Ternary Ni-W-P films were produced by electroless deposition using baths with different tungsten concentrations. After deposition, the coated surfaces were annealed at 400°C for 1h. Surface morphology and film composition in the as-plated condition were assessed by SEM and EDS analyses, respectively. The crystalline phases after annealing were investigated by X-ray diffraction (XRD). Nanoindentation tests were performed to assess the mechanical properties of the deposited films. Surface roughness was determined by confocal laser scanning microscopy (CLSM). Friction coefficient was evaluated by reciprocating were tests in a nanotribometer. The corrosion behavior was evaluated by potentiodynamic polarization curves. The results showed that the surface morphology, crystallization behavior and corrosion resistance were affected by the tungsten content in the film. The best corrosion performance was obtained for the ternary films after annealing. Hardness, surface roughness and friction coefficient were dependent of the tungsten concentration in the film.

The aim of the present work was to study the passive film stability and pitting corrosion behavior of the AISI 409 stainless steel. The electrochemical tests were carried out in 0.1 M NaCl solution at room temperature. The general electrochemical behavior was assessed using electrochemical impedance spectroscopy (EIS) measurements whereas the semiconducting properties of the passive film were evaluated by the Mott-Schottky approach. Pitting corrosion was investigated using potentiodynamic and potentiostatic polarization tests. Surface morphology was examined using confocal laser scanning microscopy and scanning electron microscopy (SEM). Energy dispersive X-ray spectroscopy (EDS) analyses were carried out to identify the composition of precipitates that could act as preferential sites for the onset of pitting corrosion. The results showed that the passive film presents n-type semiconductive behavior. Grain boundaries played an important role as pitting initiation sites for the AISI 409 stainless steel.

This study reports the high temperature erosion-oxidation (E-O) behavior of conventional and nanostructured Cr3C2-25(Ni-20Cr) coatings prepared by high velocity oxygen fuel (HVOF) spraying. As-received and nanostructured Cr3C2-25(Ni-20Cr) powders with mean crystallite sizes of 145 nm and 50 nm respectively, were used to prepare 120 - 200 µm thick coatings on AISI 310 samples. The E-O behavior of the coatings prepared with the as-received (AR) and nanostructured (NS) powders was determined as weight change in a custom designed rig at room temperature, 450, 700 and 800 ºC. The Vickers microhardness, Young's Modulus and fracture toughness of the AR and NS coatings were determined, and the NS coatings exhibited higher values compared with the AR coatings. The E-O resistance of the NS coating was higher than that of AR coating at all temperatures, and particularly at 800 ºC. The increase in E-O resistance of the NS coatings is due to its superior mechanical properties as well as to the presence of some heterogeneities in the AR coatings. The E-O mechanisms of both types of the coatings are discussed, with special attention to that at high temperatures. The results suggest that at 800 ºC the E-O process is controlled by erosion of the oxide.