Abstract Fly ash is one of the main precursors for alkali-activated cement.However, the combined use of fly ash and bottom ash is not common and little information is present.Therefore, this paper focuses on investigating the fresh and hardened properties of alkali-activated pastes with the addition of fly ash and bottom ash. In the fresh state, setting time, fluidity and plasticity were evaluated. In the hardened state, mechanical, chemical, and microstructural properties were evaluated.The incorporation of bottom ash up to 50% improves the workability of the pastes, in addition to acting as a retardant for setting. Mechanical strength tends to decrease with increasing ash content.However, the paste containing 100% bottom ash was 14.4 MPa, indicating potential for application. The main reaction product was identified in chemical and microstructural analyses as the N-A-S-H gel.In general, the blend based on bottom ash and fly ash has the potential for alkali activation, so a higher valorization of these by-products can be obtained, especially of the bottom ash.

Resumo A cinza volante é um dos principais precursores para cimentos álcali-ativados. Contudo, o uso combinado de cinza volante e cinza pesada não é comum e são poucas as informações disponíveis. Portanto, o foco deste artigo é investigar as propriedades no estado fresco e no estado endurecido de pastas álcali-ativadas com adição de cinza volante e cinza pesada. No estado fresco foram avaliados o tempo de pega, a fluidez e a plasticidade. No estado endurecido foram avaliadas propriedades mecânicas, químicas e microestruturais. Os resultados indicam que a incorporação de cinza pesada em até 50% melhora a trabalhabilidade das pastas, além de atuar como retardador de pega. A resistência mecânica tende a diminuir com o aumento do teor de cinza pesada. Contudo, a pasta contendo 100% de cinza pesada alcançou 14,4 MPa, indicando potencial de aplicação. O gel N-A-S-H foi identificado nas análises químicas e microestruturais como principal produto de reação. De modo geral, a mistura à base de cinza pesada e cinza volante tem potencial para a álcali-ativação, portanto, pode-se obter uma maior valorização desses subprodutos, principalmente da cinza pesada.

ABSTRACT The chemical composition of ceramics has a deep impact on our understanding of their physical and chemical properties. This work performed a chemical and mineralogical characterization of clay mixtures with incorporation of a residue from the steel industry. The clay mixtures could be used in the brick production. Two types of clays were mixed with the proportion of 1:1 and the residue were incorporated with the proportions of 5%, 10%, 15%, and 20%. Each material had their chemical composition analysed before the burning step. Five specimens were used to analyse their mineralogical composition after the burning step at the temperature of 800 °C. The tests performed to make the characterization were: X-Ray Fluorescence (XRF), X-Ray Diffraction (XRD), Thermogravimetry (TG) and Differential Scanning Calorimetry (DSC). The XFR analysis showed that the main components of the clays are the silicon oxide (SiO2) and the aluminium oxide (Al2O3), and for the residue, the main components are the iron oxides, represented by iron content (T-Fe). The XRD analysis showed the quartz as the most abundant mineral in clays, but that hematite, the most abundant mineral in the residue, appeared more as the amount of residue increased in the sample. Thermal Analysis confirmed the expected peaks in clays and identified an exothermic reaction in the sample with residue. The increase in the percentage of residue caused changes in the chemical composition of the samples, however, these variations were not remarkable, which suggests the red clay industry could add the residue in its production.

RESUMO A composição química das cerâmicas tem grande importância no entendimento das propriedades químicas e físicas desse material. Neste trabalho foram realizadas caracterizações química e mineralógica de misturas de argilas, incorporando um resíduo proveniente de uma indústria siderúrgica, para aplicar na produção de cerâmica. Dois tipos de argila foram misturados na proporção de 1:1 e o resíduo foi adicionado nas proporções de 5%, 10%, 15% e 20%. Avaliou-se a composição química de cada material puro e a composição mineralógica foi analisada após a etapa de queima, na qual 5 corpos de prova foram submetidos a uma temperatura de 800 °C. A caracterização foi realizada com os ensaios de Fluorescência de Raios X (FRX), Difração de Raios X (DRX), Termogravimetria (TG) e Calorimetria Exploratória Diferencial (DSC). A FRX mostrou os óxidos de silício (SiO2) e alumínio (Al2O3) como principais componentes das argilas e os óxidos de ferro (T-Fe, teor de ferro) como principais componentes do resíduo. A DRX mostrou o quartzo como o mineral mais abundante nas argilas, mas que à medida que a concentração de resíduo aumentava na amostra, aumentava também o teor de hematita, principal mineral encontrado no resíduo. A TG e a DSC confirmaram picos esperados nas argilas e identificou uma reação exotérmica nas amostras com resíduo. O aumento do percentual de resíduo provocou alterações na composição química das amostras, no entanto, não foram alterações significativas, o que indica a possibilidade do uso desse resíduo na produção de cerâmica vermelha.

