Thin films containing silver nanoparticles homogeneously dispersed, with narrow size distribution below 10 nm, were synthesized on flat glass surface, by using an ionic silsesquioxane as stabilizer and crosslinking agent. The films can be prepared without previous functionalization of substrate surfaces and without addition of other components. The films were heat treated up to 200 ºC and characterized by ultraviolet-visible, transmission electron microscopy, atomic force microscopy, thermogravimetric analysis and ellipsometry. The films were thermally stable when heated up to 200 ºC, presenting the same thickness, and maintaining both optical and morphological properties of silver nanoparticles. The antibacterial activity of the films, containing the silver nanoparticles, was evaluated against Staphylococcus aureus by using the film applicator coating method, showing an excellent performance even after the third cycle of sterilization.

Tratamentos superficiais por plasma e ultravioleta de vácuo (VUV) foram utilizados para introduzir grupos funcionais contendo oxigênio em amostras de polipropileno, com objetivo de modificar sua molhabilidade. Análises por ATR-FTIR, AFM e ângulo de contato (AC) foram utilizadas para analisar as mudanças químicas e físicas na superfície do PP em função do tempo. Os resultados mostraram que as mudanças na molhabilidade das amostras tratadas por VUV ocorreram principalmente devido à alteração química da superfície. Nas amostras tratadas por plasma, o envelhecimento ocorreu mais rapidamente que as amostras tratadas por VUV. Para ambos os tratamentos, provavelmente ocorreu um rearranjo das cadeias durante o envelhecimento, além de uma possível reticulação da superfície na amostra tratada por VUV.

Surface treatments using plasma and vacuum ultraviolet radiation (VUV) were used to introduce oxygen-containing functional groups in samples of polypropylene, in order to modify its wettability. ATR-FTIR, AFM and contact angle (CA) measurements were used to analyze the chemical and physical changes on the PP surface as a function of time. The results showed changes in wettability of the VUV-treated samples mainly due to chemical modification of the surfaces. For plasma-treated samples, aging occurred faster than for the VUV-treated ones. For both treatments, a rearrangement of the polymer chains during aging has probably occurred, with possible crosslinking of surface macromolecules for the VUV-treated samples.