Abstract This paper presents the results of experimental investigation on microstructure (size and morphology of eutectic Si), impact toughness and sliding wear properties of A356 Al-Si alloy and composites containing 10, 20 and 25 wt% of SiCp reinforcement produced by semisolid stirring technique. The results revealed that an increase in SiCp content leads to a reduction in the size of eutectic Si and also changes its morphology from plate-like to equiaxed. Furthermore, addition of 10 and 20 wt% silicon carbide reinforcement decreased the impact toughness by 6 and 18%, respectively. A356/25wt%SiCp composite registered the lowest impact toughness with reduction of 33% due to debonding and agglomeration of SiCp in the matrix. The sliding wear results showed that the wear resistance of the composites was significantly higher than that of the matrix alloy due to the increase in hardness as well as reduction in the size and also morphology transformation of eutectic silicon with increase in SiCp content. However, the existence of particle-porosity clustering with increasing the SiCp content to 25 wt% played a significant role in deteriorating the wear behavior of the composite.

Effect of calcium addition on microstructure, hardness value and corrosion behavior of five different Mg-xCa binary alloys (x = 0.7, 1, 2, 3, 4 wt. (%)) was investigated. Notable refinement in microstructure of the alloy occurred with increasing calcium content. In addition, more uniform distribution of Mg2Ca phase was observed in a-Mg matrix resulted in an increase in hardness value. The in-vitro corrosion examination using Kokubo simulated body fluid showed that the addition of calcium shifted the fluid pH value to a higher level similar to those found in pure commercial Mg. The high pH value amplified the formation and growth of bone-like apatite. Higher percentage of Ca resulted in needle-shaped growth of the apatite. Electrochemical measurements in the same solution revealed that increasing Ca content led to higher corrosion rates due to the formation of more cathodic Mg2Ca precipitate in the microstructure. The results therefore suggested that Mg-0.7Ca with the minimum amount of Mg2Ca is a good candidate for bio-implant applications.