RESUMO Foi estudada a viabilidade técnica da utilização de resíduos de granito como matéria prima na fabricação de corpos de prova cerâmicos, com adições dos Produtos da Combustão do Carvão Mineral (PCC’s) como fase reforço. Os materiais utilizados foram granito Asa Branca (RGAB) e os Produtos da Combustão do Carvão mineral (PCC´s), nas concentrações de 0%p, 5%p, 10%p, 15%p, 20%p, 25%p e 30%p de PCC´s. Para a caracterização das matérias primas e das amostras foram utilizadas as técnicas de: Difração de Raios-X, Fluorescência de Raios-X, Microscopia Eletrônica de Varredura. Para a determinação das propriedades mecânicas foram realizados os ensaios de Microdureza Vickers e Resistência à compressão diametral. Foram feitos ensaios de Microscopia óptica e EDS a fim de verificar entre as composições químicas da superfície e do interior das amostras. Foi feito análise estatística dos resultados (análise de variância – ANOVA), através do teste de Tukey, que teve como objetivo comparar se as médias aritméticas obtidas nos testes mecânicos eram estatisticamente significantes. Foi atribuído o número 1, para os pares em que as médias eram estatisticamente diferentes, e o número 0, para parem em que não houve diferença estatística entre as médias. Os resultados obtidos permitem concluir que o uso do rejeito do Granito Asa Branca com a adição de PCC´s para a fabricação de revestimento cerâmico é viável.

ABSTRACT The technical feasibility of the use of granite residues as raw material in the manufacture of ceramic test specimens, with additions of the Coal Mineral Combustion (PCC's) products as a reforestation phase, was studied. The materials used were White Wing granite (RGAB) and Coal Combustion Products (PCC), in concentrations of 0% w / w, 5% w / w, 10% w / w, 15% w / P of PCCs. For a characterization of the raw materials and the samples with the techniques of: X-Ray Diffraction, X-Ray Fluorescence, Scanning Electron Microscopy. For a determination of the mechanical properties performed with tests of Vickers Microhardness and Diametral Compression Resistance. Optical microscopy and EDS assays were performed to verify the chemical composition of the surface and the interior of the samples. Statistical analysis of the results (analysis of variance -ANOVA) was analyzed through the Tukey test, which had as objective as sections as arithmetic means obtained in the mechanical testicles were statistically significant. We assigned the number 1, for the pairs in which as means are statistically different, and the number 0, to stop where is not the statistical difference between as means. The results obtained allow to conclude the use of the tailings of the Asa Branca Granite with an addition of PCC to a ceramic coating manufacturing is feasible.

RESUMO O Fosfato Tricálcico-β (TCP-β) é um material sintético que apresenta composição química similar à do tecido ósseo, sendo, por essa razão, frequentemente empregado como biomaterial. Nesta pesquisa, TCP-β foi sintetizado por reação via estado sólido e caracterizado por Difração de Raios X (DRX), Espectroscopia de Infravermelho (IV), Microscopia Eletrônica de Varredura (MEV) e Espectroscopia de Raios X por Dispersão de Energia (EDX). A área superficial e a distribuição do tamanho de partículas foram determinadas pelo método BET (Brunauer-Emmet-Teller). Também se realizou teste de citotoxicidade segundo as normas ISO 10993-5 e ISO 10993-12. As técnicas de DRX e IV permitiram confirmar a formação da fase fosfato tricálcico-β, mediante seus padrões de difração e dos grupos funcionais característicos, respectivamente. Através do BET, constatou-se o caráter nanométrico das partículas sintetizadas. O MEV permitiu comparar a evolução da morfologia microestrutural, antes e após o tratamento térmico. Com os resultados de EDX, calculou-se a razão molar entre cálcio e fósforo, parâmetro usualmente empregado para identificação das diferentes fases de apatitas. No ensaio de citotoxicidade, as amostras não apresentaram alterações celulares (morfologia) e nem inibição do crescimento celular, indicando que, nas condições in vitro, o material não é tóxico. Todas essas caracterizações sugerem que o fosfato tricálcico-β obtido pode ser potencialmente utilizado para aplicações biomédicas.

