This paper looks into the influences of martensitic transformations on the cavitation-erosion (CE) damage initiation mechanism and pitting corrosion resistance of a lean austenitic stainless steel. The ε and α' martensites are prime sites of CE damage initiation for this steel, whereas grain boundaries are more favourable damage initiation sites for other similar steels. The profusion of ε and α' results in fast surface roughening during the CE process, which may cause a compromise in performance when this steel (or similar steels that have the same CE damage mechanism) is used for such applications as hydro-machinery or piping. ε and α' also detrimentally affect the pitting resistance of this steel and so they are expected to affect CE resistance adversely due to the synergism between CE and corrosion.
Keywords
Cavitation erosion; Lean austenitic stainless steel; Martensitic transformation; Pitting corrosion