Natural fibers are increasingly used as composite reinforcement in different fields of engineering. Caraua fiber stands out for its good mechanical properties and adherence to resin; however, little is known about its behavior in the manufacture of a composite or whether classic failure theory applies in this case. The present study assesses the mechanical properties of two laminas reinforced with unidirectional curaua fiber containing fiber volume fractions of 30 % and 22 %, and compares the results with the values obtained for four failure criteria, using analysis of variance (ANOVA). To that end, tensile tests were conducted along the fiber direction and at other loading angles, in addition to iosipescu shear tests. The results show that the Hashin criterion was the best and the maximum stress criterion does not represent the failure behavior of these materials.

ABSTRACT This study aimed to assess the effect of hybridization on thermomechanical properties and water absorption of composite materials, by introducing sisal fiber tissue into the material. To that end, two composite material plates were manufactured, the first with five layers of E-glass reinforcement mat and the second with three layers of E-glass fiber interspersed with two layers of sisal fibers, both used as an orthophthalic polyester resin matrix. The material was then submitted to tensile, three-point bending and water absorption tests. It was observed that hybridization causes a change in both the final strength and stiffness of the material.