Abstract Regular use of toothpaste with fluoride (F) concentrations of ≥ 1000 ppm has been shown to contribute to reducing caries increment. However, when used by children during the period of dental development, it can lead to dental fluorosis. Objective: In this study, we aimed to evaluate the in vitro effect of a toothpaste formulation with reduced fluoride (F) concentration (200 ppm) supplemented with sodium trimetaphosphate (TMP: 0.2%), Xylitol (X:16%), and Erythritol (E: 4%) on dental enamel demineralization. Methodology: Bovine enamel blocks were selected according to initial surface hardness (SHi) and then divided into seven experimental toothpaste groups (n=12). These groups included 1) no F-TMP-X-E (Placebo); 2) 16% Xylitol and 4% Erythritol (X-E); 3) 16% Xylitol, 4% Erythritol and 0.2%TMP (X-E-TMP); 4) 200 ppm F (no X-E-TMP: (200F)); 5) 200 ppm F and 0.2% TMP (200F-TMP); 200 ppm F, 16% Xylitol, 4% Erythritol, and 0.2% TMP (200F-X-E-TMP); and 7) 1,100 ppm F (1100F). Blocks were individually treated 2×/day with slurries of toothpastes and subjected to a pH cycling regimen for five days (DES: 6 hours and RE: 18 hours). Then, the percentage of surface hardness loss (%SH), integrated loss of subsurface hardness (ΔKHN), fluoride (F), calcium (Ca), and phosphorus (P) in enamel were determined. The data were analyzed by ANOVA (1-criterion) and the Student-Newman-Keuls test (p<0.001). Results: We found that the 200F-X-E-TMP treatment reduced %SH by 43% compared to the 1100F treatments (p<0.001). The ΔKHN was ~ 65% higher with 200F-X-E-TMP compared to 1100F (p<0.001). The highest concentration of F in enamel was observed on the 1100F treatment (p<0.001). The 200F-X-E-TMP treatment promote higher increase of Ca and P concentration in the enamel (p<0.001). Conclusion: The association of 200F-X-E-TMP led to a significant increase of the protective effect on enamel demineralization compared to the 1100F toothpaste.

Abstract Objective To evaluate the effects of fluoride (F) gels supplemented with micrometric or nano-sized sodium trimetaphosphate (TMPmicro and TMPnano, respectively) on the in vitro remineralization of caries-like lesions. Methodology Bovine enamel subsurface lesions (n=168) were selected according to their surface hardness (SH) and randomly divided into seven groups (n=24/group): Placebo (without F/TMP), 4,500 ppm F (4500F), 4500F + 2.5% TMPnano (2.5% Nano), 4500F + 5% TMPnano (5% Nano), 4500F + 5% TMPmicro (5% Micro), 9,000 ppm F (9000F), and 12,300 ppm F (Acid gel). The gels were applied in a thin layer for one minute. Half of the blocks were subjected to pH cycling for six days, whereas the remaining specimens were used for loosely- (calcium fluoride; CaF2) and firmly-bound (fluorapatite; FA) fluoride analysis. The percentage of surface hardness recovery (%SHR), area of subsurface lesion (ΔKHN), CaF2, FA, calcium (Ca), and phosphorus (P) on/in enamel were determined. Data (log10-transformed) were subjected to ANOVA and the Student-Newman-Keuls’ test (p<0.05). Results We observed a dose-response relation between F concentrations in the gels without TMP for %SHR and ΔKHN. The 2.5% Nano and 5% Micro reached similar %SHR when compared with 9000F and Acid gels. For ΔKHN, Placebo and 5% Nano gels had the highest values, and 5% Micro, 2.5% Nano, 9000F, and Acid gels, the lowest. All groups had similar retained CaF2 values, except for Placebo and Acid gel. We verified observed an increase in Ca concentrations in nano-sized TMP groups. Regarding P, TMP groups showed similar formation and retention to 9000F and Acid. Conclusion Adding 2.5% nano-sized or 5% micrometric TMP to low-fluoride gels lead to enhanced in vitro remineralization of artificial caries lesions.

