Abstract
This study aimed to evaluate the influence of calcium silicate-based sealers on the bond strength of fiber posts using conventional and self-adhesive resin cement. Sixty single-rooted teeth were selected. The canals were prepared with a reciprocating instrument 40.06. The roots were randomly distributed in six groups (n = 10) according to the strategies for root canal filling and fiber posts cementation: AH Plus/RelyX ARC; AH Plus/RelyX U200; Bio C Sealer/RelyX ARC; Bio C Sealer/RealyX U200; Sealer Plus BC/RelyX ARC; and Sealer Plus BC/RelyX U200. The roots were transversally sectioned, and one slice per post-third was obtained. The push-out test was performed at a crosshead speed of 1mm/min. The failure patterns were described after assessment with a stereomicroscope with a 10× magnification. Bond strength was calculated and analyzed using the ANOVA and Tukey test. AH Plus did not influence the bond strength of fiber posts cemented with conventional (RelyX ARC) or with self-adhesive resin cement (RelyX U200). The lowest bond strength values were obtained when calcium silicate-based sealers were associated with conventional resin cement (Bio C Sealer/RelyX ARC and Sealer Plus BC/RelyX ARC). Except for Sealer Plus BC/RelyX ARC, all groups presented lower bond strength at the apical portion compared to the cervical portion of the post. Adhesive failures between cement and post and cement and dentin were predominant (55.3%). Calcium silicate-based sealers decreased the bond strength of fiber posts cemented with conventional resin cement.
Key Words:
Bioceramic; calcium silicate-based sealer; fiber post; push-out bond strength; resin cement
Thumbnail