construction methods. These are the responsibility of those individuals who contractually have to comply with the specifications. In this case, con- crete is defined in terms of measurable fresh and hardened properties and durability and as there are no restrictions regarding materials and their proportions in the performance specifications, innovative solutions may be used in order to achieve the performance requirements. Currently, most concrete specifications are predominantly prescriptive with some performance requirements. Nevertheless, there is a consensus that in order to extend the service life of concrete structures, this has to be changed. This paper gives an overview of the international specifica- tions and describes the international efforts on the performance specification implementation in the concrete industry.

O estudo dos fenômenos fluido-dinâmicos de escoamento em meios porosos tem sido de grande interesse por diversas áreas das ciências, de forma a se avaliar não só a permeabilidade do material, mas também analisar o comportamento do fluido permeante quando no interior destes materiais. Tratando-se de compósitos à base de cimento, a mensuração da permeabilidade torna-se fundamental para que sua durabilidade possa ser estimada, pois é a permeabilidade que controla a taxa de ingresso e movimentação de agentes deletérios no interior destes materiais. Dessa forma, diversas metodologias e equacionamentos matemáticos têm sido utilizados para prever a permeabilidade de materiais à base de cimento. No entanto, várias discrepâncias e disparidades nos resultados têm sido encontradas. Dentre as metodologias empregadas para mensurar a permeabilidade de meios porosos, encontra-se a desenvolvida por Thenoz, a qual tem demonstrado bons resultados em materiais à base de cimento. Dessa forma, este trabalho visa, por meio de ensaio de permeabilidade ao ar, realizado de acordo com a metodologia de Thenoz, avaliar o comportamento fluido-dinâmico do ar durante o ensaio de permeabilidade em argamassas. Para isto, foram utilizadas argamassas preparadas com dois tipos de cimento Portland (CP II E - 32 e CP III - 32), duas relações água/cimento (0,5 e 0,6) e ensaiadas em idades de 14 e 28 dias. Por meio dos resultados obtidos foi possível observar que durante o escoamento a compressibilidade do ar pode ser ignorada e o regime de escoamento pode ser considerado como laminar, demonstrando que a metodologia proposta por Thenoz e o equacionamento matemático empregado pode resultar em coeficientes de permeabilidade ao ar confiáveis, pois fenômenos e considerações que poderiam influenciar neste tipo de escoamento podem ser negligenciados.

Fluid-dynamic phenomena study in porous media flow has been of great interest for diverse areas of sciences. These studies not only have evaluated the permeability of porous media, but also to analyze the behavior of the fluid during the flow. Being about to the cement based materials, the measuring of the permeability becomes basic so that the durability of these can be estimate, therefore is the permeability that controls the rate of ingression and movement of deleterious agents inside these materials. Thus, diverse methodologies and mathematical equations have been used to foresee the permeability of cementitious materials, however, some discrepancies and nonsense in the results have been found. Amongst the used methodologies to measure the permeability of porous media, one meets developed it by Thenoz, which it has demonstrated good results in cement based materials. Thus, this work aims at, by means of assay of permeability to air, carried through in accordance with the methodology of Thenoz, to evaluate the fluid-dynamic behavior of air during the assay of permeability in mortars. For this, mortars prepared with two types of Portland cement of blast furnace (CP IIE-32 and CP III - 32), two relations water/cement (0.5 and 0.6) and ages of 14 and 28 days were used. By means of the gotten results it was possible to observe that during the draining the compressibility of air can be ignored, the regimen of draining can be considered as to plate, demonstrating that the methodology proposal for Thenoz and used mathematical equations can result in coefficients of trustworthy air permeability, therefore phenomena and considerations that could influence in this type of flow can be neglected, in accordance with what it is considered by literature.