Abstract Objectives: To evaluate the mechanical, physicochemical, and antimicrobial properties of four different formulations containing micro- or nanoparticles of sodium trimetaphosphate (mTMP and nTMP, respectively). Methodology: Four experimental groups were used in this investigation: two mTMP groups and two nTMP groups, each containing zirconium oxide (ZrO2), and solution containing either chitosan or titanium oxide (TiO2) nanoparticles (NPs). Setting time, compression resistance, and radiopacity were estimated. The agar diffusion test was used to assess the antimicrobial activity of the formulations against five different microbial strains: Streptococcus mutans, Lactobacillus casei, Actinomyces israelii, Candida albicans, and Enterococcus faecalis. Parametric and nonparametric tests were performed after evaluating homoscedasticity data (p<0.05). Results: From the properties evaluated, nTMP cements required less setting time and showed greater resistance to compression. Cements containing TiO2 showed greater radiopacity for both nTMP and mTMP. All four cement formulations showed antimicrobial activity against S. mutans and L. casei Conclusion: Formulations containing nTMP have shorter setting times and higher compressive strength, and those with TiO2 nanoparticles showed antimicrobial activities. Clinical relevance: The cement containing nTMP, ZrO2, and TiO2 could be an alternative material for protecting the pulp complex.

Abstract A new sugarcane-derived cystatin (CaneCPI-5) showed anti-erosive properties when included in solutions and strong binding force to enamel, but the performance of this protein when added to gel formulations and its effect on surface free energy (SFE) requires further studies. Objective 1) to evaluate the protective effect of gels containing different concentrations of CaneCPI-5 against initial enamel erosion (Experiment 1); and 2) to analyze the SFE (γS) after treating the enamel surface with CaneCPI-5 solution (Experiment 2). Methodology In Experiment 1, 75 bovine enamel specimens were divided into five groups according to the gel treatments: placebo (negative control); 0.27%mucin+0.5%casein (positive control); 0.1 mg/mL CaneCPI-5; 1.0 mg/mL CaneCPI-5; or 2.0 mg/mL CaneCPI-5. Specimens were treated with the gels for 1 min, the AP was formed (human saliva) for 2 h and the specimens were incubated in 0.65% citric acid (pH=3.4) for 1 min. The percentage of surface hardness change (%SHC) was estimated. In Experiment 2, measurements were performed by an automatic goniometer using three probing liquids: diiodomethane, water and ethylene glycol. Specimens (n=10/group) remained untreated (control) or were treated with solution containing 0.1 mg/mL CaneCPI-5, air-dried for 45 min, and 0.5 µL of each liquid was dispensed on the surface to measure contact angles. Results Gels containing 0.1 and 1.0 mg/mL CaneCPI-5 significantly reduced %SHC compared to the other treatments (p<0.05). Treated enamel showed significantly lower γS than control, without changes in the apolar component (γSLW), but the polar component (γSAB=Lewis acid-base) became more negative (p<0.01). Moreover, CaneCPI-5 treatment showed higher γS - (electron-donor) values compared to control (p<0.01). Conclusions Gels containing 0.1 mg/mL or 1.0 mg/mL CaneCPI-5 protected enamel against initial dental erosion. CaneCPI-5 increased the number of electron donor sites on the enamel surface, which may affect AP formation and could be a potential mechanism of action to protect from erosion.

Abstract The present study evaluated the ability of Bifidobacterium and Lactobacillus species associated with streptococci to increase insoluble extracellular polysaccharide (EPS) production and initial caries lesion progression. Bovine enamel blocks (n = 190; 4 mm x 4 mm) were prepared, selected according to initial surface hardness (SH), and divided into two groups: a) double combinations: S. mutans with Bifidobacterium or Lactobacillus, and b) triple combinations: S. mutans and S. sobrinus with Bifidobacterium or Lactobacillus species. The blocks were exposed to the bacterial associations for 7 days. Subsequently, quantity of EPS from biofilms and caries lesion depth were determined by means of colorimetric and cross-sectional enamel hardness (ΔKHN) analysis. The data were submitted to one-way analysis of variance, followed by the Bonferroni test (p < 0.05). S. mutans with B. animalis or B. dentium produced a higher quantity of EPS; S. mutans + B. animalis led to the highest ∆KHN. S. mutans + S. sobrinus + B. longum induced greater EPS and ∆KHN values. In conclusion, associations of B. animalis and B. longum with streptococci promoted EPS production and caries lesion progression.

