ABSTRACT Due to the environmental problem related to the deposition of residues from the production of mineral coal in Brazil, the objective of this study was to use the residue of mineral coal in the production of mortar as a mineral addition and also as a substitute for Portland cement. For analysis of the physical-mechanical properties of mortars, 5x10 cm specimens were used. Starting from a mortar trace without addition of residue, called reference, to later be used the contents of 10 and 15% for addition, and 20 and 30% for substitution of Portland cement with mineral coal residue. The mortar samples underwent a curing process in a humid chamber and, at 28 days, density tests in the hardened state, water absorption by capillarity, compressive strength and X-ray diffractometry were performed. The results obtained indicated that the mineral coal waste increased the water absorption of mortar by 67% and 100% for the addition of 10 and 15% of coal, respectively. To replace 20 and 30%, the increases in absorption were 133% and 33%, respectively. The mechanical resistance, on the other hand, showed a reduction, for addition of 10 and 15%, of 33% and 42%, respectively. For the replacement of cement by 20 and 30%, a reduction in strength of 35% and 47% was observed.

RESUMO Devido à problemática ambiental relacionada à deposição de resíduos provenientes da produção de carvão mineral no Brasil, o objetivo deste estudo foi utilizar o resíduo do carvão mineral na produção de argamassas como adição mineral e também como substituição ao cimento Portland. Para análise das propriedades físico-mecânicas das argamassas foram utilizados corpos de prova de 5x10 cm. Partindo de um traço de argamassa sem adição de resíduo, denominado referência, para posteriormente serem utilizados os teores de 10 e 15% para adição, e de 20 e 30% para substituição de cimento Portland por resíduo de carvão mineral. As amostras de argamassa passaram por um processo de cura em câmara úmida e, aos 28 dias, foram realizados os ensaios de densidade no estado endurecido, absorção de água por capilaridade, resistência à compressão e difratometria de raios X. Os resultados obtidos indicaram que o resíduo de carvão mineral aumentou a absorção de água das argamassas em 67% e 100% para adição de 10 e 15% de carvão, respectivamente. Para substituição de 20% o aumento na absorção foi de 150%; com substituição de 30% a absorção de água foi considerada estatisticamente igual ao traço referência. Já a resistência mecânica apresentou redução, para adição de 10 e 15%, de 33% e 42%, respectivamente. Para a substituição de cimento em 20 e 30%, foi observada redução de resistência de 35% e 47%.

RESUMO As falhas de dosagem e execução de pisos de concreto, constantemente levam ao surgimento de manifestações patológicas. Sendo assim, é indispensável o conhecimento dos fatores que influenciam o comportamento do concreto ou alteram suas características, bem como a utilização de mão de obra de qualidade. Em vista disso, este estudo avaliou a influência da adição de microfibras de polipropileno nos teores de 0 g/m3, 600 g/m3 e 900 g/m3 e de diferentes condições de cura (sem cura, cura úmida e cura úmida após três dias de exposição ao ambiente) nos concretos empregados em pisos. Para tanto, foram realizados ensaios de exsudação, resistência à compressão uniaxial e dureza superficial por esclerometria. Os resultados indicam que a utilização das microfibras influenciou de forma significativa a exsudação e a resistência à compressão, ainda que a dureza superficial não tenha sido afetada diretamente por este material e nem pelo tipo de cura. De maneira geral, pode-se dizer que dentre os teores de microfibras de polipropileno avaliados, o teor de 600 g/m3 é o mais indicado para adição no concreto, apresentando melhor desempenho naspropriedades analisadas. É possível afirmar ainda que a cura, apesar de não ter causado influência significativa na superfície do concreto, é um fator de extrema importância para suas propriedades de massa.

ABSTRACT Failures of dosing and execution of concrete floors, constantly lead to the emergence of pathological manifestations. Therefore, it is indispensable to know the factors that influence the behavior of the concrete or alter its characteristics, as well as the use of quality manpower. This study evaluated the influence of the addition of polypropylene microfibers in the contents of 0 g/m3, 600 g/m3 and 900 g/m3 and of different curing conditions (without cure, wet cure and wet cure after three days of exposure) in concrete used in floors. For that, tests of bleeding, compressive strength and surface hardness by rebound hammer were per-formed. The results indicate that the use of microfibers significantly influenced the bleeding and the compressive strength, although the surface hardness was not affected directly by this material nor by the type of cure. In general, it can be said that of the polypropylene microfiber contents evaluated, the 600 g/m3 content is the most suitable for addition in the concrete, presenting better performance in the analyzed properties. It is possible to affirm still that the cure, although not having caused significant influence on the surface of the concrete, is a factor of extreme importance for its mass properties.

RESUMO Descolamentos e fissuras são manifestações patológicas recorrentes em revestimentos de fachadas de edificações brasileiras. Neste contexto, sabe-se que o revestimento de argamassa ainda é o mais utilizado no mercado da construção civil e tem demonstrado diversos problemas decorrentes dos materiais e da execução de maneira inadequada. Portanto, o presente trabalho buscou avaliar a influência do uso de diferentes telas como reforço de revestimento argamassado, com o objetivo de identificar qual apresenta o melhor desempenho. Foram utilizados três modelos de telas, dois metálicos galvanizados de diferentes malhas e espessuras e um modelo de polietileno de alta densidade (PEAD). A fim de caracterizar a tela isoladamente quanto à resistência à tração, foi realizado o ensaio de tração simples em corpos de prova de 250x300 mm para cada modelo de tela. Para avaliar seu comportamento em conjunto com a argamassa, foi realizado o ensaio de tração na flexão de 4 pontos em corpos de prova prismáticos de 200x500 mm, no qual foram inseridas amostras das telas nas posições de 15, 25 e 30 mm da base para um corpo de prova com espessura de 50 mm. Os resultados obtidos indicam que a tela metálica eletrosoldada galvanizada, de malha quadrada 25x25 mm e fio de 1,24 mm, apresentou o melhor desempenho dentre os modelos testados.

ABSTRACT Displacement and fissures are recurrent pathological manifestations in the facade coating of brazilian buildings. In this context, it is known that mortar coating is still the most used in the civil construction market and has demonstrated several problems due to inappropriate employment and execution. Therefore, the present work aimed to evaluate the influence of different meshes as reinforcement for mortar coating, in order to identify which one present the best performance. It was used three mesh models, two made of galvanized metal with different meshes and thicknesses and one made of high-density polyethylene. In order to isolated characterize the meshes for tensile strength, it was performed the tensile assay in specimens of 250x300 mm for each mesh models. To evaluate the influence of the different meshes in conjunction with the mortar, the tensile test in bending at 4 points in specimens of 200x500 mm was carried out, where the meshes were inserted at 15, 25 and 30 mm from the bottom of the specimen with 50 mm thickness. The data indicate that the square 25x25 mm and 1.24 mm wire galvanized metal mesh presented the best performance among the tested models.