Nanostructured zinc oxide (ZnO) prepared by combustion in solution was used to obtain nanocomposites. The ZnO particles were characterized by Brunauer-Emmett-Teller (BET), X-ray diffraction (XRD), and scanning electron microscopy (SEM), showing crystallite size of 32 nm and a superficial area of 32.6 m2 g-1. Nanocomposites with 1, 3, and 5 wt.% of ZnO in the polymeric matrix were obtained using the in situ polymerization of ethylene with catalytic activities between 1500-1700 kg (molZr h PE)-1. The high-density polyethylene nanocomposites (PEZnO) were characterized by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), SEM, and transmission electron microscopy (TEM). The nanocomposites with 1 wt.% ZnO gave excellent mechanical properties, and all were active against Gram-positive (Staphylococcus aureus) and Gram-negative (Escherichia coli) bacteria.

This work aimed to produce graphene oxide with few graphene layers, a low number of defects, good conductivity and reasonable amount of oxygen, adequate for use as filler in polymeric composites. Two starting materials were evaluated: expanded graphite and graphite flakes. The method of oxidation used was the Staudenmaier one, which was tested over different lengths of time. No appreciable differences were found among the oxidation times and so the lowest oxidation time (24 h) was chosen as the most adequate. An investigation was also conducted into suitable temperatures for the reduction of graphite oxide. A temperature of 1000 ºC gave the best results, allowing a good quality material with few defects to be obtained. The reduction was also evaluated under inert and normal atmosphere. The best results were obtained when the least modified material, e. g., graphite flakes, was used as a starting material, oxidized for 24h and reduced at 1000 ºC for 30 s in a quartz ampoule under a normal atmosphere.