Abstract This study evaluates how atenolol affects dental mineralization in offspring of female spontaneously hypertensive rats (fSHR) and normotensive Wistar rats (fW). fSHR and fW were treated with atenolol (100 mg/Kg/day, orally) during pregnancy and lactation. Non-treated fSHR and fW were the control groups. Enamel and dentin hardness were analyzed (Knoop, 15 g load, 10s) in mandibular incisor teeth (IT) and molar teeth (MT) obtained from the male offspring of atenolol-treated and non-treated fWistar and fSHR. Data were analyzed by ANOVA, followed by Tukey post hoc test (p < 0.05). Atenolol reduced the arterial blood pressure (SBP) in fSHR, but it did not change the SBP in fW. The offspring of non-treated fSHR had lower enamel (IT and MT) and dentin (IT) hardness than the offspring of non-treated fW (p < 0.05). Atenolol increased enamel and dentin hardness in the IT obtained from the offspring of fSHR and fW (p<0.05), but the offspring of fSHR presented higher values (p < 0.05). Atenolol did not alter enamel width in the IT obtained from any of the groups, but it increased enamel and dentin hardness in the IT obtained from the offspring of fSHR and fW. Atenolol affected the IT obtained from the offspring of fSHR. Atenolol increased only enamel hardness in the MT obtained from the offspring of fW. In conclusion, maternal hypertension reduces tooth hard tissues, and treatment with atenolol increases tooth hardness in male offspring of hypertensive and normotensive female rats.

Abstract Sources of calcium and phosphate have been added to dental restorative materials to improve their anticaries effect. Objective This study evaluated the effect of adding calcium glycerophosphate (CaGP) to resin-modified glass ionomer cement (RMGIC) on the physico-mechanical properties, ion release, and enamel demineralization. Material and Methods: Specimens were fabricated for each experimental group: RMGIC without CaGP (Control), RMGIC with 1, 3 and 9% CaGP. To determine the release of fluoride (F), calcium (Ca) and phosphorus (P), six specimens were immersed in demineralization and remineralization solutions for 15 days. In another experimental trial, the following physico-mechanical properties were evaluated at time intervals of 1 and 7 days after fabrication: compressive strength (n=12), diametral tensile strength (n=12), surface hardness of material (n=6) and the degree of conversion of monomers (n=8). To study enamel demineralization, specimens (n=12) were attached to enamel blocks and submitted to pH-cycling. Subsequently, surface and cross-sectional hardness and the concentration of F, Ca and P in enamel were determined. Results The addition of CaGP to RMGIC led to higher mean release of F, Ca and P when compared with control (p<0.001). Mechanical properties were within the range of those of the ionomer cements after addition of 1% and 3% CaGP. The degree of conversion did not differ between groups at the 1st and the 7th day (p>0.439). The addition of 3% and 9% CaGP reduced mineral loss and increased F, Ca and P in the enamel when compared with control (p<0.05). Conclusion The addition of 3% CaGP in RMGIC increased the release of F, P and Ca, reduced enamel demineralization, and maintained the physico-mechanical properties within the parameters for this material.

