Influence of the diameter of ground date pits on the technological properties of clay bricks

Djafri, G.; Chelouah, N.

doi:10.1590/0366-69132018643722483

G. Djafri

University of Bejaia, Faculty of Technology, Laboratory of Construction Engineering and Architecture, 0600 Bejaia, Algeria

N. Chelouah ^* * nasser_chelouah@yahoo.fr

University of Bejaia, Faculty of Technology, Laboratory of Construction Engineering and Architecture, 0600 Bejaia, Algeria

* nasser_chelouah@yahoo.fr

Thumbnail

Figure 1
X-ray diffraction pattern of the clay.

Figura 1
Difratograma de raios X da argila.

Thumbnail

Figure 2
TGA and DTA curves of GDP.

Figura 2
Curvas de TGA e DTA de CTM.

Thumbnail

Figure 3
TGA curves of the sample containing 5 wt% of GDP compared with the control sample.

Figura 3
Curvas de TGA de amostra contendo 5% em massa de CTM em comparação com a amostra de controle.

Thumbnail

Figure 4
SEM micrograph of GDP (ground date pits).

Figura 4
Micrografia de MEV de CTM (caroço de tâmara moído).

Thumbnail

Figure 5
Shrinkage as a function of diameter and content of GDP of unfired (a) and fired (b) samples.

Figura 5
Retração em função do diâmetro e fração de CTM de amostras antes (a) e depois (b) da queima.

Thumbnail

Figure 6
SEM micrographs of fired clay bricks with different diameter of GDP: a) 0-0.20 mm; b) 0.20-0.25 mm; c) 0.25-0.50 mm; and d) 0.50-1.0 mm.

Figura 6
Micrografias de MEV de tijolos após queima com diferentes diâmetros de CTM: a) 0-0.20 mm; b) 0.20-0.25 mm; c) 0.25-0.50 mm; e d) 0.50-1.0 mm.

Thumbnail

Figure 7
Compressive strength as a function of diameter and content of GDP of unfired (a) and fired (b) samples.

Figura 7
Resistência à compressão em função do diâmetro e fração de CTM de amostras antes (a) e depois (b) da queima.

Thumbnail

Figure 8
Compressive strength as a function of diameter and content of GDP of unfired (a) and fired (b) samples.

Figura 8
Resistência à flexão em função do diâmetro e fração de CTM de amostras após queima.

Thumbnail

Figure 9
Thermal conductivity as a function of diameter and content of GDP of fired samples.

Figura 9
Condutividade térmica em função do diâmetro e fração de CTM de amostras após queima.

Thumbnail

Figure 10
Pore size distribution curves of clay containing 5 to 20 wt% of ground date pits (GDP) with diameter of 0.5-1 mm.

Figura 10
Curvas de distribuição de tamanho de poros de argila contendo 5 a 20% em massa de caroços de tâmara moídos (CTM) com diâmetro de 0,5-1 mm.

Thumbnail

Table I
Chemical composition of the clay (wt%).

Tabela I
Composição química da argila (% em massa).

Thumbnail

Table II
Mineral composition of the clay (wt%).

Tabela II
Composição mineral da argila (% em massa).

Thumbnail

Table III
Chemical composition of ground date pits - GDP (wt%).

Tabela III
Composição química dos caroços de tâmara moídos - CTM (% em massa).

Thumbnail

Table IV
Water content for plasticity (%) of clay-GDP mixtures as a function of diameter and content of the GDP.

Tabela IV
Teor de água para plasticidade (%) das misturas argila-CTM em função do diâmetro e fração de CTM.

Thumbnail

Table V
Water absorption coefficient - C (%) as a function of diameter and content of GDP of fired samples, according to NA 1957 standard.

Tabela V
Coeficiente de absorção de água - C (%) em função do diâmetro e fração de CTM de amostras após queima, de acordo com norma NA 1957.

Thumbnail

Table VI
Water absorption (%) as a function of diameter and content of GDP of fired samples.

Tabela VI
Absorção de água (%) em função do diâmetro e fração de CTM de amostras após queima.

Thumbnail

Table VII
Apparent density (g/cm3) as a function of diameter and content of GDP of fired samples.

