The presence of acicular ferrite (AF) in the microstructure of weld bead, in a specified range of values, increase considerably the toughness of welded joints. The present paper, for that reason, study the relationship between the acicular ferrite quantity in the deposited metal and the oxygen present in the active gas mixture of CO2+O2, during the execution of butt welded joints with straight edges, in low carbon steels with consumable electrode and gas protection (GMAW) in invariable conditions of process parameters (welding current, arc voltage, welding speed, electrode extension, and gas flow). The graphic relation between the acicular ferrite and the oxygen content was established, as result of the research work.

La presencia de ferrita acicular (FA) en la microestructura del cordón de soldadura, dentro de determinado rango de valores, eleva considerablemente la tenacidad de las uniones soldadas. Es por ello, que el presente trabajo trata sobre un estudio que relaciona la cantidad de ferrita acicular en el cordón en función del contenido de oxígeno presente en la mezcla activa CO2+O2, durante la realización de uniones soldadas de bordes rectos en aceros de bajo carbono con el proceso con electrodo fusible y protección gaseosa (GMAW) en condiciones invariables de parámetros de proceso (corriente de soldadura, voltaje de arco, velocidad de soldadura, longitud libre y flujo de gas protector). Como resultado del trabajo se estableció la relación gráfica existente entre la ferrita acicular y el contenido de oxígeno en la mezcla.

En el presente trabajo se desarrolló un modelo de elementos finitos para simular la unión a tope, con electrodo E 7018 de 3,2 mm de diámetro, de dos placas de acero con bajo contenido de carbono y baja aleación. Adicionalmente, se estudia la influencia sobre la distribución de temperaturas en la placa al considerar la termo-dependencia de diferentes propiedades físicas del acero (conductividad térmica y calor específico).

A finite element model was developed to simulate the butt joint, with a 3.2 mm diameter electrode E 7018, of two plates of low carbon and low alloy steel. Also, the influence on the temperature distribution was studied considering temperature-dependent physical properties (thermal conductivity and specific heat).

En este trabajo se presenta una metodología de modelación de la evolución de la historia térmica, tensiones y deformaciones producidas por el proceso de soldadura, mediante el software de elementos finitos de uso general ANSYS Multiphysics versión 9.0. Dicha metodología integra una información que se encuentra dispersa en la literatura, proponiendo variantes que en ocasiones superan lo publicado en trabajos precedentes. La metodología es aplicada exitosamente en la modelación tridimensional de una soldadura GMAW automática sobre chapas de aleación de aluminio al magnesio 5083-O, de amplio empleo en la industria moderna, validándose los resultados que brinda el modelo contra datos experimentales publicados. El estudio permitió establecer que las mejores respuestas, para este tipo de aleación, se obtienen empleando una temperatura de corte igual a la temperatura de sólido del metal, utilizando los modelos de material bilineal sin endurecimiento, o con endurecimiento cinemático, y activando los elementos de la soldadura en el instante en que sobre ellos se encuentra la fuente de calor en ambas corridas térmica y mecánica

A modeling methodology of the evolution of thermal history, stresses and strains due to the welding process, using the general purpose finite elements software ANSYS Multiphysics release 9.0, is exposed. This methodology integrates existing information and new variants that, in occasions, provide better results than those previously published results. This methodology was applied to the three-dimensional modeling of automatic GMAW on 5083-O aluminum - magnesium alloy plates, which are frequently employed in the modern industry. Model results were validated against published experimental dates. The study allowed to define that for this alloy type the best results are obtain using a cut-off temperature similar to the metal solid temperature, employing the bilinear material models without hardening or using kinematics hardening, and activating welding elements when thermal source is right over them, during both thermal and mechanic races

The thermal behavior during in service repair welding of oil transportation pipes was studied by finite element analysis in the present paper. Regression equations that relate peak temperature at the inner surface of the pipe and cooling time between 800 and 500ºC in the heat affected zone to the welding heat input, preheat temperature, and convection heat transfer coefficient were obtained. The former parameters govern, respectively, the possibility of burn through and cold cracking, and the latter parameters define the thermal behavior during welding. The existence of conditions that simultaneously satisfy the obtained equations, for different combinations of related variables, was proved. Graphical representations of relevant practical importance that were developed from the solution of obtained equations are presented.

En el presente artículo, empleando el análisis por elementos finitos, se estudió el comportamiento térmico durante la soldadura de reparación, en condiciones de servicio, de un tubo que transporta petróleo. Se obtuvieron ecuaciones de regresión que relacionan a la temperatura máxima en la superficie interna del tubo y al tiempo de enfriamiento desde 800 ºC hasta 500 ºC de un punto situado en la zona afectada por el calor (ZAC), parámetros que gobiernan la ocurrencia de perforaciones en la pared del tubo y agrietamiento en frío respectivamente, con el calor de entrada de la soldadura, la temperatura de precalentamiento y el coeficiente de transferencia de calor por convección, variables que definen el comportamiento térmico durante la ejecución del proceso de soldadura. Se probó la existencia de una zona en que se satisfacen simultáneamente las ecuaciones obtenidas, para diferentes combinaciones de las variables relacionadas. Se presentaron nomogramas con un importante valor práctico, desarrollados a partir de la solución de las ecuaciones obtenidas.