ABSTRACT The β-tricalcium phosphate (β-TCP) is a synthetic material that present similar chemical composition to bone tissue and is frequently used as biomaterial. In this research, β-TCP was synthesized by solid state reaction and characterized by X-ray Diffraction (XRD), Infrared (IR) Spectroscopy, Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDX). The surface area and particle size distribution were determined by BET method (Brunauer-Emmet-Teller). A cytotoxicity test was performed according to ISO 10993-5 and ISO 10993-12. Diffraction patterns (XRD) and characteristic functional groups (IR) of material allowed to confirm the formation of the β-TCP phase. BET leaded to verification of the nanometric character of the synthesized particles. SEM allowed to compare the evolution of the microstructural morphology before and after heat treatment. Molar ratio of calcium phosphate nanoparticles, usually used to identify the different phases of apatites, was calculated by EDX. In the cytotoxicity assay, the samples showed no cellular morphological

RESUMO O Fosfato Tricálcico-β (TCP-β) é um material sintético que apresenta composição química similar à do tecido ósseo, sendo, por essa razão, frequentemente empregado como biomaterial. Nesta pesquisa, TCP-β foi sintetizado por reação via estado sólido e caracterizado por Difração de Raios X (DRX), Espectroscopia de Infravermelho (IV), Microscopia Eletrônica de Varredura (MEV) e Espectroscopia de Raios X por Dispersão de Energia (EDX). A área superficial e a distribuição do tamanho de partículas foram determinadas pelo método BET (Brunauer-Emmet-Teller). Também se realizou teste de citotoxicidade segundo as normas ISO 10993-5 e ISO 10993-12. As técnicas de DRX e IV permitiram confirmar a formação da fase fosfato tricálcico-β, mediante seus padrões de difração e dos grupos funcionais característicos, respectivamente. Através do BET, constatouse o caráter nanométrico das partículas sintetizadas. O MEV permitiu comparar a evolução da morfologia microestrutural, antes e após o tratamento térmico. Com os resultados de EDX, calculou-se a razão molar entre cálcio e fósforo, parâmetro usualmente empregado para identificação das diferentes fases de apatitas. No ensaio de citotoxicidade, as amostras não apresentaram alterações celulares (morfologia) e nem inibição do crescimento celular, indicando que, nas condições in vitro, o material não é tóxico. Todas essas caracterizações sugerem que o fosfato tricálcico-β obtido pode ser potencialmente utilizado para aplicações biomédicas.

ABSTRACT The β-tricalcium phosphate (β-TCP) is a synthetic material that present similar chemical composition to bone tissue and is frequently used as biomaterial. In this research, β-TCP was synthesized by solid state reaction and characterized by X-ray Diffraction (XRD), Infrared (IR) Spectroscopy, Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDX). The surface area and particle size distribution were determined by BET method (BrunauerEmmet-Teller). A cytotoxicity test was performed according to ISO 10993-5 and ISO 10993-12. Diffraction patterns (XRD) and characteristic functional groups (IR) of material allowed to confirm the formation of the β-TCP phase. BET leaded to verification of the nanometric character of the synthesized particles. SEM allowed to compare the evolution of the microstructural morphology before and after heat treatment. Molar ratio of calcium phosphate nanoparticles, usually used to identify the different phases of apatites, was calculated by EDX. In the cytotoxicity assay, the samples showed no cellular morphological changes or inhibition of cell growth, indicating that the material is non-toxic. All these characterizations suggest that the obtained β-tricalcium phosphate may be potentially used for biomedical applications.