Abstract Materials such as magnesium phosphate cement (MPC) have attracted significant attention of researchers, therefore, understanding the effects of dosage parameters, such as water content and MgO/NH4H2PO4 ratio on phase formation is essential for obtaining cementitious matrices with improved performance. In the present work MgO was sintered at 900 °C and 1110 °C in a conventional oven, and the effect of water concentration and MgO/NH4H2PO4 (or ADP) ratio on the properties of MPC was evaluated in terms of phase formation by X-ray diffraction, pore size distribution, mechanical properties, and microstructure. For less-reactive MgO (calcined at 1100 °C) with a high MgO/ADP ratio, increased water content did not cause additional solubilization of ADP or formation of more hydrated phases, although the cement porosity increased. Compositions with more reactive MgO (calcined up to 900 °C) formed dittmarite (NH4MgPO4.H2O) independent of water content. Higher water content and MgO calcination temperature were associated with increased MPC setting time and decreased mechanical strength due to higher porosity.

Magnesium phosphate cements (MPCs) are formed when an aqueous solution of ammonium dihydrogen phosphate (ADP, NH4H2PO4) and magnesium oxide (MgO) react in the presence of other aggregates for filling or reinforcement (e.g., fibers, waste, and sand). Therefore, understanding how the MgO/ADP ratio influences phase formation to produce cementitious matrices with better performance is essential. MgO dissolved in an acid solution undergoes numerous transformations because of which different opinions exist regarding the mechanisms by which the setting reactions and formation of hydrated phases occurs in MPCs. In this study, the effect of different MgO/ADP ratios on the properties of MPCs was evaluated regarding phase formation using X-ray diffraction, setting time, and pore size distribution. Increased ADP concentration was found to increase the concentration of hydrated phases, however, this increases the pore content while decreasing the apparent density of MPCs. Compared with compositions with lower MgO/ADP ratios, the composition with the highest MgO/ADP ratio required higher setting time due to the lower concentration of hydrated phases.

This paper aims to evaluate the synthesis and annealing parameters for production of nanometric Bi4Ti3O12 and its properties. The powders were obtained through the solution combustion route and the impacts of annealing temperature on the materials’ physicochemical features as well as their optical and electrical properties were investigated. Thus, the prepared powders were annealed at 600ºC, 700ºC and 800ºC and then characterized by several techniques. The results demonstrated that the combustion method was effective for production of nanocrystalline powders with high levels of purity. A trend for particle and crystallite growth was observed as the calcination temperature increased. X-Ray, HRTEM and Raman spectroscopy confirmed the crystalline nature of the powders, whereas impedance spectroscopy demonstrated a reduction of electrical resistance according to the calcination temperature applied. Optical properties were not highly influenced by annealing. The temperature of 600ºC was appropriate to produce crystalline particles with desirable low sizes for application.

This paper aims to study the influence of including wood sawdust and sodium silicate in the production process of calcined clay lightweight ceramics. In the production process first, a sample used by a company that produces ceramic products in Brazil was collected. The sample was analysed by techniques of liquidity (LL) and plasticity (LP) limits, particle size analysis, specific mass, X-ray diffraction (XRD) and X ray fluorescence spectrometry (XRF). From the clay, specimens of pure clay and mixtures with wood sawdust (10%, 20% and 30% by mass) and sodium silicate were produced and fired at a temperature of 900 ºC. These specimens were submitted to tests of water absorption, porosity, specific mass and compressive strength. Results of this research indicate that the incorporation of wood sawdust and sodium silicate in the ceramic paste specimens can be useful to make calcined clay lightweight ceramics with special characteristics (low values of water absorption and specific mass and high values of compressive strength), which could be used to produce calcined clay lightweight aggregates to be used in structural concrete.

Coprecipitation synthesis of nanocrystalline india-stabilized zirconia with high surface area and codoping with MoO3, WO3, TaO2.5, or NbO2.5 is reported. The concentration of codopants was defined by the charge-compensating mechanism. Ethanol washing followed by azeotropic distillation and freeze drying were compared as dehydration techniques for the gels. As determined by XRD and Raman scattering, 9 mol% of InO1.5 plus charge-compensating dopants is sufficient to completely stabilize the high-temperature tetragonal phase of zirconia. The effect of alloying hexavalent and pentavalent oxides was secondary compared to the InO1.5 concentration in the retention of the tetragonal structure. Improved specific surface area of 106.1 m2 g‒1 and crystallite size between 8 and 9 nm were achieved through ethanol washing and subsequent azeotropic distillation even after calcination at 600 ºC. This result is attributed to the effect of the incorporation of ethoxy and butoxy groups after the treatment of the gels in organic medium, as detected by FT-IR spectroscopy and DSC/TG.

Ba0.5Sr0.5Co0.8Fe0.2O3-δ (BSCF) perovskite-type oxide is currently one of the most promising materials for applications in solid-oxide fuel cells (SOFCs), protonic ceramic fuel cells (PCFCs), oxygen separation membranes, and catalytic membranes for methane conversion. BSCF powder synthesis has received considerable attention and new synthesis methods have been proposed to obtain nanoscale powders with high chemical homogeneity. In this study, BSCF perovskite powder has been successfully prepared by microwave assisted combustion in aqueous solution. The synthesized powder was characterized by DSC, BET, XRD, and SEM. BSCF powder presented phase homogeneity, high specific surface area (9.93 g/m2) and nanometric crystallite size (23nm). The microwave sintering has been conducted in different conditions of dwell time and temperature. The influence of the temperature and the dwell time on microstructure was evaluated by optical microscopy. The results showed that microwave sintering could achieve the same densification compared to conventional sintering with only 10% of processing time. This shorter processing time has resulted in a reduction of grain size of up to 46.5%, compared to conventional sintering.

