OBJECTIVES: To compare, in vivo, the accuracy of conventional and digital radiographic methods in determining root canal working length. MATERIAL AND METHODS: Twenty-five maxillary incisor or canine teeth from 22 patients were used in this study. Considering the preoperative radiographs as the baseline, a 25 K file was inserted into the root canal to the point where the Root ZX electronic apex locator indicated the APEX measurement in the screen. From this measurement, 1 mm was subtracted for positioning the file. The radiographic measurements were made using a digital sensor (Digora 1.51) or conventional type-E films, size 2, following the paralleling technique, to determine the distance of the file tip and the radiographic apex. RESULTS: The Student "t" test indicated mean distances of 1.11 mm to conventional and 1.20 mm for the digital method and indicated a significant statistical difference (p<0.05). CONCLUSIONS: The conventional radiographic method was found to be superior to the digital one in determining the working length of the root canal.

OBJECTIVE: This study used dye leakage assay and scanning electron microscopy to evaluate, respectively, the sealing ability and marginal adaptation of three root-end filling materials used as apical plugs, as well as the possible correlation between these properties. MATERIAL AND METHODS: Ninety-eight single-rooted human teeth were prepared to simulate an open apex. The teeth were allocated to three experimental groups (n = 30), which received a 5-mm thick apical plug of (1) gray MTA AngelusTM, (2) CPM TM and (3) MBPc, and two controls groups (n = 4). After immersion in 0.2% Rhodamine B solution for 48 h, the teeth were sectioned longitudinally and analyzed by Image Tool 3.0 software. The marginal adaptation between apical plugs and the root canal walls were analyzed by SEM. RESULTS: MBPc had significantly less (p<0.05) apical leakage than the other materials. Regarding marginal adaptation, CPM TM showed the best numerical results, though without statistical significance from the other materials (p<0.05). There was no correlation between the two properties. CONCLUSIONS: When used as apical plugs, the tested root-end filling materials had similar marginal adaptation to the dentin walls, but MBPc had the best sealing ability, as demonstrated by the least apical leakage from all tested materials.

This study evaluated the sealing ability of apical plugs fabricated with gray MTA AngelusTM sealer, CPM TM sealer and MBPc sealer. The root canals of 98 extracted single-rooted human teeth were instrumented with #5 to #1 Gates Glidden drills according to the crown-down technique until the #1 drill could pass through the apical foramen. The specimens were then prepared with K-files, starting with an ISO 50 until an ISO 90 could be visualized 1 mm beyond the apex. After root canal preparation, the external surface of each root was rendered impermeable and roots were assigned to 3 experimental groups (n = 30), which received a 5-mm thick apical plug of gray MTA AngelusTM, CPM TM and MBPc, and two control groups (n=4). The remaining portion of the canal in the experimental groups was filled by the lateral condensation technique. The teeth of each group, properly identified, were fixed on utility wax by their crowns and were placed in plastic flasks, leaving the apex free and facing upward. The flasks were filled with 0.2% Rhodamine B solution, pH 7.0, so as to completely cover the root apex of all teeth. The sealing ability was analyzed by measuring 0.2% Rhodamine B leakage after all groups had been maintained in this solution for 48 hours. Data were analyzed statistically by Kruskal-Wallis test and Dunn test with a=5%. The results showed that, among the tested materials used for fabrication of apical plugs, MBPc sealer had the least amount of leakage with statistically significant difference (p<0.05).

This study evaluated the sealing ability of apical plugs made of white and gray MTA-Angelus® and white Portland cement placed via the root canal and having different thicknesses (2, 5 and 7 mm). Ninety extracted human single-rooted teeth were instrumented using a size 40 K-file to standardize the foraminal opening by the stepback technique. The teeth were assigned to 3 groups (n=30), according to the material used for fabrication of the apical plugs: A = gray MTA; B = white MTA; C = white Portland cement. The groups were subdivided into groups of 10 teeth each according to the apical plug thickness (2, 5 and 7 mm). Marginal apical dye leakage was assessed using 0.2% Rhodamine B solution in which the specimens were immersed for 72 hours at 37ºC. The roots were sectioned longitudinally in a buccolingual direction for apical plug exposure, and digital photographs were taken and analyzed by Image Tool image-analysis software. Data were analyzed statistically by Kruskal-Wallis and Dunn's tests. Significance level was set at 5%. The least percent leakage was observed for 5- and 7-mm-thick plugs (p<0.05). No significant difference (p>0.05) was found between gray MTA and white Portland cement. Among the three materials analyzed, white MTA presented the highest marginal leakage (p<0.05). The findings of the present study showed that gray MTA and Portland cement had better sealing ability than white MTA when used as apical plugs. Dye leakage was smaller for 5- and 7-mm-thick plugs compared to 2-mm-thick plugs.