Abstract Dental applications based on the unique characteristics of amorphous calcium phosphate stabilized by casein phosphopeptides (CPP-ACP) have been proposed, as well as the improvement of its properties. Objectives: The objective of this study was to determine the ability of topically applied CPP-ACP from a commercial product to remineralize subsurface lesions when applied for extended periods of time (3 h and 8 h). Material and Methods: Artificially induced carious lesions were produced in 50 bovine enamel blocks previously selected by surface hardness. After treatments with gel without F and CPP-ACP applied for 1 minute (Placebo); 2% NaF neutral gel applied for 1 minute (Fluoride 1 min); CPP-ACP applied for 3 min (ACP 3 min); and CPP-ACP applied for 3 h (ACP 3 h) and for 8 h (ACP 8 h), the enamel blocks were submitted to the remineralization pH-cycling. Surface hardness and synchrotron micro-tomography were used to determine the percentage of surface hardness recovery (%SHR) and to calculate mineral concentration (gHAp.cm−3), respectively. The data were submitted to ANOVA followed by the Student-Newman-Keuls test (p<0.05). Results: Fluoride gel presented higher %SHR followed by ACP 3 min (p<0.001). No difference (p = 0.148) was found for Placebo, ACP 3 h and ACP 8 h groups for %SHR. Fluoride gel showed greater mineral concentration (p<0.001) when compared with the other groups. ACP 3 min demonstrated a significant difference (p<0.001) from ACP 3 h and ACP 8 h. The ACP 3 h and 8 h presented a subsurface lesion with development of laminations in all blocks. Conclusion: In this in vitro study the use of CPP-ACP for extended periods of time did not produce an additive effect in the remineralization process.

Abstract This study assessed fluoride (F) and sodium trimetaphosphate (TMP) release into artificial saliva from varnishes containing 0%, 2.5%, and 5% NaF, supplemented or not with 5% TMP. The varnishes were applied on polyester sheets (n = 8/group), and F and TMP released into artificial saliva were measured for up to 24 hours. The amount of F and TMP released were directly related to NaF and TMP concentrations in the varnishes. The highest F release was seen for 5% NaF and 5% NaF + 5% TMP, whereas 5% TMP released the highest amount of TMP. However, the simultaneous addition of NaF and TMP to varnishes significantly reduced the amount of F and TMP released from the products.

The aim of this study was to evaluate in vitro and in vivo the effects of 2 brands of probiotic fermented milk on biofilms, oral microbiota, and enamel. For the in situ experiment, ten volunteers wore palatine devices containing four blocks of bovine dental enamel over 3 phases, during which 20% sucrose solution, Yakult® (Treatment A), and Batavito® (Treatment B) were dropped on the enamel blocks. Salivary microbial counts were obtained and biofilm samples were analyzed after each phase. For the in vivo experiment, the same ten volunteers drunk Yakult® (Treatment C) and Batavito® (Treatment D) in two phases. Saliva samples were collected for microbial analysis after each phase. The in situ study showed that in comparison with Treatment A, Treatment B resulted in fewer total cultivable anaerobes and facultative microorganisms in biofilms, higher final microhardness, lower percentage change in surface hardness, and smaller integrated subsurface enamel hardness. In the in vivo study, Treatment D resulted in a reduction in the counts of all microorganisms. The results suggested that the probiotic fermented milk Batavito®, but not Yakult®, reduced the amount of oral microorganisms and mineral loss in bovine enamel.

O presente estudo avaliou a ação do trimetafosfato de sódio (TMP) e/ou fluoreto sobre a hidroxiapatita. Pó de hidroxiapatita foi suspenso em diferentes soluções: água deionizada, 500 µg F/mL, 1100 µg F/mL, 1%TMP, 3%TMP, 500 µg F/mL adicionado a 1%TMP e 500 µg F/mL associado a 3%TMP. O pH das soluções foi reduzido para 4,0 e depois de 30 min, elevado para 7,0 (três vezes). Depois do processo de ciclagem de pH, as amostras foram analisadas por difração de raios-X e espectroscopia por infravermelho. As concentrações de fluoreto de cálcio, fluoreto, cálcio e fósforo também foram determinadas. A adição de 1% ou 3% TMP na solução contendo 500 µg F/mL produziu uma maior quantidade de fluoreto de cálcio comparado às amostras tratadas com uma solução de 1100 µg F/mL. A respeito da concentração de cálcio, amostras tratadas com soluções de 1100 µg F/mL e 500 µg F/mL adicionado ao TMP foram estatisticamente similares e mostraram maiores valores. Soluções de 1100 µg F/mL e 500 µg F/mL adicionado ao TMP resultaram em uma proporção molar Ca/P mais próxima à da hidroxiapatita. Conclui-se que a associação de TMP e F favoreceu a precipitação de uma hidroxiapatita mais estável.

