The ability of a pool of bovine bone morphogenetic proteins bound to synthetic microgranular hydroxyapatite (BMPb-HA) to stimulate bone repair was determined in rat critical size defects. An 8-mm diameter defect was created in the calvaria of 25 rats. In 15 rats, the defects were filled with BMPb-HA homogenized with blood (experimental group), and in 10 rats the defects were filled only with blood clots (control). The calvariae of experimental rats were collected 1, 3 and 6 months after surgery and of the control rats at the end of surgery and 6 months thereafter. The morphometric results obtained in the radiographs showed an absence of new bone formation at 1 and 3 months post-surgery and, histologically, the defects were filled with fibrous connective tissue and numerous foci of a foreign body-type granulomatous reaction around hydroxyapatite agglomerates. At the end of 6 months, the number and size of the granulomatous foci decreased and the area of the defects was reduced by 22% compared to the 0-hour control due to the formation of new bone at their borders, although the mean area was similar to the 6-month control. We conclude that the use of BMPb-HA in the treatment of critical size bone defects of the rat skull leads to the formation of a foreign body-type granulomatous reaction that markedly inhibits new bone formation, suggesting that synthetic microgranular hydroxyapatite does not represent a good carrier for BMP-induced bone formation.
bovine BMP; hydroxyapatite; bone repair; critical size; skull