A series of activated carbons (AC) were prepared from waste of the olive oil production in the Cuyo Region, Argentine by two standard methods: a) physical activation by steam and b) chemical activation with ZnCl2. The AC samples were characterized by nitrogen adsorption at 77 K and evaluated for natural gas storage purposes through the adsorption of methane at high pressures. The activated carbons showed micropore volumes up to 0.50 cm³.g-1 and total pore volumes as high as 0.9 cm³.g-1. The BET surface areas reached, in some cases, more than 1000 m².g-1. The methane adsorption -measured in the range of 1-35 bar- attained values up to 59 V CH4/V AC and total uptakes of more than 120 cm³.g-1 (STP). These preliminary results suggest that Cuyo's olive oil waste is appropriate for obtaining activated carbons for the storage of natural gas.

Ferric chloride as a new activating agent was used to obtain activated carbons from agroindustrial waste. This material was prepared at three temperatures of pyrolysis, 200, 280 and 400 ºC. The carbonaceous materials obtained after the activation processes showed high specific surface areas (BET), with values higher than 900 m² g-1. The materials showed different behaviors in the adsorption of methylene blue dye and reactive red textile dye in water solutions. An important fact in the use of FeCl3 as an activating agent is that the activation temperature is at 280 ºC, well below of those commonly employed in chemical or physical activations described in the literature.