The present study analyzed the action of sodium trimetaphosphate (TMP) and/or fluoride on hydroxyapatite. Hydroxyapatite powder was suspended in different solutions: deionized water, 500 µg F/mL, 1,100 µg F/mL, 1%TMP, 3%TMP, 500 µg F/mL plus 1%TMP and 500 µg F/mL plus 3%TMP. The pH value of the solutions was reduced to 4.0 and after 30 min, raised to 7.0 (three times). After pH-cycling, the samples were analyzed by X-ray diffraction and infrared spectroscopy. The concentrations of calcium fluoride, fluoride, calcium and phosphorus were also determined. Adding 1% or 3% TMP to the solution containing 500 µg F/mL produced a higher quantity of calcium fluoride compared to samples prepared in a 1,100 µg F/mL solution. Regarding the calcium concentration, samples prepared in solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP were statistically similar and showed higher values. Using solutions of 1,100 µg F/mL and 500 µg F/mL plus TMP resulted in a calcium/phosphorus ratio close to that of hydroxyapatite. It is concluded that the association of TMP and fluoride favored the precipitation of a more stable hydroxyapatite.

No in situ protocol has assessed the dose-response effects of fluoride dentifrices involving low-fluoride formulations. Objective: To assess the ability of an in situ remineralization model in determining dose-response effects of dentifrices containing low fluoride concentrations ([F]) on bovine enamel. Material and Methods: Volunteers wore palatal appliances containing demineralized enamel blocks and brushed their teeth and devices with the dentifrices supplied (double-blind, crossover protocol) separately for 3 and 7 days. Surface hardness (SH), integrated subsurface hardness (ΔKHN) and [F] in enamel were determined. Data were analyzed by ANOVA, Tukey's test and Pearson's correlation (p<0.05). Results: Dose-response relationships were verified between [F] in dentifrices and SH, ΔKHN and enamel [F]. Higher correlation coefficients between enamel [F] and SH and ΔKHN were obtained for the 3-day period. Significant differences in SH and ΔKHN were observed among all groups for the 3-day period, but not between 0-275, 275-550, and 550-1,100 µg F/g dentifrices for the 7-day period, nor between 3- and 7-day periods for the 1,100 µg F/g groups. Conclusions: Considering that the peak remineralization capacity of the conventional dentifrice (1,100 µg F/g) was achieved in 3 days, this experimental period could be used in future studies assessing new dentifrice formulations, especially at low-fluoride concentrations.

Este estudo avaliou o efeito de diferentes concentrações de trimetafosfato de sódio (TMP) com e sem fluoreto (F) nas concentrações de cálcio (Ca), fósforo (P) e F na hidroxiapatita (HA). Pó de HA sintético (0,15 g) foi suspenso (n=6) em soluções (75 mL) de TMP com concentrações de 0%, 0,1%, 0,2%, 0,4%, 0,6%, 0,8%, 1,0%, 2,0%, 4,0%, 6,0%, 8,0% e 10% na presença ou na ausência de 100 ppm F e foram submetidas ao processo de ciclagem de pH. O precipitado foi filtrado seco a 70°C por 24 h e triturado em um pó fino. As concentrações de F (solúvel em KOH: CaF2, e em HCl: FA), Ca (Arsenazo III) e P (método do molibdato) foram determinadas na HA. Os dados de Ca, P e de proporção Ca/P foram submetidos ao teste de Tukey e os dados de F ao teste Student-Newman-Keuls (p<0,05). A adição de TMP reduziu a deposição de F em 98% (p<0,001). Os grupos contendo 100 ppm F e TMP 0,4% e 0,6% apresentaram maiores concentrações de Ca do que o grupo contendo somente 100 ppm F (p<0,05). Além disso, a HA tratada com 0,2% e 0,4% de TMP e 100 ppm F apresentou maiores proporções Ca/P em relação aos demais grupos (p<0,001). Em conclusão, TMP nas concentrações de 0,2%, 0,4% e 0,6% quando associado ao F é capaz de precipitar uma HA com menor solubilidade. Entretanto, especialmente em altas concentrações, TMP interfere com a deposição de F na HA.

