ABSTRACT The Ti-β alloys have become highly demanded in industry, due to their good physical and chemical characteristics. In the present work, a Ti-13Ta-3Sn (%at) alloy was synthesized using mechanical alloying (MA) between the times of 2 and 100h. The alloys were characterized by X-ray diffraction (XRD) and analyzed by the Rietveld method with the MAUD software. The microstructural changes and the evolution of the Ti-α and Ti-β phases were characterized. Identifying the presence of a new metastable fcc phase and the synthesis of an alloy with 79.80%wt of Ti-β phase, both alloys with nanometric crystallite size.

RESUMEN Las aleaciones Ti-β se han vuelto altamente demandadas en la industria, por sus buenas características físicas y químicas. En el presente trabajo, se sintetizó una aleación Ti-13Ta-3Sn (%at) por aleado mecánico con tiempos entre 2 y 100h. Las aleaciones se caracterizaron por difracción de rayos X (DRX) y los patrones se analizaron por el método Rietveld con el software MAUD. Se caracterizaron los cambios microestructurales y la evolución de las fases Ti-α y Ti-β. Se identificó la presencia una nueva fase metaestable fcc y la síntesis de una aleación con un 79,80% en peso de fase Ti-β, ambas con tamaño de cristalita nanométrico.

ABSTRACT Nickel aluminides have been extensively studied in recent decades to replace superalloys, in some components of aircraft turbines, because they have excellent corrosion resistance. Many industrial cities have the problem of air pollution, which has forced the study of the degradation of these alloys in the presence of acid rain. The aim of this work is to study the electrochemical corrosion behavior of nickel aluminides in a medium of simulated acid rain. Potentiodynamic Polarization, Linear polarization resistance curves, Rp, Nyquist data and Bode curves obtained by electrochemical impedance spectroscopy were used to study the corrosion behavior of two intermetallic compounds. The polarization curves show that both intermetallic Ni3Al and NiAl have very similar corrosion potential, showing a slightly nobler behavior the NiAl intermetallic. The intermetallic Ni3Al has an active-passive behavior where the anode branch presents a general dissolution of the alloy, indicating that it is under cathodic control. NiAl intermetallic shows an active dissolution region, followed by a passive behavior. At longer immersion times, Ni3Al intermetallic has a higher polarization resistance, which means a lower corrosion rate.