Abstract The aim of this study was to evaluate the thickness of resin cements in the root thirds when using conventional fiberglass posts (CP) and relined fiberglass posts (RP) in weakened roots and to evaluate the morphological characteristics of the dentin-resin interface. Forty human maxillary anterior teeth had the crown sectioned below the cemento-enamel junction. The canals were endodontically treated and weakened with diamond burs. Teeth were divided into four groups (n = 10): Group 1 – CP + RelyX ARC; Group 2 – CP + RelyX U200; Group 3 – RP + RelyX ARC; and Group 4 – RP + RelyX U200. Prior to luting, 0.1% Fluorescein and 0.1% Rhodamine B dyes were added to an adhesive and resin cement, respectively. Slices were obtained from the apical, middle, and cervical thirds of the root. Confocal laser scanning microscopy images were recorded in four areas (buccal, lingual, mesial, distal) of each third. In each area, four equidistant measures of the resin cement were made and the mean value was calculated. The interface morphology was observed. The data were submitted to three-way ANOVA and Tukey’s test (α = 0.05). The interaction between fiberglass posts, resin cement, and root thirds was significant (p < 0.0001). The resin cement thicknesses were significantly lower for RP in comparison with CP, except in the apical third. There was no significant difference between the resin cements for RP. There was formation of resin cement tags and adhesive tags along the root for RP. RP favored the formation of thin and uniform resin cement films and resin tags in weakened roots.

OBJECTIVES: CO2, Er:YAG and Nd:YAG lasers have been used in endodontic surgery. This in vitro study evaluated 1% Rhodamine B dye penetration using computer-assisted morphometry (ImageTool Software®) of 108 endodontically treated human permanent canines. MATERIAL AND METHODS: Teeth were divided into 9 groups according to the technique used: A: 90-degree apicoectomy with bur, root-end cavity preparation with ultrasound and filled with MTA; B: 90-degree apicoectomy with bur, root-end cavity prepared with ultrasound and filled with MTA, and treatment of apical surface with CO2 laser (1 W, CW/CW); C: 90-degree apicoectomy with bur, and treatment of apical surface with Nd:YAG laser (150 mJ, 10 Hz); D: 90-degree apicoectomy with bur, and treatment of apical surface with CO2 laser,(1 W, CW/CW); E: apicoectomy with Er:YAG laser (400 mJ, 10 Hz), root-end cavity prepared with ultrasound and filled with MTA; F: apicoectomy with Er:YAG laser (400 mJ, 10 Hz) and treatment of apical surface with Nd:YAG laser (150 mJ, 10Hz); G: apicoectomy with CO2 laser (5W, CW/SP), root-end cavity prepared with ultrasound and filled with MTA; H: irradiation of apical end with CO2 laser (1 W, CW/CW); I: irradiation of apical end with Nd:YAG laser (150 mJ, 10 Hz). RESULTS: Dye penetration was found in all specimens at different rates, the lowest penetration occurring in groups C (16.20%), B (17.24%) and F (17.84%). CONCLUSIONS: Groups B, C and F represent the best technical sequences to perform endodontic surgery.