Use of glass waste in the production of metakaolin-based geopolymer submitted to room temperature and thermal curing

Utilização de resíduo de vidro na produção de geopolímero de base metacaulim submetido a cura ambiente e em estufa

Abstract

Metakaolinis the principal raw material utilized in the synthesis of geopolymers, although its ratio of silica and alumina contents is not ideal. Normally, the SiO₂ content is adjusted with the use of silicates present in the activating solution. An eco-efficient alternative would be the use of glass waste as an additional source of silica.This work evaluates the efficiency of the alkaline activation of metakaolin, using potassium hydroxide and silicate, with and without the substitution of 12.5% of metakaolin by microparticles of glass. The efficiency of the alkaline activation was evaluated by X ray diffractometry, spectroscopy in the infrared region with the Fourier transform, nuclear magnetic resonance spectroscopy of ²⁷Al and ²⁹Si, specific mass and compressive strength. The results indicate the occurrence of geopolymerization with and without the use of glass waste. It was observed that the substitution of 12.5% favors the mechanical performance of the compounds at 28 days, with increases by 37% and 47% in the mechanical strength of the material with thermal curing and ambient temperature curing, respectively.

Keywords:
Metakaolin; Glass waste; Potassium hydroxide; Alkaline activation; Geopolymerization