Bacterial cellulose produced from Gluconacetobacter xilinus was used to produce cellulose nanocrystals by sulfuric acid hydrolysis. Hydrolysis was performed with 64% sulfuric acid at 50 ºC with the hydrolysis time ranging between 5 and 90 min. The production of nanocrystals was observed to have size distributions that were dependent on hydrolysis times up to 10 min, after which time the suspensions showed distributions closer in size. Results from thermal analysis and X-ray diffraction showed that the amorphous cellulose was removed, leaving only the crystalline portion. Self-supported films were formed from the suspension of nanocrystals and had iridescence characteristics. The films were characterized by microscopy measures and specular reflectance.

Multicomponent ( Al2O3, CaO, SiO2, MgO) calcium aluminate-based glasses containing Nd3+ were prepared in order to evaluate their possibilities as laser host materials. The refractive index, UV-visible-near IR absorption spectrum, IR and visible luminescence spectra, and fluorescence decay time were measured. Judd-Ofelt model was used to obtain experimental intensity parameters ( omega2, omega4 and omega6), emission cross-section, radiative lifetimes, emission branching ratios and quantum efficiency.

Domestic microwave oven was modified for laboratory applications. Electronic system was made for controlling magnetron irradiation time. Exhaustion and air circulation systems were installed to clean the internal oven atmosphere during operation. The cavity walls were coated with aluminized thermal paint to avoid chemical corrosion. These modifications allowed the usage of the oven for drying and processes using reflux.