Tabela VII
Densidade aparente (g/cm3) em função do diâmetro e fração de CTM de amostras após queima.

Thumbnail

Table VIII
Apparent porosity (%) as a function of diameter and content of GDP of fired samples.

Tabela VIII
Porosidade aparente (%) em função do diâmetro e fração de CTM de amostras após queima.

Thumbnail

(A)

Table I Chemical composition of the clay (wt%).

SiO₂	Al₂O₃	CaO	Fe₂O₃	MgO	K₂O	Na₂O	SO₃	TiO₂	P₂O₅	LOI
43.30	13.35	15.34	5.01	1.89	2.03	1.06	0.71	0.63	0.19	16.50

Table II Mineral composition of the clay (wt%).

Quartz	Calcite	Muscovite	Kaolinite	Albite	Gypsum	Dolomite	Palygorskite	Clinochlore	Ferruginous minerals
22	26	17	10	6	2	3	5	4	5

Table III Chemical composition of ground date pits - GDP (wt%).

Moisture	Carbohydrate	Protein	Lipid	Cellulose	Ash
6.46	50.50	7.22	9.51	16.20	10.20

Table IV Water content for plasticity (%) of clay-GDP mixtures as a function of diameter and content of the GDP.

GDP	0-0.20 mm	0.20-0.25 mm	0.25-0.50 mm	0.50-1.0 mm
5%	22.96±0.19	23.18±0.19	23.97±0.20	25.05±0.22
10%	24.86±0.20	25.32±0.20	26.38±0.21	28.29±0.20
15%	27.73±0.20	28.97±0.20	29.91±0.20	32.29±0.20
20%	33.45±0.21	34.52±0.22	35.56±0.22	37.29±0.22

Table V Water absorption coefficient - C (%) as a function of diameter and content of GDP of fired samples, according to NA 1957 standard.

GDP	0-0.20 mm	0.20-0.25 mm	0.25-0.50 mm	0.50-1.0 mm
5%	16.25±0.21	18.22±0.21	19.48±0.19	20.98±0.20
10%	20.45±0.19	21.21±0.24	22.23±0.21	23.65±0.21
15%	25.98±0.20	25.79±0.24	26.50 ± 0.21	27.10±0.20
20%	27.98±0.22	28.97±0.19	29.89±0.20	30.39±0.19

Table VI Water absorption (%) as a function of diameter and content of GDP of fired samples.

GDP	0-0.20 mm	0.20-0.25 mm	0.25-0.50 mm	0.50-1.0 mm
5%	17.86±0.22	18.68±0.22	20.02±0.21	23.87±0.22
10%	22.20±0.20	24.05±0.21	24.84±0.21	26.59±0.21
15%	24.93±0.21	26.27±0.21	27.11±0.22	28.55±0.22
20%	26.97±0.23	28.80±0.23	30.55±0.21	31.38±0.20

Table VII Apparent density (g/cm3) as a function of diameter and content of GDP of fired samples.

GDP	0-0.20 mm	0.20-0.25 mm	0.25-0.50 mm	0.50-1.0 mm
5%	1.68±0.03	1.66±0.04	1.58±0.03	1.46±0.04
10%	1.43±0.04	1.39±0.03	1.37±0.03	1.33±0.03
15%	1.32±0.03	1.30±0.03	1.28±0.03	1.25±0.03
20%	1.27±0.04	1.24±0.03	1.23±0.03	1.20±0.03

Table VIII Apparent porosity (%) as a function of diameter and content of GDP of fired samples.

GDP	0-0.20 mm	0.20-0.25 mm	0.25-0.50 mm	0.50-1.0 mm
5%	30.00±0.22	31.00±0.22	31.63±0.25	34.85±0.24
10%	31.74±0.23	33.33±0.25	34.03±0.26	35.36±0.21
15%	32.90±0.28	34.15±0.26	34.70±0.26	35.68±0.22
20%	34.25± 0.22	35.59±0.22	37.57±0.24	37.65±0.25

[1] * nasser_chelouah@yahoo.fr

Brasil

Brasil

Influence of the diameter of ground date pits on the technological properties of clay bricks

Influência do diâmetro de caroços de tâmara moídos nas propriedades tecnológicas de tijolos de argila

Abstract