Copper-substituted bismuth vanadate has been considered a promising material for composite cathodes in SOFC. However, high reactivity of BICUVOX.10 towards the electrolytes still has been its greatest shortcoming. This paper describes reactions between BICUVOX.10 and yttria-stabilized zirconia (YSZ) electrolytes. Secondary phases formed were evaluated by X-ray diffraction, scanning electron microscopy and a.c. impedance spectroscopy. A deleterious interaction between BICUVOX.10 and YSZ was observed, mainly regarding the yttrium depletion from ZrO2 lattice through reaction with VO2.5, resulting in YVO4 phase nucleation and destabilization of the tetragonal and cubic ZrO2 polymorphs to monoclinic. The ZrO2 destabilization and YVO4 nucleation are related phenomena and were interpreted through a theoretical mechanism using charge-compensating dopants description. Thus, these reactions were seen as detrimental to the cathode/electrolyte contact, especially regarding the highly resistive layer formed in the BICUVOX.10/YSZ junction, discouraging further usage of BICUVOX.10 as a cathode in yttria-stabilized zirconia electrolytes.

This study evaluated the feasibility of using sugar cane bagasse ash (SCBA), a by-product of the sugar cane ethanol industry, obtained under controlled calcination as a partial replacement for Portland cement in mortars. Materials with pozzolanic characteristics may be used to partially replace cement in mortars or concrete and are known to provide durability to the products. Initially, TG/DTA curves of the sugar cane bagasse were conducted to define suitable calcination temperatures (500ºC, 600ºC and 700ºC), and tests were conducted to characterize the physical-chemical parameters of the SCBA and the pozzolanic activity according to NP EN 196-5. The results showed the technical feasibility of using the SCBA as a pozzolanic material in construction, which would provide an alternative to proper disposal for this waste while providing products with high technical performance.

Red mud, the main waste generated in aluminum and alumina production by the Bayer process, is considered hazardous due to its high pH, according to the Brazilian standard NBR 10004/2004, and worldwide generation of this waste exceeds 117 million tons/year. In this work, non-calcined red mud was used, thus requiring less energy and time and reducing costs, which is the ideal condition for reusing wastes. Mortars containing 30 wt. (%) of cement substituted by red mud showed higher strength of hardened products. The pozzolanic activity index was evaluated based on physical and mechanical parameters (Brazilian NBR 5751 and NBR 5752 standards) and on a chemical analysis (European EN 196-5 standard). A comparison of the reference mixture (without red mud) and the results obtained with red mud confirm the potential of non-calcined red mud for use a as pozzolanic additive in cementitious materials. The setting time (according to the MERCOSUL NM 65 standard) tends to increase but workability remains almost unchanged.

Red mud, which is a solid waste produced in the alumina production process, is classified as dangerous due to its high pH. In this work, the concentration of chlorides was monitored by measuring the conductivity of the anolyte, which initially was distilled water. The steady and nonsteady-state chloride diffusion coefficients were estimated from the "time lag"� and "equivalent time" between diffusion and migration experiments. The capillary water absorption, apparent porosity and pore size distribution of concretes were also analyzed. The addition of red mud apparently ensured lower chloride diffusion in the tested mixtures due to its superfine particle-size distribution and its "filler"� effect. Red mud lengthened the service life of the concrete to 35 years (double that of the reference concrete). This finding is very positive since it indicates a delay in the onset of the rebar corrosion process caused by the migration of chloride ions.

The sheave leather was subjected to chemical treatment in an attempt to immobilize chromium ion in a matrix of cement. Cementitious pastes were obtained by adding different proportions of waste treated solutions (5 and 10% compared to the cement mass) and the pH and setting time (hardening) were measured. Aiming to check the leather influence in Portland cement pastes, the phases formation were observed by X-ray diffraction (XRD). The results showed that the pretreatment was effective for the waste dissolution and the pH of treated waste chemical solutions did not influence significantly the characteristics of cement paste, with a slight increase in setting time results.

Magnesium phosphate cement materials are formed by reacting magnesium oxide with water-soluble phosphates such as monoammonium dihydrogen phosphate (ADP), which solidifies at ambient temperature through the formation of hydrated phases in the material. Cylindrical specimens of magnesium phosphate cement were molded and varying amounts (0 to 30% weight) of grinding dust were added to the ceramic matrices. The influence of the addition of grinding dust on the characteristics of the mortars in terms of microstructure (SEM), mechanical strength and capillary water absorption was verified. The results obtained proved very satisfactory for the use of this waste as an additive in magnesium phosphate mortars.

The constant heating rate method employed in sintering studies offers several advantages over the isothermal method, particularly the fact that all the parameters that describe the sintering phenomena can be obtained from a single sample. The purpose of this work is to determine the parameters of sintering kinetics of nanosized Ni-Zn ferrite powders synthesized by combustion reaction. The nonisothermal sintering method was studied using a constant heating rate (CHR). The Ni-Zn ferrite powders, with average particle size varying from 18 nm to 29 nm, were uniaxially pressed and sintered in an horizontal dilatometer at a constant heating rate of 5.0 °C/min from 600 °C up to complete densification, which was reached at 1200 °C. The compacts were characterized by scanning electron microscopy (SEM). Experimental results revealed three different sintering stages, which were identified through the Bannister Theory. The shrinkage and the shrinkage rate analyzed showed a viscous contribution in the initial sintering stage, which was attributed to the mechanism of structural nanoparticle rearrangement.