This study evaluated the effect of different concentrations of sodium trimetaphosphate (TMP) with and without fluoride (F) on the concentration of calcium (Ca), phosphorus (P) and F in hydroxyapatite (HA). Synthetic HA powder (0.15 g) was suspended (n=6) in solutions (75 mL) of TMP at 0%, 0.1%, 0.2%, 0.4%, 0.6%, 0.8%, 1.0%, 2.0%, 4.0%, 6.0%, 8.0% and 10% concentrations in the presence and absence of 100 ppm F and subjected to a pH-cycling process. The precipitates were filtrated, dried at 70° C for 24 h and ground onto a fine powder. The concentrations of F (KOH (CaF2) and HCl (FA) soluble), Ca (Arsenazo III), and P (molybdate method) in HA were determined. The Ca P, and Ca/P ratio data were subjected to Tukey's test and the F data were subjected to Student-Newman-Keuls test (p<0.05). The addition of TMP to the samples reduced F deposition to 98% (p<0.001). The groups containing 100 ppm F and 0.4% or 0.6% TMP exhibited a higher Ca concentration than the group containing only 100 ppm F (p<0.05). Furthermore, the HA treated with 0.2% and 0.4% TMP and 100 ppm F showed a higher Ca/P ratio than the other groups (p<0.001). In conclusion, TMP at 0.2%, 0.4% and 0.6% concentrations combined with F seemed to be able to precipitate HA with low solubility. However, especially at high concentrations, TMP interferes with F deposition on HA.

O objetivo do presente trabalho foi avaliar in vitro o efeito de um dentifrício com reduzida concentração de fluoreto (450 µgF/g, NaF) associado ao citrato de cálcio (Cacit) e trimetafosfato de sódio (TMP) na remineralização do esmalte. Blocos de esmalte bovino tiveram sua superfície de esmalte polida seqüencialmente para determinação da dureza de superfície. Após o desenvolvimento de lesões artificiais de cárie, os blocos selecionados através da dureza de superfície foram submetidos a ciclagem de remineralização e tratamento diário com suspensões de dentifrícios (diluição em água deionizada ou saliva artificial): placebo, 275, 450, 550 e 1.100 µgF/g e com dentifrício comercial (controle positivo, 1.100 µgF/g). Ao término, determinou-se a dureza de superfície e em secção longitudinal, para cálculo da variação da dureza de superfície (%SH) e do conteúdo mineral (%∆Z). O fluoreto presente no esmalte também foi determinado. Os dados de %SH, %∆Z e fluoreto foram submetidos a análise de variância a dois critérios seguido pelo teste de Student-Newman-Keuls (p<0,05). O ganho mineral (%SH e %∆Z) foi maior para os dentifrícios diluídos em saliva (p<0,05), exceto para os dentifrícios 450 µg F/g com Cacit/TMP (p>0,05). Os dentifrícios 450 Cacit/TMP e controle positivo apresentaram resultados semelhantes (p>0,05) quando diluídos em água. Uma relação dose-resposta foi observada entre a concentração de fluoreto nos dentifrícios e o fluoreto presente no esmalte, independente da diluição. Concluiu-se que é possível melhorar a capacidade de remineralização de dentifrícios com reduzida concentração de fluoreto pela adição de compostos orgânico (Cacit) e inorgânico (TMP) com afinidade a hidroxiapatita.

