The influence of the structural and microstructural characteristics of graphitic precursors on the production of graphite oxide (GO) is investigated in the present work. Six different graphitic precursors were used to produce GO following a modified Hummers method, namely: natural graphite, commercial lubricant graphite, milled graphite, graphite flakes, high-purity graphite and graphite recycled from Li-ion batteries. The products were characterized by X-ray diffraction (XRD), thermogravimetry, solid-state 13C nuclear magnetic resonance (NMR) and scanning electron microscopy (SEM). 13C NMR spectra revealed the presence of epoxy, hydroxyl, carbonyl and lactol groups in the synthesized GOs. However, the oxidation degree of each product was found to be dependent on the average crystallite size (Lc) and particle size of the graphitic precursors, with the best GO samples being produced from the milled graphite and the graphite recycled from ion-Li batteries. These results were rationalized in terms of the structural and microstructural differences among the graphitic precursors, as revealed by the XRD patterns and SEM images, evidencing the importance of the correct choice of the precursor aiming the achievement of a well-developed structure for the GO product.

This work consists in a study about the chemical activation of charred rice hulls using NaOH as the activation agent. The influence of the naturally-occurring silica was particularly evidenced. X-ray diffraction patterns showed the formation of sodium carbonate and silicates in the activated samples, whereas thermogravimetric curves revealed a strong reduction in the ash content of these samples after washing with water. Nitrogen adsorption data indicated a microporosity development only in the washed samples, with BET surface area values of 450 and 1380 m²/g achieved for the samples activated at 800 °C starting from the precursor with or without silica, respectively.