In this research, the effect of stand-off distance on the interfacial mechanical and metallurgical properties of explosively bonded 321 austenitic stainless steel to 1230 aluminum alloy tubes was investigated. Interfacial microstructure was evaluated by optical microscopy and scanning electron microscope. Also, Microhardness tests were also carried out. The results show that with increasing of stand-off distance from 1 mm to 2.5 mm, thickness of intermetallic compounds at the interface increased from 3.5 µm to 102.3 µm, and also shape of interface was transited from smooth to wavy. The microhardness of the sample with 1 mam stand-off distance was 650 HV that increased to 927 HV in the sample with 2.5 mm stand-off distance which is related to intermetallic amount. The proportional amount of strength were 103.2 MPa and 214.5 MPa in the above samples respectively.
Keywords:
explosive welding; stand-off distance; intermetallic compound