The objective of this study was to evaluate in vitro the effect of a low fluoride toothpaste (450 µgF/g, NaF) combined with calcium citrate (Cacit) and sodium trimetaphosphate (TMP) on enamel remineralization. Bovine enamel blocks had the enamel surface polished sequentially to determine the surface hardness. After production of artificial carious lesions, the blocks selected by their surface hardness were submitted to remineralization pH cycling and daily treatment with dentifrice suspensions (diluted in deionized water or artificial saliva): placebo, 275, 450, 550 and 1,100 µgF/g and commercial dentifrice (positive control, 1,100 µgF/g). Finally, the surface and cross-section hardness was determined for calculating the change of surface hardness (%SH) and mineral content (%∆Z). Fluoride in enamel was also determined. The data from %SH, %∆Z and fluoride were subjected to two-way analysis of variance followed by Student-Newman-Keuls's test (p<0.05). The mineral gain (%SH and %∆Z) was higher for toothpastes diluted in saliva (p<0.05), except for the 450 µgF/g dentifrice with Cacit/TMP (p>0.05). The 450 Cacit/TMP toothpaste and the positive control showed similar results (p>0.05) when diluted in water. A dose-response was observed between fluoride concentration in toothpastes and fluoride present in enamel, regardless of dilution. It was concluded that it is possible to enhance the remineralization capacity of low F concentration toothpaste by of organic (Cacit) and inorganic (TMP) compounds with affinity to hydroxyapatite.

O presente estudo objetivou avaliar a capacidade de dentifrícios fluoretados acidulados (pH 4,5) em promover a remineralização do esmalte utilizando um modelo de ciclagem de pH e compará-lo a um dentifrício padrão (1.100 µgF/g). Blocos de esmalte tiveram suas superfícies polidas e a dureza de superfície determinada (SH). Em seguida, foram submetidos à desmineralização subsuperficial e a dureza de superfície pós-desmineralização foi determinada. Os blocos foram divididos em seis grupos experimentais (n=10): placebo (controle negativo), 275, 412, 550, 1.100 µgF/g e um dentifrício padrão (controle positivo). Os blocos foram submetidos à ciclagem de pH durante seis dias e tratamentos com dentifrício diluído duas vezes por dia. Após a ciclagem de pH, a dureza de superfície e em secção transversal foram avaliadas para obtenção da porcentagem de recuperação de dureza de superfície (%SHR) e área integrada da perda de dureza de subsuperfície (ΔKHN). Os resultados mostraram que %SHR foi semelhante entre os dentifrícios ácidos 412, 550, 1.100 µgF/g e controle positivo (teste de Tukey; p>0,05). Para ΔKHN, o dentifrício acidulado com 550 µgF/g mostrou uma performance melhor quando comparado ao controle positivo. Conclui-se que os dentifrícios acidulados 550 µgF/g apresentaram capacidade de remineralização semelhante ao controle positivo.

This study evaluated the capacity of fluoride acidic dentifrices (pH 4.5) to promote enamel remineralization using a pH cycling model, comparing them with a standard dentifrice (1,100 µgF/g). Enamel blocks had their surface polished and surface hardness determined (SH). Next, they were submitted to subsurface enamel demineralization and to post-demineralization surface hardness analysis. The blocks were divided into 6 experimental groups (n=10): placebo (without F, pH 4.5, negative control), 275, 412, 550, 1,100 µgF/g and a standard dentifrice (positive control). The blocks were submitted to pH cycling for 6 days and treatment with dentifrice slurries twice a day. After pH cycling, surface and cross-sectional hardness were assessed to obtain the percentage of surface hardness recovery (%SHR) and the integrated loss of subsurface hardness (ΔKHN). The results showed that %SHR was similar among acidic dentifrices with 412, 550, 1,100 µgF/g and to the positive control (Tukey's test; p>0.05). For ΔKHN, the acidic dentifrice with 550 µg F/g showed a better performance when compared with the positive control. It can be concluded that acidic dentifrice 550 µgF/g had similar remineralization capacity to that of positive control.